Wyniki wyszukiwania - BazTech

1

Protective-conducting spinel coatings applied in IT-SOFC interconnects

Brylewski T., Bobruk M., Gil A.

Ochrona przed Korozją

|

2017

|

nr 5

136--140

EN

The aim of the presented study was to deposit a protective-conducting Mn1.45Co1.45Dy0.1O4 coating on the E-Brite ferritic steel by means of electrophoresis and to evaluate its physicochemical properties. The structure and morphology of the powder, sinter, and the steel/coating layered system, and the electrical conductivity of both the sinter and the coating on the steel after oxidation were investigated by means of X-ray diffraction (XRD), scanning electron microscopy combined with energydispersive spectroscopy (SEM-EDS), and the two-probe dc method. The obtained spinel exhibited a two-phase composition and high electrical conductivity, while the coating it formed was compact and adhered well to the metallic substrate; moreover, the measured ASR of the steel/ coating system was significantly lower than the level acceptable for interconnect materials. The conducted research confirmed the suitability of the Mn1.45Co1.45Dy0.1O4 spinel as a coating on the E-Brite ferritic steel to be applied in the production of interconnects used in intermediatetemperature SOFCs.

PL

Celem niniejszej pracy jest otrzymanie oraz badania właściwości fizykochemicznych powłoki ochronno-przewodzacej Mn1.45Co1.45Dy0.1O4 naniesionej na stal ferrytyczną E-Brite przy użyciu metody elektroforetycznej. Strukturę oraz morfologię proszku, spieku oraz układu warstwowego stal/powłoka, a także przewodnictwo elektryczne zarówno spieku, jak i powłoki na stali po utlenianiu badano przy pomocy dyfrakcji promieniowania rentgenowskiego (XRD), skaningowej mikroskopii elektronowej (SEM-EDS) oraz stałoprądowej metody dwusondowej. Uzyskany spinel wykazuje skład dwufazowy oraz wysokie przewodnictwo elektryczne, zaś uzyskana z niego powłoka jest zwarta i dobrze przylega do podłoża metalicznego, a ponadto wartość zmierzonej rezystancji układu stal/powłoka jest zdecydowanie niższa od dopuszczalnego poziomu ASR dla materiałów interkonektorowych. Na podstawie tych badań potwierdzono przydatność spinelu Mn1.45Co1.45Dy0.1O4 na powłoki do modyfikacji powierzchniowej stali ferrytycznej E-Brite z przeznaczeniem na interkonektory do ogniw paliwowych typu IT-SOFC.

2

Physicochemical properties of the Fe-25Cr/(La,Sr)CrO3 layer system in air and Ar/H2/H2O gas mixture

Bobruk M., Brylewski T.

Ochrona przed Korozją

|

2015

|

nr 11

392--395

EN

The oxidation kinetics and electrical properties of the Fe-25Cr stainless steel with the (La,Sr)CrO3 thick film coating were studied during its oxidation at 1073 K for 650 hrs in air and the Ar/H2/H2O gas mixture. The investigated material was the DIN 50049 steel covered with the (La,Sr)CrO3 paste using the screen printing method. To prepare the paste, La0.8Sr0.2CrO3 micropowder was obtained via EDTA gel processes. Kinetic studies demonstrated that the application of the investigated coating can reduce the rate of corrosion of this type of steel by approximately as much as an order of magnitude. The measured values of area-specific resistance of the Fe-25Cr/(La,Sr)CrO3 layered system after oxidation in the afore-mentioned atmospheres were ca. 50% lower than the upper limit specified for interconnects (0.1 Ω⋅cm2).

PL

W pracy przedstawiono wyniki badań kinetyki utleniania i właściwości elektrycznych stali ferrytycznej Fe-25Cr z powłoką (La,Sr)CrO3 podczas jej utleniania w 1073 K przez 650 godz. w powietrzu i mieszaninie gazu Ar/H2/H2O. Badaniom poddano stal DIN 50049 z naniesioną pastą (La,Sr)CrO3 za pomocą metody sitodruku. Do przygotowania pasty użyto mikroproszku La0.8Sr0.2CrO3, który otrzymano metodą EDTA gel processes. Badania kinetyczne dowiodły, że w wyniku zastosowania powłoki ceramicznej można obniżyć szybkość korozji tego typu stali nawet o około rząd wielkości. Zmierzone wartości powierzchniowej rezystancji elektrycznej układu warstwowego Fe-25Cr/(La,Sr)CrO3 po utlenianiu w w/w atmosferach były około 2 razy niższe od górnej granicy dopuszczalnej dla interkonektorów (0,1 Ω⋅cm2).

3

Influence of yttrium on the physicochemical properties of the Fe-25Cr ferritic steel for IT-SOFC interconnects

Brylewski T., Gil A., Dąbek J.

Ochrona przed Korozją

|

2015

|

nr 11

410--415

EN

The study investigates the influence of yttrium ion implantation on the heat resistance and electrical conductivity of the Fe-25- Cr ferritic steel used as a material for interconnects applied in intermediate-temperature solid oxide fuel cells (IT-SOFCs). The oxidation kinetics of the Fe-25Cr steel, both unmodified and modified, were determined during 200 hrs of observation under isothermal conditions in air and the Ar/H2/H2O and Ar/CH4/H2O gas mixtures at 1073K. A significant improvement in corrosion resistance was observed after surface modification. XRD and SEM-EDS investigations showed that a protective scale composed mainly of Cr2O3 had formed. The yttrium-implanted steel exhibited the lowest area-specific resistance (ASR), which did not exceed the level acceptable for IT-SOFC interconnect materials (0.1 Ω⋅cm2), unlike the ASR of the unmodified steel.

PL

W pracy zbadano wpływ implantowanego jonowo itru na żaroodporność i przewodnictwo elektryczne stali ferrytycznej Fe-25Cr, stosowanej na interkonektory do ogniw paliwowych IT-SOFC. Wyznaczono kinetykę utleniania w warunkach izotermicznych (1073 K, 200 godz.) dla materiału wyjściowego oraz modyfikowanego w środowisku powietrza oraz w mieszaninach gazów: Ar/H2/H2O i Ar/CH4/H2O. Stwierdzono, że stal modyfikowana za pomocą implantacji jonowej charakteryzuje się wyższą odpornością na korozję. Badania XRD i SEM-EDS wykazały, że ochronna zgorzelina w zasadniczej części zbudowana była z Cr2O3. Stal implantowana itrem, w przeciwieństwie do niemodyfikowanej, posiadała niższą powierzchniową rezystancją elektryczną ASR od wartości dopuszczalnej (0,1 Ω⋅cm2) dla materiałów przeznaczonych na IT-SOFC interkonektory.

4

Fizykochemiczne właściwości układu warstwowego Fe-25Cr/(La,Ca)CrO3 w atmosferze powietrza i mieszanin gazów Ar/H2/H2O i Ar/CH4/H2O

Brylewski T., Bućko M.M., Rakowska A., Dąbek J., Przybylski K.

Materiały Ceramiczne

|

2013

|

T. 65, nr 1

8--19

PL

W pracy przedstawiono wyniki badań kinetyki utleniania i właściwości elektrycznych stali ferrytycznej Fe-25Cr z powłoką (La,Ca)CrO3 podczas jej utleniania w 1073 K w powietrzu i mieszaninach gazów Ar/H2/H2O i Ar/CH4/H2O. Badaniom poddano stal DIN 50049 z naniesioną pastą (La,Ca)CrO3 przy pomocy metody sitodruku. Do przygotowania pasty użyto mikroproszku La0,8Ca0,2CrO3, który otrzymano metodą współstrącania i kalcynacji. Kinetykę wzrostu zgorzeliny na stali czystej oraz pośredniej warstwy reakcyjnej na granicy rozdziału stal/powłoka układu warstwowego Fe-25Cr/(La,Ca)CrO3 w w/w warunkach można opisać w przybliżeniu prawem parabolicznym. Morfologię oraz skład chemiczny i fazowy produktów utleniania stali czystej i stali z powłoką (La,Ca)CrO3 badano przy pomocy SEM-EDS, TEM-SAD i XRD. Wpływ pośredniej warstwy reakcyjnej na właściwości elektryczne badanego układu stal/powłoka przedyskutowano w aspekcie jego przydatności do konstrukcji metalicznych interkonektorów dla ogniw paliwowych SOFC.

EN

The oxidation kinetics and electrical properties of the Fe-25Cr stainless steel coated in the (La,Ca)CrO3 thick film were studied during its oxidation at 1073 K in air and Ar/H2/H2O and Ar/CH4/H2O gas mixtures. The material for the experiments was the DIN 50049 steel covered with the (La,Ca)CrO3 paste, using the screen printing method. To prepare the paste, La0.8Ca0.2CrO3 micropowder was obtained via co-precipitation and calcination. The kinetic growth of the scale on pure steel and of the intermediate reactive layer at the steel/coating interface of the Fe-25Cr/(La,Ca)CrO3 layer system in the afore-mentioned conditions approximately follows the parabolic rate law. The morphology, and the chemical and phase compositions of the oxidation products of pure steel and the steel coated with (La,Ca)CrO3 were investigated using SEM-EDS, TEM-SAD and XRD analyses. The effect of the intermediate reactive layer on the electrical properties of the studied system is discussed in terms of its applicability for the construction of metallic interconnects used in SOFCs.