Thermoplastic film from superfine wool powder

Wang X., Xu W., Li W., Wang X. G.

Fibres & Textiles in Eastern Europe

2009

Vol. 17, no. 2 (73)

82--86

In this paper a research work is described in which superfine wool powder was plasticised by glycerol and hot-pressed into a kind of thermoplastic film. SEM photos show that the powder is moulded into a smooth surface and is conglutinated into a continuous phase in the cross-section of the film. The glycerol content, moulding pressure, temperature and moulding time were changed in the moulding process. The sizes and thickness aw well as tensile strength, modulus, breaking elongation and breaking energy of the films were also tested to investigate the thermoplasticity and mechanical properties of the films. The best moulding techniques included a glycerol content of 30%, a moulding pressure of 5 MPa, a temperature of 160 °C and a moulding time of 5 minutes.

W artykule przedstawiono badania , w których super drobny pył wełniany był plastyfikowany gliceryną i prasowany na gorąco dla otrzymania termoplastycznych błon. Fotografie SEM wskazują, że pył został stopiony i przetworzony w folie o gładkiej powierzchni oraz przekroju poprzecznym charakterystycznym dla fazy ciągłej. W trakcie badań zmieniano zawartość gliceryny, ciśnienie wywierane podczas topienia, temperaturę i czas obróbki. Dla wykonanych folii określano wielkość cząstek, grubości folii, wytrzymałość, moduł, wydłużenie przy zerwaniu oraz energię zrywania. Pozwoliło to na określenie termoplastyczności folii i ich właściwości mechanicznych. Najlepsze wyniki uzyskano przy zawartości gliceryny 30%, ciśnieniu 5Mpa, temperaturze 160 0C i czasie obróbki 5 min.