Effect of γ phase content on martensitic transformation and mechanical properties in Co–Ni–Al shape memory alloys

Maziarz Wojciech

Inżynieria Materiałowa

2019

Vol. 40, nr 4

86--90

The effect of γ phase content on the martensitic transformation and mechanical properties of Co–Ni–Al alloys was investigated. For nine Co–Ni–Al alloys with different chemical composition corresponding to the e/a ratio from 7.9 to 7.55, a quantitative microstructure investigations as well as tensile tests have been performed. The alloys were induction melted, casted, homogenized, plastically deformed by hot rolling with thickness reduction of 90% and finally again annealed and water quenched (solution treated). Quantitative image analyse of microstructure after homogenization allowed to determine the γ content from 14 to 39% for alloys containing from 25 to 30 at. % Al respectively, while further hot rolling and solution treatment caused reduction of γ phase content from 6 to 23%. Linear relationships between Ms temperature and e/a ratio was found for alloys with the e/a ratio from 7.9 to 7.72, in which the amount of γ phase increases slightly from 21 to 23%, and for composition where e/a decreases from 7.69 to 7.55 and γ phase content rises up from 6 to 12%. Tensile tests revealed that alloys with the highest γ phase content (about 20%) have the best mechanical properties; strength at the level of 1000 MPa combined with plasticity at the level of 18%.

Celem pracy było określenie wpływu zawartości fazy γ w dwufazowych β + γ stopach z pamięcią kształtu z układu Co–Ni–Al po procesie walcowania na gorąco, a następnie przesycania z wysokiej temperatury (z zakresu jednofazowego β) na zakres przemiany martenzytycznej i właściwości mechaniczne tych stopów.

Microstructure Characterization of High Carbon Alloy from the Ni-Ta-Al-Co-Cr System

Bała P.

Archives of Metallurgy and Materials

2012

Vol. 57, iss. 4

937-941

In the present work results of investigations of the new high carbon alloy from the Ni-Ta-Al-Co-Cr system are presented. The alloy has been designed to have a good tribological properties at elevated temperatures. The chemical composition of this material was designed to obtain a matrix strengthening by the precipitation of γ phase (Ni3(Al,Ta)) and the primary carbides volume fraction above 25%. The primary carbides should remain stable in the microstructure, regardless of the heat treatment, in order to increase a wear resistance. The results of microstructure investigations in the as-cast condition are presented. The type of phases appearing in the microstructure was determined and their morphology described. The main microstructure components of the investigated Ni-based alloy with high carbon, cobalt and chromium content are: the γ phase, which constitutes a matrix, the γ phase, which occurs as fine globular precipitates and the primary Ta and Cr carbides (of MC and M7C3 type - respectively).

W pracy przedstawiono nowy stop na osnowie niklu o dużym stężeniu węgla, przewidywany do pracy w wysokiej temperaturze i w warunkach silnego zużycia tribologicznego. Skład chemiczny nowego materiału zaprojektowano tak, aby umocnienie osnowy uzyskać w wyniku wydzielania fazy γ (Ni3(Al,Ta)), a udział węglików pierwotnych wynosił ponad 25%. Węgliki powinny pozostać stabilne w mikrostrukturze niezależnie od obróbki cieplnej, wpływając korzystnie na odporność na ścieranie. Zamieszczono wyniki badan mikrostruktury stopu w stanie lanym. Określono rodzaj faz występujących w mikrostrukturze oraz opisano ich morfologie. Głównymi składnikami mikrostruktury badanego stopu na osnowie Ni, o dużej zawartości węgla, kobaltu i chromu są: faza γ (która stanowi osnowę) faza γ (która występuje w postaci drobnych kulistych wydzieleń) oraz pierwotne węgliki Ta (typu MC) i Cr (M7C3).