Co-based alloy surface layers with boron carbide particles produced on S235 steel by laser cladding method

Bartkowski D., Dudziak B., Piasecki A., Gościański M.

Journal of Research and Applications in Agricultural Engineering

2014

Vol. 59, nr 1

12--16

The work presents results of study of the surface layers formed during the laser cladding process with powder mixture of Co-based alloy and B4C particles on S235 steel. The study included production of the surface layers by using laser device equipped with three-stream nozzle powder feeding system. The different feed rate and the same value of laser beam power have been used. The influence of powder morphology on efficiency of laser metal deposition as well as influence of B4C additive on microhardness, microstructure and chemical composition of produced surface layers have been investigated.

W pracy przedstawiono wyniki badań warstw powierzchniowych wytworzonych przez napawanie laserowe mieszaniny proszkowej stopu na bazie kobaltu i cząstek węglika boru B4C na stali S235. Badania obejmowały wykonanie warstw powierzchniowych przy użyciu urządzenia laserowego wyposażonego w dyszę z trójstrumieniowym systemem podawania proszku. Zastosowano różne prędkości posuwu wiązki lasera przy jednakowej wartości mocy. Stwierdzono, że rodzaj morfologii proszku ma wpływ na wydajność procesu napawania. Określono wpływ dodatku węglika boru na twardość, mikrostrukturę i skład chemiczny wytwarzanych warstw powierzchniowych.

The elevated temperatures influence on the cobalt base cladding layer

Smoleńska H.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

366-368

Purpose of this paper is to evaluate the microstructure, chemical composition and mechanical properties of the clad layers made of the cobalt base powder which were undergone oxidation studies in air at 850, 950 and 1100°C for 200 hours. The layers were made by cladding technique. Cladding was conducted by Plasma Transformed Arc method. The performance of the hardfaced materials were evaluated by microstructure (light and scanning electron microscope SEM), chemical and XRD analysis and microhardness measurements. For all the cases the presence of the scales were observed. The lower temperature of oxidation (850°C) does not influence significantly on the structure in the depth of the clad however dendrites became more regular and coarsening of interdenritic regions were noticed. The higher temperatures resulted in thicker scale layers, partially spalled and in degradation of the surface part of the clad. Microhardness measurements revealed in the outer surface sublayer with thickness of about 0.3 mm significant decrease of hardness. This observation was correlated with the microstructural changes, i.e. the disappearance of carbides in the interdendritic region and their replacement by Cr oxide.

W artykule przedstawiono ocenę zmian mikrostrukturalnych, chemicznych i mechanicznych napawanych warstw wykonanych ze stopu na bazie kobaltu i poddanych utlenianiu w powietrzu w temperaturze 850, 950 i 1100°C przez 200 godzin. Warstwy napawane były metodą plazmową (PTA). Analizowano zmiany w mikrostrukturze (mikroskop świetlny i skaningowy mikroskop elektronowy), składzie chemicznym, składzie fazowym (XRD) oraz mikrotwardości warstw. We wszystkich przypadkach na powierzchni powstawały warstwy zgorzeliny. Utlenianie w najniższej temperaturze nie powodowało znaczących zmian w mikrostrukturze napoiny. Wyższa temperatura prowadziła do powstawania grubszej zgorzeliny, częściowo odpadającej i znacznej degradacji wierzchniej warstwy napoiny. Pomiary mikrotwardości warstwy napawanej wykazały znaczący spadek twardości zewnętrznej warstwy napoiny o grubości ok. 0,3 mm. Potwierdza to zaobserwowane zmiany mikrostrukturalne - m.in. zanik węglików w obszarach międzydendrytycznych i ich zastąpienie przez tlenek chromu.