Modification of asphalt binders by polyethylene-type polymers

Brożyna D., Kowalski K. J.

Journal of Building Chemistry

2016

Vol. 1, iss. 1

37-41

This investigation tested the effects of asphalt binder modification, using polyethylene-type polymers. During the research, five different polymers were used: HDPE, LDPE, LLDPE, copolymer EBA (ethylene/butyl acrylate) and terpolymer EBM (ethylene/butyl acrylate/maleic anhydride). Those polyethylene-type polymers were used to in-lab modification of 50/70 raw unmodified road bitumen. Modified specimens were tested in terms of penetration, softening temperature and elastic recovery. Samples were aged using the Rolling Thin Film Oven Test procedure. The gathered data suggest that addition of polyethylene-type polymers to the asphalt binders reduces penetration, and increases softening temperature. In terms of elastic recovery only terpolymer EBM presented significant improvement, reaching a 75% relative elastic recovery.

Assessment of polyethylen-modified bitumen adhesion using computer image analysis

Brożyna D., Kowalski K. J.

Archives of Civil Engineering

2016

Vol. 62, nr 4/II

3--18

In order to achieve extended life of asphalt pavement, one of key points is to achieve a good bonding between it’s components. This research paper presents findings on the topic of influence of polyethylene bitumen modification on the adhesion between bitumen and aggregate. A novel method of quantifying the bitumen coated area, based on computer image analysis, has been developed for this study. Two different methods of adhesion testing were employed, namely boiling water method and the rolling bottle method. Aggregates used in this study were granite and limestone. Based on 108 measurements, it was concluded that polyethylene modification has a negative impact on binder aggregate adhesion.

W związku ze stale rosnącą wielkością ruchu drogowego, dla prawidłowego rozwoju gospodarki, niezbędna jest budowa trwałych nawierzchni drogowych. Jednym ze sposobów osiągnięcia tego celu jest zastosowanie wysokiej jakości mieszanek mineralno-asfaltowych (MMA). Mieszanki te są kompozytami kruszyw oraz lepiszczy asfaltowych. Tematyka adhezji pomiędzy lepiszczami a kruszywem była przedmiotem badań prezentowanych w wielu publikacjach, np. [6, 11, 18 and 20]. Stwierdzić należy, że stosunkowo mało uwagi zostało poświęcone tematyce wpływu modyfikacji lepiszczy asfaltowych polietylenami na ich adhezję do kruszyw [1]. Celem badań prezentowanych w artykule była oceny wpływu modyfikacji lepiszczy asfaltowych polietylenami na zjawisko adhezji pomiędzy kruszywem a lepiszczem.