Experimental and numerical analysis of fracture in 41Cr4 steel – issues of the stationary cracks

Graba M.

International Journal of Applied Mechanics and Engineering

|

2018

|

Vol. 23, no. 1

37--63

EN

This paper analyzes the process of fracture in 41Cr4 steel on the basis of experimental and numerical data obtained for non-propagating cracks. The author’s previous and latest experimental results were used to determine the apparent crack initiation moment and fracture toughness for the material under plane strain conditions. Numerical simulations were carried out to assess changes in the J-integral, the crack tip opening displacement, the size of the plastic region and the distribution of stresses around the crack tip. A complex numerical analysis based on the true stress-strain curve was performed to determine the behavior of 41Cr4 steel under increasing external loads.

2

Badania wpływu obróbki laserowej na właściwości tribologiczne stali 40H

Napadłek W., Przetakiewicz W

Prace Naukowe Instytutu Konstrukcji i Eksploatacji Maszyn Politechniki Wrocławskiej. Konferencje

|

2002

|

Vol. 87, nr 27

249-254

PL

W pracy przedstawiono wybrane wyniki badań tribologicznych stali 40H hartowanej indukcyjnie oraz laserowo. Stwierdzono, że istotny wpływ na procesy zużycia ściernego i ścierno-adhezyjnego warstwy wierzchniej ma układ laserowych ścieżek hartowniczych. Hartowanie laserowe znacząco zwiększa odporność badanej stali na zużycie w stosunku do stanu po ulepszaniu cieplnym i nieznacznie w stosunku do stali hartowanej indukcyjnie.

EN

The selected results of tribology researches of 40H steel being induction and laser hardened are presented in this elaboration. There was found that the laser hardened paths arrangement has essential influence on processes of abrasive and abrasive-adhesion wear of superficial layer. The laser hardening significantly increases of wear-resistant of tested steel in relation to state after quenching and tempering and only insignificantly (marginally) in relation to induction hardened.

3

Właściwości mechaniczne stali 40H hartowanej laserowo

Napadłek W.

Krzepnięcie Metali i Stopów

|

2000

|

R. 2, nr 42

343--355

PL

Praca porusza problematykę badań wybranych właściwości mechanicznych w oparciu o próbę statycznego rozciągania, stali 40H po różnych obróbkach cieplnych (ulepszonej cieplnie, hartowanej indukcyjnie, hartowanej laserowo - przy różnych układach ścieżek hartowniczych). Określono parametry Rm, R0,2, A5, Z. Charakter złomów analizowano na podstawie obserwacji przy wykorzystaniu SEM i TEM (metoda replik). Stwierdzono bardzo korzystny wpływ obróbki laserowej, powodującej wzrost właściwości wytrzymałościowych i plastyczności badanej stali. Zaobserwowano również interesujące mechanizmy pękania inicjowane w strefie przejściowej (hartowanie bez przetopienia), lub w strefie przetopionej (hartowanie z przetopieniem).