Synthesis of samarium oxide layers by MOCVD method

Sawka A., Kwatera A., Bućko M., Cholewa-Kowalska K., Halski D.

Inżynieria Materiałowa

2007

Vol. 28, nr 3-4

733-735

This work presents results of investigations on synthesis of samarium oxide layers on quartz glass by MOCVD method using samarium tris(2,2,6,6-tetramethyl-3,5-heptanedionate) as precursor. Air and argon were used as carrier gases. Air was also necessary for elimination of carbon - solid by product of Sm(tmhd)3 pyrolisis. Sm203 layers were deposited in the range of temperatures 500-700°C. The temperature of Sm(tmhd)3 vapours was changed from 200 to 300°C. The synthesis time was 15-30 min. The other parameters of synthesis process were established in a such way to assure the value of extended criterion Grx/Rex2<0,01. This research is related to works on obtainment of a new composite electrolyte (Ce02+Sm203/Zr02+Y203) for solid oxide fuel cells (SOFC).

W pracy przedstawiono wyniki badań nad syntezą warstw tlenku samaru na szkle kwarcowym metodą MOCVD z użyciem tetrametylohepanodionianu samaru jako prekursora. Powietrze i argon stosowano jako gazy nośne. Powietrze było również konieczne do eliminacji węgla - ubocznego produktu pirolizy Sm(tmhd)3. Warstwy Sm203 osadzano w temperaturach 500-700°C. Temperaturę par Sm(tmhd)3 zmieniano od 200 do300°C. Czas syntezy warstw wynosił 15-30 min. Pozostałe parametry procesu syntezy tak dobierano, by wartość rozwiniętego kryterium Grx/Rex2<0,01. Badania te związane są z pracami nad otrzymaniem nowego kompozytowego elektrolitu (Ce02+Sm203/Zr02+Y203) dla tlenkowych ogniw paliwowych (SOFC).