Effect of high-temperature heating on chemical changes in M7C3 carbides of AISI D2 tool steel

Nykiel T., Hryniewicz T.

International Letters of Chemistry, Physics and Astronomy

2014

Vol. 17, iss. 3

258--271

The paper presents the study results obtained on 16H12MF/NC11LV/D2 tool steel. The main purpose of the study was to establish the chemical composition of the coarse primary M7C3 carbides occurring in that steel after a standard soft annealing. The effect of high-temperature annealing in the air atmosphere was investigated. The study was limited to the decarburized layer, on the distance of about 0.4 mm from the surface, of hardened steel after annealing and austenitizing at 1150 ºC in the air atmosphere for the periods of 30 and 90 minutes. It was found that the coarse primary M7C3 carbides of the annealed D2 tool steel differ significantly as to the contents of Cr, Mo, and V, and in the most degree to the contents of chromium and molybdenum. The average concentration of chromium rises successively with the growth of austenitizing time. On the other hand, the concentrations of molybdenum and vanadium are lower after 30 minutes of austenitizing than their concentrations in the similar carbides of the annealed steel. Prolongation of the austenitizing time up to 90 minutes results in the increase of molybdenum and vanadium contents in the coarse carbides. It was found that austenitizing of AISI D2 tool steel at the temperature of 1150 ºC in the air atmosphere leads to precipitation of the second phase, brighter in the BSE_Z pictures, in relation to the matrix of carbides, with the amount and magnitude being higher with the annealing time.

Fluctuations in Chemical Composition of M7C3 Carbides in the Soft Annealed Nc11lv/D2 Steel

Hryniewicz T., Nykiel T.

Advances in Materials Science

2014

Vol. 14, nr 1(39)

24--30

The paper presents the study results on chemical composition of the coarse primary M7C3 carbides occurring in the soft annealed NC11LV/D2 tool steel consisting of: 1.53% C; 11.65% Cr; 0.01% W; 0.81% Mo; 0.068% V; (balance iron plus admixtures), used for cold operation. The microanalyzer of type SEMPROBE Su-30, French made by CAMECA Co., equipped with two WDS X-ray spectrometers and an EDS VOYAGER 3 100, NORAN Instruments Co., made in USA. It was found that out of the three alloying elements occurring in the big carbides of the annealed NC11LV/D2 steel, i.e. Cr, Mo, and V, the chromium appears to be the most uniformly distributed. The big carbides vary concerning C, Cr, Mo, V; the greatest differentiation degree of the contents of Mo and Cr, and the least - of vanadium. The average chemical composition of the big/coarse carbides is as follows: C = 9.42±1.28%; Cr = 44.17±2.95%; Mo = 4.48±3.52%; V = 4.53±0.31%; balance Fe.