Surface tension and density of Cu-Ag, u-In and Ag-In alloys

Kucharski M., Fima P., Skrzyniarz P., Przebinda-Stefanowa W.

Archives of Metallurgy and Materials

2006

Vol. 51, iss. 3

389-397

The sessile drop method has been used to measure density and surface tension of Cu, In and Cu-Ag, Cu-In and Ag-In mixtures. For pure metals (Cu, In) and for Cu-Ag, Ag-In alloys, the negative temperature coefficients of surface tension have been obtained. In case of Cu-In alloys, the temperature coefficients of surface tension take negative or positive values depending on composition. Experimental values of the surface tension of Cu-Ag, Cu-In and Ag-In are compared with those computed from Butler model and a fairly good agreement is observed.

Praca prezentuje wyniki pomiarów gęstości i napięcia powierzchniowego czystych metali (Cu, In) oraz stopów podwójnych Cu-Ag, Cu-In oraz Ag-In. Dla czystych metali (Cu, In) oraz dla stopów podwójnych Cu-Ag i Ag-In uzyskano ujemne wartości współczynników temperaturowych napięcia powierzchniowego. Natomiast w przypadku stopów Cu-In uzyskano, w zależności od składu, dodatnie lub ujemne wartości współczynników temperaturowych napięcia powierzchniowego. Dla wszystkich badanych stopów uzyskano zadawalającą zgodność pomiędzy wartościami napięcia powierzchniowego obliczonymi z modelu Butlera, a wynikami eksperymentu.

Experimental study of phase equilibria in the silver-copper-indium alloys

Wierzbicka A., Czeppe T., Zabdyr L.

Archives of Metallurgy and Materials

2006

Vol. 51, iss. 3

377-387

The brief thermodynamic characteristic of binary subsystems were given, and phase diagrams presented. Then cross-section of ternary system Ag-Cu-In was calculated along the constant Cu/In ratio equal 1, using binary formalism. Considerable discrepancies were observed between calculation results and the known informations about thermodynamic behaviour of the liquid alloys. To explain it, this study was undertaken, employing two exerimental techniques: differential thermal analysis, DTA, and differential scanning calorimetry, DSC. Three cross sections were investigated for constant Cu/In ratio equal 3, 1 and 1/3, with silver content varying from 10 at.% to 90 at.%, every 10%. Results are presented in tables and figures, exhibiting two different trends: 1) good agreement of experiment and calculations for higher Ag content (>60%), 2) considerable discrepancies between experiment and calculations for lower silver content, especially for the cross-section Cu/In = 1. Resuls of both experimental techniques agree well each other. Experimental data obtained in this work are to be used for thermodynamic modelling and phase diagram calculations of the system under accord by CALPHAD approach.

Na wstępie przedstawiono wykresy fazowe dwuskładnikowych stopów składowych: Ag-Cu, Ag-In i Cu-In, podając ich krótką charakterystykę termodynamiczną. Następnie obliczono przekrój poprzeczny układu trójskładnikowego Ag-Cu-In wzdłuż linii stałego stosunku zawartości Cu/In, równego 1. Wyniki obliczeń pozostają w znacznej rozbieżności z uzyskanymi już wcześniej informacjami o charakterze termodynamicznym stopów trójskładnikowych. Dla wyjaśnienia tych rozbieżnosci podjęto niniejsze badania przy zastosowaniu dwóch technik eksperymentu: różnicowej analizy termicznej, DTA, i różnicowej mikrokalorymetrii skaningowej, DSC. Zbadano stopy o składach leżących wzdłuż trzech linii stałej zawartości Cu/In, równej: 3, 1 i 1/3, oraz przy zawartości srebra zmieniającej się od 10% at. do 90% at., co 10%. Wyniki tabeli przedstawiono w tabelach i na wykresach. Uzyskane rezultaty wykazują dwojaką tendencję: 1) dobra zgodność z wynikami obliczeń dla stopów o wysokiej zawartości srebra (>60%); 2) znaczne rozbieżności z wynikami obliczeń dla stopów o niższej zawartości srebra, największe dla przekroju Cu/In = 1. Zaobserwowano również dobrą zgodność wyników pochodzących z obydwu zastosowanych metod eksperymentu: DTA i DSC. Dane eksperymentalne uzyskane w niniejszej pracy będą zastosowane wraz z innymi informacjami do obliczenia diagramu fazowego ukladu Ag-Cu-In metodą CALPHAD.