The effect of surface modification of LaNi4.5Co0.5 hydride alloy with SiC layer on its hydrogen storage and kinetic electrochemical properties

Stefaniak A., Bordolińska K., Bala H., Pawlak W., Wendler B.

Ochrona przed Korozją

|

2018

|

nr 3

66--69

EN

The effect of encapsulation of LaNi4.5Co0.5 hydrogen storage powdered material, with thin magnetron sputtered layer of SiC, on basic hydrogenation parameters of the composite hydride electrode has been discussed. The multicycle galvanostatic charge/discharge method allowed to determine electrode hydride capacity, exchange current density of the H2O/H2 system, and evaluate material tendency to corrosion degradation. The electrochemical diagnostic experiments carried out at room temperature, at charge/discharge rates of −186/+186 mA g−1 , revealed the initial discharge capacities on the level of 289 mA h g−1 for the tested electrodes. The presence of SiC layers on hydride powder improves kinetics of hydrogen electrosorption process.

PL

Badano wpływ enkapsulacji materiału magazynującego wodór LaNi4.5Co0.5 cienką warstwą SiC, uzyskiwaną przez rozpylanie magnetronowe, na podstawowe parametry kompozytowej elektrody wodorkowej. Galwanostatyczna wielocykliczna metoda ładowania/rozładowania pozwoliła określić pojemność wodorkową, gęstość prądu wymiany układu H2O/H2 i ocenić tendencję materiału do degradacji korozyjnej. Charakterystyki elektrochemiczne zmierzone w temperaturze otoczenia przy szybkościach ładowania/rozładowania równych −186/+186 mA g−1 pozwoliły ustalić, iż początkowe pojemności rozładowania badanych elektrod są na poziomie 289 mA h g−1 . Obecność warstw SiC na materiale proszkowym poprawia kinetykę procesu elektrosorpcji wodoru.

2

Electrochemical characteristics of LaNi4,5Co0,5 alloy composite hydrogen storage material at high discharge rates

Stefaniak A., Bordolińska K., Bala H.

Ochrona przed Korozją

|

2018

|

nr 4

90--92

EN

Electrochemical hydrogen storage behavior of LaNi4,5Co0,5 powder composite electrode cycled in 6M KOH solution at increased discharge rates is discussed. Galvanostatic charging/discharging technique has been applied to determine high rate discharge ability (HRD) after N = 15 and N = 60 cycles. The anodic plots for both tested options are typical: electrode potential nearly linearly (with very low slope) increases with electrode discharge and then sharply jumps towards Eend = –0.5V (HgO/Hg) after electrode full dehydrogenation. Maximum discharge capacity (298 mAh·g–1 at –0.5C/+0.5C i.e. –186/+186 mA·g−1 ) has been achieved after N = 31 cycles. The HRD markedly decreases with electrode cycling. After 15 cycles the HRD falls to 46.8 % at discharge rate of 5C. The SEM examinations reveal severe structural deterioration of the electrode, especially evident after 60 cycles at the greatest discharge rates.

PL

Dyskutowane jest elektrochemiczne zachowanie cyklowanego stopu wodorochłonnego LaNi4,5Co0,5 w środowisku 6M KOH, przy wzrastających szybkościach rozładowania. Dla wyznaczenia zdolności do rozładowywania przy wysokich prądach anodowych (HRD), zastosowano technikę galwanostatycznych krzywych ładowania/rozładowania. Zmiany HRD mierzono po N = 15 i N = 60 cyklach. Proces anodowego rozładowania dla dwu wymienionych opcji wykazywał typowe przebiegi: potencjał elektrodowy nieznacznie wzrasta, po czym, po całkowitym utlenieniu wodoru, obserwuje się jego gwałtowny skok do wartości Eend = –0,5V (HgO/Hg). Maksymalną pojemność rozładowania (298 mAh·g–1 przy –0,5C/+0,5C, tj. –186/+186 mA·g−1 ) elektroda osiąga po N = 31 cyklach. Parametr HRD wyraźnie maleje wskutek cyklowania. Po 15 cyklach HRD osiąga poziom 46,8% dla szybkości rozładowania równej 5C. Obserwacje SEM ujawniają silną destrukcję strukturalną elektrody, szczególnie ewidentną dla 60 cykli przy największych szybkościach rozładowania.

3

Wyposażenie mostów i kontrola drgań

Stefaniak A.

Mosty

|

2018

|

nr 3/4

68--72

PL

W artykule przedstawiono urządzenia wyposażenia i kontroli drgań mostów. Szerzej opisano masowe tłumiki drgań oraz urządzenia tłumienia wiskotycznego.

EN

Every bridge must be designed in a way that enables it to deform in ranges anticipated by the designer and disables to develop excessive forces that could cause the structure overload. Bridge bearings, expansion joints, tuned mass dampers and viscous damping devices are special products aimed at conforming to the above design requirements. The article presents the devices of bridge equipment and vibration control. Tuned mass dampers and viscous damping devices have been described in detail.

4

Ocena szybkości dyfuzji atomowego wodoru w kompozytowej elektrodzie LaNi4,5Co0,5

Stefaniak A., Bordolińska K., Bala H.

Przemysł Chemiczny

|

2017

|

T. 96, nr 9

1939--1941

PL

Za pomocą metody Randlesa i Sevčika oceniono szybkość dyfuzji atomowego wodoru w kompozytowej elektrodzie LaNi4,5Co0,5. Ze względu na powolny transport wodoru w obrębie cząstek materiału aktywnego stosowano małe szybkości polaryzacji (0,01-0,1 mV/s). Przed każdym pomiarem woltamperometrycznym elektrody ładowano wodorem galwanostatycznie, dla zapewnienia im stężenia wodoru na poziomie 0,06 mol/cm3. Zmierzone wartości efektywnych współczynników dyfuzji (DH ok. 3·10-10 cm2) są obarczone błędem wynikającym z niepewności co do rzeczywistej powierzchni materiału aktywnego (S) w obrębie elektrody, dlatego bardziej miarodajny dla oceny jest iloczyn S2·DH. Iloczyn ten dla badanego materiału przyjmuje wartości ok. 10-8 cm6/s i maleje nieco ze wzrostem szybkości polaryzacji.

EN

The Randles-Sevčik relationship was used to evaluate at. H2 diffusivity in LaNi4.5Co0.5 composite electrode at low polarization rates (0.01–0.1 mV/s). The electrodes were cathodically hydrogenated before voltammetric measurements to provide them H2 concn. 0.06 mol/cm3. The effective diffusion coeffs. were affected by errors from the actual surface area of the active material (S), therefore more reliable for evaluation is the ratio of S2DH.

5

Passivation of hydrogen storage alloy in strong alkaline solution

Bala H., Bordolińska K., Stefaniak A.

Ochrona przed Korozją

|

2017

|

nr 9

314--317

EN

Anodic potentiodynamic polarization of dehydrogenated LaNi4.5Co0.5 compact electrode at very slow potential scan rate has been applied to evaluate material corrosion rate in 6 M KOH within passive region. Chronoamperometric measurements carried out at E = –0.2 V (HgO/Hg) allowed to obtain steady state anodic current of electrode passivation which corresponds to alloy stationary corrosion rate. It has been shown that corrosion rate determined in such a way is in very good agreement with alloy initial corrosion rate found on the basis of capacity fade of powdered, composite electrode prepared from this material.

PL

Do oceny szybkości korozji pozbawionej wodoru litej elektrody LaNi4.5Co0.5 w 6 M roztworze KOH zastosowano technikę potencjodynamicznej polaryzacji przy bardzo powolnym skaningu potencjału. Pomiary chronoamperometryczne wykonane przy E = –0,2 V (HgO/Hg) pozwoliły znaleźć ustaloną wartość prądu anodowego pasywacji elektrody, który odpowiada stacjonarnej szybkości korozji. Pokazano, że szybkość korozji wyznaczona w ten sposób jest w bardzo dobrej zgodności z początkową szybkością korozji znalezioną na podstawie spadku pojemności proszkowej, kompozytowej elektrody wykonanej z tego materiału.

6

Effect of surface modification of LaNi4.5Co0.5 active material on electrochemical parameters of hydride electrode in conditions of long-lasting cycling

Stefaniak A., Bordolińska K., Sozańska M.

Ochrona przed Korozją

|

2016

|

nr 9

330--333

EN

The analysis of galvanostatic charge/discharge curves for the hydrogen powder electrode in long-term cycling conditions (N = 40 cycles) is presented. The surface of active powder (LaNi4.5Co0.5; fraction 20÷50 μm) has been modified by 8-hours magnetron sputtering using Fe-Si target. The effect of deposition of thin Fe-Si layers on functional parameters of modified electrode has been characterized. It has been shown that magnetron sputtering scarcely affects electrode discharge capacity, but it decreases a little the slope of rectilinear segment of logQdisch = f(N) relationship, thus, inhibits the corrosion degradation of the electrode. For N > 22 cycles hydride capacity of modified electrode reaches practically constant level, close to 270 mAh/g, which testifies to disappearance of corrosion degradation. The sputtered layers improve the kinetics of hydrogen electrosorption because their presence increases exchange current density of H2O/H2 system.

PL

Dokonano analizy krzywych galwanostatycznego ładowania/rozładowania dla wodorkowej elektrody proszkowej w warunkach długotrwałego cyklowania (N = 40 cykli). Powierzchnię proszku aktywnego (LaNi4.5Co0.5; frakcja 20÷50 μm) modyfikowano poprzez 8-godzinne rozpylanie jonowe stopu Fe-Si stanowiącego target. Scharakteryzowano wpływ osadzania cienkich warstw Fe-Si w zależności od parametrów użytkowych zmodyfikowanej elektrody. Pokazano, że proces rozpylania ma niewielki wpływ na pojemność rozładowania, jednak zmniejsza nieco nachylenie odcinka prostoliniowego zależności logQrozł = f(N), tym samym hamuje degradację korozyjną elektrody. Dla N > 22 cykli pojemność wodorkowa elektrody modyfikowanej osiąga praktycznie stały poziom, ok. 270 mAh/g, co świadczy o zaniku degradacji korozyjnej. Warstwy napylone poprawiają również kinetykę elektrosorpcji wodoru, gdyż w ich obecności zwiększa się gęstość prądu wymiany układu H2O/H2.

7

Effect of magnetron sputtering of active powder with Fe-Cr-Ni layers on electrochemical parameters of metal hydride electrode

Bordolińska K., Stefaniak A., Bala H.

Ochrona przed Korozją

|

2016

|

nr 2

43--45

EN

Particles of hydrogen storage, LaNi4.5Co0.5 powdered material have been encapsulated with thin (about 40 nm) Fe-Cr-Ni layers using magnetron sputtering method. The acid resistant, 1.4301 (EN 10088) stainless steel has been applied as a target. The effect of powder encapsulation on galvanostatic charge/discharge characteristics (hydride capacity, exchange current density of the H2O/H2 system, susceptibility to oxidation) for the modified hydride electrodes has been evaluated. The plots of discharge curves testify to limitation of active material tendency to working surface development. The material modified reveals comparatively high discharge capacities which should be attributed to inhibition of oxidation processes of active material by the surface layers formed. The powder sputtering does not worsen the kinetics of charge/discharge processes for modified electrode.

PL

Cząstki proszku materiału wodorochłonnego LaNi4,5Co0,5 enkapsulowano cienkimi (ok. 40 nm) warstwami Fe-Cr-Ni poprzez napylanie magnetronowe, z użyciem stali kwasoodpornej 1,4301 (EN 10088) jako targetu. Oceniono wpływ enkapsulacji proszku na parametry galwanostatycznego procesu ładowania/rozładowania (pojemność wodorkowa, gęstość prądu wymiany układu H2O/H2, podatność na utlenianie) dla zmodyfikowanej w ten sposób elektrody wodorkowej. Przebieg krzywych rozładowania wskazuje, iż po procesie enkapsulacji zmniejsza się podatność materiału aktywnego na rozwijanie powierzchni roboczej. Materiał enkapsulowany wykazuje stosunkowo wysokie pojemności rozładowania, co jest konsekwencją hamowania procesów utleniania materiału aktywnego przez wytworzone warstwy. Napylanie proszku nie pogarsza kinetyki procesów ładowania/rozładowania zmodyfikowanej elektrody.

8

Characterization of hydride electrode modified with Fe-Si layers by sputtering

Stefaniak A., Bordolińska K., Bala H.

Ochrona przed Korozją

|

2016

|

nr 4

91--93

EN

Magnetron sputtering method has been employed for deposition of thin Fe-Si layers on active powder substrate of LaNi4.5Co0.5 hydrogen storage alloy. The sputtering process was carried out through two different time periods. Cyclic galvanostatic charge/ discharge curves have been measured to evaluate the effect of sputtering time on the characteristic parameters of modified hydride electrode. The discharge capacity (Qdisch) of modified LaNi4.5Co0,5 powder alloy corresponding to N = 10 cycle was 229 and 250 mAh∙g−1 after 2 and 8 h of sputtering, respectively. The longer sputtering time the greater exchange current densities of H2O/H2 system on the modified electrodes. The exchange currents matching 10th cycle were 38 and 53 mA∙g−1 after 2 and 8 hours of sputtering, respectively.

XX

Metodę napylania magnetronowego zastosowano do osadzania cienkich warstw Fe-Si na podłożu sproszkowanego stopu wodorochłonnego LaNi4.5Co0.5. Proces napylania był prowadzony w dwu wybranych okresach czasu. Dla oceny wpływu czasu osadzania warstw na charakterystyczne parametry zmodyfikowanych w ten sposób elektrod wodorkowych, zmierzono dla nich galwanostatyczne krzywe ładowania/rozładowania. Pojemność rozładowania (Qdisch) odpowiadająca N = 10 cyklowi, w przypadku modyfikowanego proszku LaNi4,5Co0,5 wynosiła odpowiednio 229 i 250 mAh∙g−1 dla czasów napylania 2 i 8 h. Wydłużenie czasu napylania prowadzi również do wzrostu gęstości prądów wymiany układu H2O/H2 dla badanych elektrod, które po 10 cyklu były równe 38 i 53 mA∙g−1, odpowiednio dla czasów napylania 2 i 8 h.

9

Manufacturing of thin Fe-Cr-Ni coatings on Cu powder substrate using magnetron sputtering technique

Stefaniak A., Bordolińska K.

Ochrona przed Korozją

|

2015

|

nr 7

261--263

EN

The magnetron sputtering technology has been applied to obtain thin coatings on high purity, Cu powder particles. The circular plates of AISI 304L (00H18N10) type stainless steel were used as sputtering targets. The Cu powder was introduced into drum-shaped rotary stage and the sputtering process was carried out under vacuum. During deposition the powder samples were periodically taken from the reaction chamber for analysis. Afterward, the Fe-Cr-Ni coatings were subjected to acid etching and the obtained solutions were analyzed on Fe2+, Cr3+ and Ni2+ ions content. The results of analysis allowed to estimate the coating thickness. After some induction period, the amounts of Fe, Ni and Cr in the coating were directly proportional to the sputtering time. The proportions of individual metal components in the coating appeared to have been very close to their proportions in the applied steel. The thickness of the sputtered layers of Fe-Cr-Ni coating was 46 nm after 3 h of the PVD process.

PL

Technologię napylania magnetronowego wykorzystano do otrzymywania cienkich powłok na cząstkach proszku miedzi o dużej czystości. Jako targetów napylających używano okrągłych płytek ze stali AISI 304L (00H18N10). Proszek miedzi umieszczano w mieszalniku obrotowym w kształcie bębna, po czym prowadzono proces napylania próżniowego. W trakcie napylania próbki proszku były okresowo pobierane z komory reakcyjnej do analizy. Następnie, powłoki Fe-Cr-Ni wytrawiano kwasowo a otrzymane roztwory analizowano na zawartość jonów Fe2+, Cr3+ i Ni2+. Wyniki analizy pozwoliły oszacować grubość powłok. Po krótkim okresie wstępnym, ilości Fe, Ni i Cr w powłoce stawały się wprost proporcjonalne do czasu napylania. Proporcje poszczególnych pierwiastków w powłoce osiągały wartości bliskie proporcjom w użytej stali. W wyniku trwającego 3 h procesu PCV uzyskano powłoki Fe-Cr-Ni o o grubości 46 nm.

10

Analiza składu chemicznego i fazowego cienkich powłok Fe-Cr wytworzonych na proszku Cu przy użyciu techniki napylania magnetronowego

Bordolińska K., Stefaniak A., Pawlik P.

Hutnik, Wiadomości Hutnicze

|

2015

|

Vol. 82, nr 10

666-669

PL

Wytwarzano cienkie powłoki Fe-Cr na podłożu sproszkowanej miedzi metodą fizycznego osadzania z fazy gazowej. Jako materiału napylającego użyto stali nierdzewnej 1,4021 (AISI 420). Próbki proszku do analizy pobierano okresowo podczas procesu napylania. Uzyskane powłoki roztwarzano w kwasie solnym, a otrzymane roztwory analizowano na obecność jonów Fe2+ i Cr3+. Stwierdzono, że ilości Fe i Cr w powłoce są wprost proporcjonalne do czasu napylania. Proporcje obu składników w powłoce były zbliżone do składu chemicznego zastosowanego targetu. Skład fazowy warstwy powierzchniowej proszku analizowano metodą asymetrycznej dyfrakcji promieniowania rentgenowskiego (XRD). Analiza nie wykazała obecności miedzi w otrzymanych powłokach.

EN

Thin Fe-Cr coatings have been deposited by physical vapor deposition on powdered copper substrate. The 1,4021 (AISI 420) stainless steel was used as a sputtering material. The powder samples were being taken periodically for analysis during sputtering process. The obtained Fe-Cr coatings were subjected to etching in hydrochloric acid and solutions - analyzed on Fe2+ and Cr3+ content. It was found that the amounts of Fe and Cr in the coatings were directly proportional to the sputtering time. The proportions of both elements in the layer are close to their contents in the applied target. The phase composition of the powder surface layers was analyzed by glancing angle X-Ray Diffraction (XRD). The analysis did not reveal the presence of the copper in the obtained coatings.

11

Systemy hybrydowe odnawialnych źródeł energii

Stefaniak A.

Czysta Energia

|

2013

|

Nr 11

22--23

12

Pomiar mocy traconej w magnesach nadprzewodnikowych akceleratora

Kosobudzki G., Stefaniak A.

Przegląd Elektrotechniczny

|

2010

|

R. 86, nr 4

66-68

PL

W artykule przedstawiono wpływ różnych czynników na dokładność wyznaczania mocy obiektów o bardzo małym współczynniku mocy. Analizę teoretyczną poparto wynikami badań mocy strat elektromagnesu nadprzewodzącego.

EN

The influence of some important factors on the result of power measurement of low power factor load was shown. The theoretical analysis was verified by investigation of real measurement data of superconducting magnets.

13

Numeryczne modelowanie zużycia wykrojów podczas walcowania kształtownika łebkowego HP220

Mróz S., Szota P., Stefaniak A.

Archiwum Technologii Maszyn i Automatyzacji

|

2010

|

Vol. 30, nr 3

159-168

PL

W artykule omówiono numeryczne modelowanie walcowania kształtowników łebkowych HP220 pod kątem wpływu kalibrowania walców na zużycie wykrojów kształtowych. W symulacjach komputerowych wykorzystano program komputerowy Forge2008Ž. Jest on oparty na metodzie elementów skończonych, pozwala na termomechaniczną symulację procesów walcowania w trójosiowym stanie odkształcenia. W modelu zużycia stosowanym w programie komputerowym Forge2008Ž wykorzystano uproszczony model Archarda.

EN

In this work results of the numerical modeling of the bulb bars HP220 rolling process from the point of view of influence of roll pass design on the wear of shape groove are presented. For carrying out the simulation, the computer program Forge2008Ž was used. The program relies on the finite-element method and allows the thermo-mechanical simulation of rolling processes in a three-axial state of strain. In the wear model implemented in Forge2008Ž computer program the Archard model was used.

14

System szkoleń wstępnych w dziedzinie bezpieczeństwa i higieny pracy oraz adaptacji zawodowej w zakładach górniczych Kompanii Węglowej S.A.

Stefaniak A., Pakura A., Kowalkowski W.

WUG : bezpieczeństwo pracy i ochrona środowiska w górnictwie

|

2009

|

nr 3

15-18

PL

Przedstawiono podstawowe akty prawne regulujące szkolenia w dziedzinie bezpieczeństwa i higieny w podziemnych zakładach górniczych oraz w zakresie dopuszczania pracowników do pracy w ruchu zakładu górniczego. Omówiono zasady szkoleń wstępnych i adaptacji zawodowej w kopalniach węgla kamiennego Kompanii Węglowej S.A. Opisano również działania podjęte w KW S.A. w celu odpowiedniego przygotowania kadry do pracy w górnictwie, ze szczególnym uwzględnieniem osób bez przygotowania zawodowego.

EN

Presented are basic legal acts regulating training in the field of safety and health in the underground mining plants and approval of workers to work in the mining plants. Discussed are rules of introductory training and professional adaptation in the hard coal mining plants of the Kompania Węglowa S.A. Described are also activities performed in the Kompania Węglowa S.A. aimed at personnel preparation to work in mining with special account of persons without professional qualifications.

15

Zakłady utylizacji odpadów jako ważne ogniwo w kompleksowej gospodarce odpadami doświadczenia Arki Konsorcjum S.A.

Stefaniak A.

Zeszyty Naukowe Politechniki Rzeszowskiej. Budownictwo i Inżynieria Środowiska

|

2000

|

z. 32[180], cz.2

395-403

EN

This report concerns the designing and executive solutions for municipal waste utilisation in Poland applied by Arka Konsorcjum.1. Introduction: Conditions of technology's choice for waste utilisation plants. The experience of Arka Konsorcjum in realisation of waste utilisation plants. 2. The issue of waste utilisation plants. 3. The characteristic of solutions for waste utilisation plants. 4. The characteristic of Waste Utilisation Plant in Gorzów Wielkopolski. 5. Conclusions.

16

Kwalifikacje, szkolenia i motywowanie pracowników w procesie restrukturyzacji zakładów górniczych

Migda J., Stefaniak A.

WUG : bezpieczeństwo pracy i ochrona środowiska w górnictwie

|

2000

|

nr 6

27-28

17

Kierunki optymalizacji kosztów materiałów wsadowych, eksploatacyjnych i energii w procesie wytwarzania stali

Zdonek B., Mazur A., Szypuła I., Stefaniak A.

Prace Instytutu Metalurgii Żelaza

|

2000

|

T. 52, z. 2

30-37

PL

Określono możliwości i kierunki optymalizacji kosztów produkcji surowej stali w procesie konwertorowym i elektrycznym, w krajowym hutnictwie. Możliwości optymalizacji kosztów produkcji dotyczą zmniejszenia kosztów materiałów wsadowych, eksploatacyjnych i energii. Do najważniejszych kierunków w dążeniu do zmniejszenia tych kosztów zalicza się: uelastycznienie zestawiania wsadu, stosowanie sposobów wydłużania trwałości wyłożenia ogniotrwałego pieców i kadzi, poprawę stopnia automatyzacji i ciągłości procesu wytwarzania surowej stali, stosowanie techniki wpływającej na wzrost uzysku żelaza.

EN

Prospects and directions of cost optimisation in production of crude steel in oxygen converters and electric arc furnaces were estimated first of all by reduction of raw material, operational and utility costs by more flexible raw material selection, life improvement of furnace and ladle linings, better automatic control, more continuous operation and improvement of yields.