Effects of SiC Coating of Carbon Fiber on Mechanical Properties in Short Carbon Fiber Reinforced Al Matrix Composite

Jang Jin Man, Ko Se-Hyun, Lee Wonsik

Archives of Metallurgy and Materials

2021

Vol. 66, iss. 4

941--946

A356 Al composites reinforced by short carbon fiber were prepared through the 2-step process: fabrication of a composite precursor and ultrasonication of the precursor melt. The short carbon fibers were coated with 0.15~1.5 μm thick SiC layer by a car-bothermal reaction, and an amount of the carbon fiber reinforcement was determined to be 1.5 vol.% and 4.0 vol.%, respectively. The addition of the carbon fiber increased the hardness of A356 alloy. However, tensile strength did not increase in the as-cast composites regardless of the SiC coating and volume fraction of the carbon fiber, due to the debonding which reduced load transfer efficiency from matrix to fiber at the interface. After T6-treatment of the composites, a significant increase in strength occurred only in the composite reinforced by the SiC-coated short carbon fiber, which was considered to result from the formation of a precipitate improving the Al/SiC interfacial strength.

Rotary friction welding of Al/Al2O3 Composites with Aluminium Alloys

Siedlec Robert, Strąk Cezary

Welding Technology Review

2020

R. 92, nr 6

23--34

Friction welding is one of the most economical process of joining solid-state materials. This technique allows to weld similar and dissimilar materials in a very short time. Friction welding of metal with composites gives new possibilities of application, due to the fact that materials have different physical and mechanical properties. In the study, aluminum alloy 44200 was friction welded to Al/Al2O3 composite. In addition, the following inspections were performed: optical microscopy, microhardness measurements and also tensile strength for all joints produced by friction welding. All of the studies were performed to evaluate the quality of connection between the 44200 alloy and the composites on the aluminum alloy matrix reinforced with ceramic phase of Al/Al2O3.

Zgrzewanie tarciowe to jedna z bardziej ekonomicznych metod trwałego łączenia materiałów w stanie stałym. Metoda ta umożliwia wykonywanie złączy zarówno jednoimiennych, jak i różnoimiennych w bardzo krótkim czasie. Zaletą zgrzewania tarciowego jest możliwość uzyskania złączy o wysokiej jakości. Zgrzewanie tarciowe kompozytów z metalami, stwarza nowe możliwości aplikacji, z uwagi na fakt, że oba materiały posiadają różne właściwości fizyczne oraz mechaniczne. W pracy przeprowadzono próby spajania stopu aluminium EN-AC-44200 z kompozytami Al/Al2O3. W opracowaniu przeprowadzono następujące badania złączy stop aluminium-kompozyt uzyskanych metodą zgrzewania tarciowego: mikroskopowe, twardości, mechaniczne (pomiar wytrzymałości na rozciąganie). Wykonane badania miały na celu ocenę jakości połączenia pomiędzy stopem 44200, a kompozytami na osnowie stopu aluminium wzmacnianymi fazą ceramiczną Al/Al2O3.