Influence of crystallographic orientation on creep resistance of single-crystal superalloy

Kościelniak Barbara, Gancarczyk Kamil, Poręba Marek, Albrecht Robert

Advances in Manufacturing Science and Technology

2020

Vol. 44, nr 3

93--98

This paper focuses on the influence of crystallographic orientation on creep resistance of CMSX-4 nickel-based superalloy. The single-crystal rods of CMSX-4 superalloy were manufactured with the use of the Bridgman method at a withdrawal rate of 3 mm/min. The crystallographic orientation of the rods was determined by the X-ray Ω-scan method with OD-EFG diffractometer and the Laue back-reflection technique. The creep tests were performed at a temperature of 982°C and the value of stress σ = 248 MPa. Microstructural investigation before and after the creep test of CMSX-4 superalloy was performed using a scanning electron microscope. The results showed that the distribution of the values of α angle strongly affects the creep resistance of a single-crystal superalloy

Directionally solidified CMSX-4 nickel based superalloys; microstructure, orientation, residual stress, microanalysis

Major B., Kubiak K., Bonarski J., Szczerba M., Major Ł., Rakowska A.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

614-617

Analysis has been performed in two directions: (i) examinations of residual stress in single-crystal blades in as cast state and after heat treatment using X-ray method, (ii) diagnostics of crystallographic preferred orientation (XRD, EBSD) and study of microstructure in the micro (SEM,TEM) and nanoatomic (HREM) scale. Method of residual stress measurement in single -crystal material has been elaborated. Examinations by SEM and TEM verified two phases character of materials comprising: cubical precipitates of y'-phase surrounded by y phase of matrix. The size of precipitates was about 1 ~m. The material has a monocrystalline structure with <001> axial orientation for precipitates and <110> orientation for the substrate. The density of dislocations was smaller in the centre of the sample and they were localized at the yy' border or they cross the border along the (110) plane. For the more detailed study of dislocations at the interphase, the filtration technique "twin-oval" mask of reflection on the Fourier transform for TEM examinations was applied. Beside microstructure studies, a chemical SEM/EDX and TEM/EDS microanalysis was carried out. Examinations of residual stress revealed its high variation in "as cast" state at the various places of the blade. Application of heat treatment led to the stress relaxation and its uniformity.

Prowadzono analizę w dwóch kierunkach: (i) badania metodą rentgenowską naprężeń własnych w monokrystalicznych łopatkach w stanie odlanym i po obróbce cieplnej, (ii) diagnozowania uprzywilejowanej orientacji krystalograficznej (XRD, EBSD) oraz mikrostruktury na poziomie skali mikro (SEM, TEM) oraz nano i atomowej (HREM). Opracowano metodę wyznaczania naprężeń własnych w materiale o charakterze monokrystalicznym. Badania SEM i TEM zweryfikowały charakter dwufazowy materiału, tj. osnowa otacza zbliżone do sześcianów wydzielenia y', wielkość których wynosiła około 1 ~m. Struktura tworzywa ma charakter monokrystaliczny o osiowej orientacji typu <001> dla wydzieleń oraz <110> dla osnowy. Dyslokacji w środku próbki było zdecydowanie mniej i lokowały się one albo w granicach faz y/y', albo przecinały je wzdłuż płaszczyzn (110). W celu ujawnienia w badaniach TEM dyslokacji na granicy faz zastosowano technikę filtracji maską twin-oval refleksu na transformacie Fouriera. Obok analizy mikrostruktury przeprowadzono badania mikroanalizy SEM/EDX oraz TEM/EDS. Pomiary naprężeń własnych w stanie po krystalizacji wykazały duże ich zróżnicowanie w łopatce. Zastosowana obróbka cieplna prowadziła do relaksacji naprężeń i ich ujednorodnienia.