Erosion resistance testing of plastic pipes

Stabik J., Makselon M., Tomanek H.

Journal of Achievements in Materials and Manufacturing Engineering

|

2007

|

Vol. 25, nr 2

47-50

EN

Purpose: The purpose of this paper was to present the results of a special abrasion test of poly(vinyl chloride) and polypropylene filled with calcium carbonate pipes. Abrasion test's results for pipes were compared with results of standard abrasion test (Taber method) and hardness test. Design/methodology/approach: Short cuts of pipe were subjected to erosion caused by erodent, usually a mixture of special kind of sand and water. The changes of pipe's wall thickness was a measure of resistance to erosion. Additionally abrasion resistance was measured using Taber method and ball-hardness was measured using Brinell apparatus. Findings: Calcium carbonate filled polypropylene exhibited lower resistance to abrasion than hard poly(vinyl chloride). Probably it is the result of filler presence in polypropylene. No correlation between hardness and abrasion resistance was found. Research limitations/implications: Applied method may be used to compare different pipe's materials but its results may not be applied to other plastics products and to other abrasion conditions. Practical implications: Abrasion test used in the research may be applied to compare different materials and different pipelines components. Achieved results showed that calcium carbonate without surface preparation decrease abrasion resistance of polypropylene. Originality/value: Applied method is rarely used for polymer materials testing. Results of presented research may be interesting for pipe manufactures and polymer pipe's formulations producers.

2

Badania nieniszczące niektórych właściwości laminatów epoksydowo-szklanych

Makselon M., Rojek M., Stabik J.

Zeszyty Naukowe. Chemia i Technologia Chemiczna / Akademia Techniczno-Rolnicza w Bydgoszczy

|

2006

|

z. 11

91-95

PL

Stosowanie tworzyw polimerowych jako materiałów konstrukcyjnych wymaga wiedzy o ich trwałości. W warunkach użytkowych nie zawsze istnieje możliwość korzystania z "klasycznych" (niszczących) metod oceny zmian właściwości wy-trzymałościowych materiałów konstrukcyjnych. Dlatego też celowe jest poszuki-wanie takich metod nieniszczących, które pozwalają na określenie stanu materia-łów konstrukcyjnych. Niniejsza praca jest próbą zastosowania techniki ultra-dźwiękowej w celu diagnozowania właściwości wytrzymałościowych laminatu epoksydowo-szklanego poddanego długotrwałym i zmiennym obciążeniom.

EN

By the use of polymeric materials for construction devices, the knowledge of its durability is necessary. In common application conditions the use of "classical" (destructive) method of properties measurements is not always possible. Therefore, it is important to look for new non-destructive methods, allowing determining the state of properties of construction materials. In this work the ultrasonic measurement technique was applied for the assessment of mechanical resistance of epoxy-glass fiber composite, after long time cyclic load.

3

Próba zastosowania techniki ultradźwiękowej dla oceny stopnia wyczerpania wytrzymałości kompozytów epoksydowo-szklanych

Makselon M., Rojek M., Wróbel G.

Przetwórstwo Tworzyw

|

2004

|

[R.] 10, nr 3

74-84

PL

Popularność tworzyw polimerowych jako materiałów konstrukcyjnych powoduje wzrost zapotrzebowania na wiedzę na temat ich trwałości. Możliwość pozyskania takiej wiedzy warunkuje prognozowanie okresu niezawodnej pracy elementów konstrukcyjnych oraz systemów je zawierających. Dlatego też, istnieje potrzeba poszukiwania nieniszczących metod bezpośredniej oceny stopnia degradacji wytrzymałościowej materiałów konstrukcyjnych. Autorzy podjęli taką próbę z zastosowaniem techniki ultradźwiękowej. Poszukiwania metody diagnozowania stanu materiału odniesiono do kompozytów poddanych obciążeniom zmęczeniowym.

EN

The popularity of polymer plastics applied as constructional materials results in the demand of knowledge concerning the durability of materials. This knowledge is indispensable for the prognosis of the safe service duty of both constructional elements and system containing them. Therefore there is a need to look for the non-destructive methods of the direct estimation of the degree of strength degradation of constructional materials. The authors undertook this trial by using of ultrasonic technique. Searching of the method for diagnosis of the condition of materials was related the composite materials under fatique load.