1
Content available Solidification path of the AlFeMnSi alloys in a stage of primary intermetallic phases precipitation
Warmuzek M.
Prace Instytutu Odlewnictwa
|
2015
|
T. 55, nr 3
51--60
EN
In this work, an analysis of the solidification course of the AlFeMnSi alloys was carried out in the Al alloys of Fe, Mn, and Si concentrations in a range supplementary for those examined until now. The morphology of the pre-dendrite and pre-eutectic precipitates of the AlFeMnSi intermetallics has been revealed in relation to alloy composition. The phase attribution of the AlFeMnSi intermetallics forming primary pre-dendrite and pre-eutectic crystals was revealed in situ through local diffraction methods. The results obtained in the present work, as compared with data published previously, revealed the critical limit of the Mn concentration, necessary to stabilize the αc-AlFeMnSi phase as equal ≤ 0.5 wt. %, in the alloys AlFe≤3.0MnSi6 and AlFe≤1.5MnSi11 and ≥ 0.5 wt. % in AlFe≥3.0MnSi11.
PL
W pracy analizowano przebieg procesu krzepnięcia stopów AlFeMnSi podczas powstawania predendrytycznych oraz preeutektycznych faz międzymetalicznych AlFeMnSi w zakresie stężenia składników, uzupełniającym badane dotychczas zakresy. Ujawniono oddziaływanie składu chemicznego stopu na morfologię predendrytycznych oraz preeutektycznych faz międzymetalicznych AlFeMnSi. Charakterystyka wydzieleń faz międzymetalicznych AlFeMnSi została zidentyfikowana in situ, z zastosowaniem lokalnych metod dyfrakcyjnych. Uzyskane wyniki zostały porównane z danymi opublikowanymi uprzednio. Oszacowano, że krytyczne stężenie manganu, konieczne do stabilizacji fazy αc-AlFeMnSi, wynosiło ≤ 0,5%, w badanych stopach AlFe≤3,0MnSi6 i AlFe≤1,5MnSi11 oraz ≥ 0,5% w stopach AlFe≥3,0MnSi11.
2
Content available remote Investigation of selected thermo-physical properties in the Co-based superalloy: Experiment and application study
Kasala J., Mäsiar H., Pernis I.
Archives of Foundry Engineering
|
2010
|
Vol. 10, iss. 1 spec.
203--206
EN
Thermo-physical properties are the critical input parameters in computational models of solidification and casting simulations. In thermodynamics, the enthalpy is quotient of thermodynamic potential of a system, which can be used to calculate the useful work obtainable from a closed thermodynamic system under constant pressure. Differential thermal analysis has been used to study melting and solidification paths in the cobalt based superalloy FSX-414. The temperature enthalpy curve was determined from differential thermal analysis curves obtained from solidification curves. A solidification simulation of a cobalt base multi-component alloy casting was carried out to predict cooling and shrinkage porosity in the casting of a turbine engine vane segment. The effect of latent heat on the heat transfer calculation was considered by enthalpy method.
3
Content available remote Solidification and solid/liquid interface paths for the formation of protective coatings
Wołczyński W., Himemiya T., Kopyciński D., Guzik E.
Archiwum Odlewnictwa
|
2006
|
R. 6, nr 18/1
359--362
EN
A solidification path was determined for the processes of diffusion soldering and hot dip galvanizing occurred at constant temperature. The solidification path is shown for binary Ni-Al and Fe-C phase diagrams. The beginning of solidification path is estimated from measurement of the average solute concentration within coating frozen during solidification. The end of solidification path is a result of a cross-section of the real temperature applied in technology and liquidus line of a given phase diagram.
PL
Ścieżka krystalizacji została wyznaczona dla procesu spajania dyfuzyjnego oraz cynkowania metodą zanurzeniową, które przebiegają w warunkach izotermicznych. Ścieżka krystalizacji jest pokazana na przykładzie podwójnych diagramów fazowych równowagi stabilnej: Ni-Al oraz Fe-C. Początek ścieżki krystalizacji jest oszacowany z pomiarów średniego stężenia składnika stopowego w powłoce zamrożonej w trakcie krystalizacji. Koniec ścieżki krystalizacji jest wynikiem przecięcia rzeczywistej temperatury zastosowanej w danej technologii oraz linii likwidus danego diagramu fazowego równowagi stabilnej.
4
Analytical electron microscopy of the gamma' and gamma phases in a nickel-base superalloy
Hodor K., Zięba P., Olszowska-Sobieraj B.
Inżynieria Materiałowa
|
2001
|
R. XXII, nr 4
380-383
EN
The morphology and chemistry in investment structural cast Ni-base superalloy have been investigated by means of analytical electron microscopy. This allowed to determine the partition of alloying elements between gamma' and gamma phases as well as at the gamma'/gamma interfaces for the two types of gamma' precipitates. The obtained results are discussed in the frame of possible solidification paths for this alloy.
PL
Zaprezentowano charakterystykę strukturalną i chemiczną nadstopu na osnowie niklu uzyskanego bezpośrednio w procesie odlewania. Zastosowanie techniki analitycznej mikroskopii elektronowej pozwoliło określić rozkład powierzchniowy poszczególnych pierwiastków w fazach gamma i gamma'. Analizę wykonano dla dwóch typów wydzieleń fazy gamma'. Przeprowadzone badania mogą być przyczynkiem do dyskusji na temat rodzaju ścieżki krystalizacji dla badanego nadstopu.