Corrosion Properties of Ca65-xMg17.5Zn17.5+x (x = 0, 2.5, 5) Alloys

Babilas R., Wojciechowski P., Bajorek A., Sakiewicz P., Cesarz-Andraczke K.

Archives of Metallurgy and Materials

2019

Vol. 64, iss. 3

1033--1040

The aim of the paper is to study the effect of zinc addition on the corrosion behavior of Ca65-xMg17.5Zn17.5+x(x = 0, 2.5, 5 at.%) alloys in simulated physiological fluids at 37°C. The electrochemical measurements allowed to determine a corrosion potential, which showed a positive shift from –1.60 V for Ca65Mg17.5Zn17.5 alloy to –1.58 V for Ca60Mg17.5Zn22.5 alloy, adequately. The more significant decrease of hydrogen evolution was noticed for Ca60Mg17.5Zn22.5 alloy (22.4 ml/cm2) than for Ca62.5Mg17.5Zn20 and Ca65Mg17.5Zn17.5 samples (29.9 ml/cm2 and 46.4 ml/cm2), consequently. The corrosion products after immersion tests in Ringer’s solution during 1 h were identified by X-ray diffraction and X-ray photoelectron spectroscopy as calcium, magnesium oxides, carbonates, hydroxides and calcium hydrate.

Fabrication of ternary Ca-Mg-Zn bulk metallic glasses

Nowosielski R., Borowski A., Guwer A., Babilas R.

Journal of Achievements in Materials and Manufacturing Engineering

2013

Vol. 56, nr 2

67--74

Purpose: The paper describes the preparation, structure and thermal properties of ternary Ca-Mg-Zn bulk metallic glass in form of as-cast rods. Design/methodology/approach: The investigations on the ternary Ca-Mg-Zn glassy rods were conducted by using X-ray diffraction (XRD), scanning electron microscopy (SEM) which energy dispersive X-ray analysis (EDS). Findings: The X-ray diffraction investigations have revealed that the studied as-cast rod was amorphous. The fractures of studied alloy could be classified as mixed fracture with indicated “river” and “smooth” fractures. Both type of the fracture surfaces consist of weakly formed “river” and “shell” patterns and “smooth” regions. The “river” patterns are characteristic for metallic glassy alloys. Practical implications: The studied Ca-based bulk metallic glasses is a relatively new group of material. Ca-based bulk metallic glasses are applied for many applications in different elements. Ca-based bulk metallic glasses have many unique properties such as low density (~2.0 g/cm³), low Youn g’s modulus ( ~20 to 30 GPa). The elastic modulus of Ca-b ased BMGs is comparable to that of hum an bone s, and Ca, Mg, and Zn are biocompatible. These features make the Ca-Mg-Zn–based alloys attractive for use in biomedical applications. Originality/value: Fabrication of amorphous alloy in the form of rod ternary Ca-Mg-Zn alloy by pressure die casting method.