Synthesis of α-Fe2O3 nanoparticles and analyzing the effect of annealing temperature on its properties

Thimmiah Bhargavi Ram, Nallathambi Gobi

Materials Science Poland

2020

Vol. 38, No. 1

116--121

α-Fe2O3 nanoparticles were synthesized via co-precipitation technique using ferric and ferrous salts and potassium hydroxide as precipitation agents. The samples were calcined at 350 °C, 550 °C and 750 °C for 3 hours. The obtained iron oxide was characterized by X-ray diffraction (XRD), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and dynamic light scattering (DLS). Crystallinity of the sample was studied by X-ray diffraction. SEM micrographs showed nonuniform size distribution of the particles forming agglomerates. TGA analysis revealed trace amount of weight loss and material stability for the samples calcined at temperatures above 500 °C. DLS results indicated that increasing of annealing temperature resulted in reduction of the particle size and more uniform size distribution. At the maximum annealing temperature of 750 °C, the mean diameter of the particles of 100 nm was observed.

Design Of A Bi-Functional α-Fe2O3/Zn2SiO4:Mn2+ By Layer-By-Layer Assembly Method

Yu R., Yun J., Pee J-H., Kim Y.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2B

1165--1167

This work describes the design of bi-functional α-Fe2O3/Zn2SiO4:Mn2+ using a two-step coating process. We propose a combination of pigments (α-Fe2O3) and phosphor (Zn2SiO4:Mn2+ ) glaze which is assembled using a layer-by-layer method. A silica-coated α-Fe2O3 pigment was obtained by a sol-gel method and a Zn2+ precursor was then added to the silica-coated α-Fe2O3 to create a ZnO layer. Finally, the Zn2SiO4:Mn2+ layer was prepared with the addition of Mn2+ ions to serve as a phosphor precursor in the multi-coated α-Fe2O3, followed by annealing at a temperature above 1000°C. Details of the phase structure, color and optical properties of the multi-functional α-Fe2O3/Zn2SiO4:Mn2+ were characterized by transmission electron microscopy and X-ray diffraction analyses.