The possibility of producing graded Al2O3-Mo, Al2O3-Cu, Al2O3-W composites using CSC method

Wachowski M., Kaszuwara W., Miazga A., Konopka K., Zygmuntowicz Justyna

Bulletin of the Polish Academy of Sciences. Technical Sciences

2019

Vol. 67, nr 2

179--184

The subject of the study was the production and characterization of three ceramic-metal graded composites, which differed in addition of the metallic phase. The following composites systems were investigated: Al2O3-Mo, Al2O3-Cu, Al2O3-W. Composites were produced by centrifugal slip casting method. This technique combines the classic casting of the slurry into porous molds with the action of centrifugal force. As a result, sleeve-shaped shapes with a metallic phase gradient were obtained. X-ray phase analysis have not revealed new phases in the produced composites. The type of metallic phase and its distribution in the ceramic matrix influenced the hardness of the produced composites.

Al2O3-Mo functionally graded material obtained via centrifugal slip casting

Zygmuntowicz J., Baczyńska A., Miazga A., Kaszuwara W., Konopka K.

Materiały Ceramiczne

2017

T. 69, nr 2

73--77

Al2O3-Mo functionally graded material (FGMs) was fabricated successfully by a centrifugal slip casting method. An aqueous ceramic slurry containing 50 vol.% of the solid phase and including 10 vol.% of the molybdenum particles was made. Consolidation was performed by using a centrifugal slip casting process at 3000 rpm for 1.5 h. The morphology and chemical composition of the produced composite were analysed using a scanning electron microscope equipped with an EDS detector. Moreover, the X-ray diffraction was made. The microstructural observation and the stereological analysis confirmed that the molybdenum particles are distributed in the material in a gradient way.

Funkcjonalny materiał gradientowy z układu Al2O3-Mo zostały wytworzony metodą odlewania odśrodkowego mas lejnych. Wodną zawiesinę o zawartość fazy stałej 50% obj. przygotowano na bazie tlenku glinu i proszku molibdenu (10% obj.). Próbki formowano metodą odlewania odśrodkowego; parametry procesu były następujące: v - 3000 obr./min, czas - 1,5 godz. Charakterystyka mikrostruktury oraz składu chemicznego wytworzonego kompozytu została wykonana przy użyciu skaningowego mikroskopu elektronowego z detektorem EDS. Przeprowadzono analizę fazową (XRD) kompozytu. Obserwacje mikrostruktury oraz analiza stereologiczna potwierdziły gradientowe rozmieszczenie cząstek molibdenu w wytworzonym kompozycie.