The Effect of Different Mn/Fe Ratio on Microstructure Alloy Based on Al-Si-Mg

Bolibruchova D., Ivanova A.

Archives of Foundry Engineering

2019

iss. 3

15--20

This article deals with the effect of manganese that is the most applied element to eliminate the negative effect of iron in the investigated alloy AlSi7Mg0.3. In this time are several methods that are used for elimination harmful effect of iron. The most used method is elimination by applying the additive elements, so-called iron correctors. The influence of manganese on the morphology of excluded iron-based intermetallic phases was analysed at various iron contents (0.4; 0.8 and 1.2 wt. %). The effect of manganese was assessed in additions of 0.1; 0.2; 0.4 and 0.6 wt. % Mn. The morphology of iron intermetallic phases was assessed using electron microscopy (SEM) and EDX analysis. The increase of iron content in investigated alloys caused the formation of more intermetallic phases and this effect has been more significant with higher concentrations of manganese. The measurements carried out also showed that alloys with the same Mn/Fe ratio can manifest different structures and characteristics of excluded iron-based intermetallic phases, which might, at the same time, be related to different resulting mechanical properties.

Evaluation of changes of stereological parameters of eutectic phases in AlSiMg alloy after precipitation hardening

Grzegorek J., Tarasek A., Olszowska-Sobieraj B., Lewicki P.

Metallurgy and Foundry Engineering

2017

Vol. 43, no. 3

169--177

Qualitative microstructure investigations of the AlSiMg alloy’s microstructure in both its original state (with the characteristic primary structure) and after precipitation hardening revealed the significant heterogeneity of the eutectic phases concerning their shape, size, and distribution. An evaluation of the stereological parameters of the eutectic phases was carried out. The computer‑image analysis was performed in order to define the fraction of the relative volume and shape of the eutectic phases and to establish their influence on the mechanical properties.

Jakościowe badania mikrostruktury stopu AlSiMg, zarówno w stanie wyjściowym (o charakterystycznej strukturze pierwotnej), jak i po utwardzaniu wydzieleniowym, wykazały występowanie w badanym stopie istotnych niejednorodności faz eutektycznych pod względem kształtu, wielkości oraz rozmieszczenia. W pracy przeprowadzono ocenę parametrów stereologicznych faz eutektycznych w stopie AlSiMg zarówno w stanie wyjściowym, jak i po utwardzaniu wydzieleniowym. Wykorzystując analizę obrazu komputerowego, określono udział objętościowy względnej faz eutektycznych oraz ich kształt, a także ustalono ich wpływ na właściwości mechaniczne.