Phase Analysis of Explosive Welded Ti-Cr/Ni Steel in As-Received State and after Heat Treatment Using Synchrotron

Ostroushko D., Mazancová E., Saksl K., Milković O.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 4

1611--1614

EN

Surface coatings protection is one of the most important processes ensuring efficient and economic use of basic materials, mostly of lower-quality. At interface of clad and basic material intermetallic phases are formed, representing quite different matrix with dissimilar properties unlike the welded materials. One type of surface coating is explosive bonding which belongs to group of pressure welding. The work is focused on interface shape line, inhomogeneities in vicinity of the wave joint both in basic material and in vicinity of weld line of the Ti and Cr/Ni stainless steel (SS) matrix. Investigated weld was both in as-received state and after heat treatment carried out at 600°C/90 minutes/air. Presented phases have been identified using X-ray diffraction performed by synchrotron. The Tiα, Fe-fcc, Fe-bcc and intermetallic phases Fe2Ti were detected at interface area.

PL

Jednym z najważniejszych procesów zapewniających skuteczne i ekonomiczne uwarunkowane stosowanie materiałów konstrukcyjnych jest pokrywanie powierzchni warstwą ochronną. W strefie połączenia następuje formowanie się faz międzymetalicznych charakteryzujących się całkowicie odmiennymi od materiałów łączonych własnościami. Jednym ze sposobów pokrycia powierzchni materiałów jest zgrzewanie wybuchowe, które należy do metod ciśnieniowych. Praca została zogniskowana na charakterystyce kształtu linii połaczenia, niejednorodnościach w okolicy rozchodzenia się fali wybuchu obydwu materiałów, jak i w okolicach linii samego połączenia Ti oraz Cr/Ni stali niskowęglowej (SS). Badania fazy przetopionej w obydwu materiałach prowadzono po przeprowadzeniu obróbki termicznej, która przeprowadzono w temperaturze 600°C przez 90 minut, bez atmosfery ochronnej. Pojawiające się fazy zostały przebadane z wykorzystaniem dyfrakcji promieni rentgenowskich w synchrotronie. Ujawniono fazy Tiα, Fe-fcc, Fe-bcc oraz fazę międzymetaliczną Fe2Ti w obszarze połączenia.

2

Wybrane aspekty technologiczne wytwarzania lutowniczych materiałów warstwowych z udziałem srebra

Ciura L., Kazana W., Księżarek S., Karpiński M.

Hutnik, Wiadomości Hutnicze

|

2012

|

Vol. 79, nr 2

115--121

PL

Przedstawiono przegląd prac obejmujących wybrane aspekty technologiczne wytwarzania lutowniczych materiałów warstwowych z udziałem srebra do zastosowań w narzędziach skrawających pracujących w trudnych warunkach eksploatacyjnych. Omówiono prace dotyczące otrzymywania trimetali metodami: platerowania na zimno i gorąco, spłaszczania drutu bimetalowego, łączenia wybuchowego, a także metodą kombinowaną łączącą platerowanie w podwyższonej temperaturze z walcowaniem na gorąco i na zimno.

EN

A review of works illustrating the technological aspects in the field of layered brazing materials with silver content for use in cutting tools working in harsh conditions was presented. Works on the production methods of multilayer materials were discussed; hot and cold plating, the bimetallic wire flattening, explosive metal cladding and combined method joining plating at increased temperature, hot with cold rolling.

3

Badania parametrów procesowych wytwarzania warstwowych spoiw twardych

Kuzana W., Ciura L., Księżarek S., Smolarczyk Z., Kubica L.

Hutnik, Wiadomości Hutnicze

|

2008

|

Vol. 75, nr 8

416-418

PL

Celem badań było określenie możliwości wytwarzania taśm spoiw warstwowych z wsadu łączonego metodą wybuchową. W badaniach ustalono parametry w zakresie przeróbki plastycznej łączonego wybuchowo wsadu warstwowego w procesie walcowania na gorąco i na zimno. Przeprowadzone badania i analiza metalograficzna uzyskanego materiału potwierdziły pełną spójność warstw i ich równomierny rozkład na przekroju poprzecznym taśmy.

EN

The aim of the reasearch was to determine possibilities of manufacturing multilayer filler metal from explosive metal clad input material. Technological parameters of metalworking have been established in the process of hot and cold rolling. Microstructure analysis of the output material have shown entire adhesion with even distribution of the layers through the cross-section of the strip.

4

Strefa przejściowa w technologiach wybuchowych i detonacyjnych

Babul W., Janecki J. T.

Tribologia

|

2001

|

nr 6

1127-1138

PL

Scharakteryzowano warstwy (strefy) pośrednie, powstające w procesie zderzenia metali, z dużymi prędkościami, jakie zachodzą przy wybuchowym łączeniu metali, także przy natryskiwaniu detonacyjnym. Warstwy takie charakteryzuje duże rozdrobnienie ziaren (niemal struktura "bezpostaciowa") i często odbiegający od materiałów wyjściowych skład chemiczny. Wywołanie ciśnienia o wartości krytycznej powoduje połączenie się obu metali niezależnie od prędkości przebiegu łączenia. Przy niższych ciśnieniach połączenie uzyskuje się jedynie wówczas, gdy prędkość przebiegu łączenia nie przekracza prędkości propagacji dyslokacji.

EN

The authors describe the substrate-surface layer interface produced due to impact of metals at very high speeds, typical of processes of the detonation bonding of metals or detonation spraying. Such and interface show a grain size reduction (almost amorphous-like structure) and different chemical composition form initial one. By reaching a critical value of the detonation pressure it is possible to bond metals irrespective of the bonding speed. At lower pressures a permanent bond is obtained only in case when the bonding speed does not exceed the rate of dislocation propagation.