The influence of the parameters of electrolysis carried out with periodic reversal current (PRC) on the morphology of silver obtained via silver chloride cathodic reduction

Ciuman-Krzemień A., Gumowska W., Burzyńska L.

Archives of Metallurgy and Materials

|

2012

|

Vol. 57, iss. 1

155-164

EN

The aim of this study was to determine the possibility to obtain compact silver deposit during cathodic reduction of AgCl with the use of periodic reversal current (PRC). The influence of the electrolysis parameters (current intensity I = 0.4-1.6 A, the ratio of working to reversal periods tw/trv = 100/10; 100/20; 100/30) on the silver morphology (size and shape of Ag grains). Under the applied electrolysis conditions powder deposits were obtained, but at I = 0.4 A and tw/trv = 100/10 a more compact deposit was produced. Cathode efficiencies of the processes were low and ranged from approx. 52% up to 85%.

PL

Celem pracy było zbadanie możliwości uzyskania srebra w postaci litego osadu w procesie elektrolizy z zastosowaniem okresowej zmiany kierunku przepływu prądu (PRC). Badano wpływ parametrów elektrolizy (natężenie prądu I = 0,4-1,6 A oraz stosunek okresów "roboczego" do odwrotnego kierunku przepływu prądu: tw/trw = 100/10, 100/20, 100/30) na morfologię srebra (wielkość i kształt ziaren Ag). W warunkach stosowanych w procesie elektrolizy uzyskano osady srebra w postaci proszków. Srebro w postaci zwartego osadu uzyskano jedynie podczas elektrolizy z zastosowaniem natężenia prądu 0,4 A oraz stosunku tw/trw = 100/10. Katodowe wydajności prądowe są stosunkowo niskie i wynoszą od około 52% do 85%.

2

Wybrane właściwości kompozytowych styków elektrycznych na osnowie srebra umacnianych TiB2, SiC oraz WO2

Ciuman-Krzemień A., Burzyńska L., Galanty M.

Kompozyty

|

2008

|

R. 8, nr 2

152-157

PL

Przedstawiono prosty sposób otrzymywania kompozytowych styków elektrycznych srebro-ceramika. Jako osnowę kompozytów zastosowano proszek srebra o unikalnych właściwościach, uzyskany metodą katodowej redukcji jonów Ag+ z AgCl w ogniwie Zn|0,5MH2SO4,AgCl|Ag. Metoda ta pozwala na recykling surowców wtórnych lub odpadowych zawierających srebro. Istnieje ponadto możliwość użycia w charakterze anody złomu cynkowego, stalowego bądź też aluminiowego. Fazę umacniającą stanowiły ceramiczne proszki borku tytanu, węglika krzemu lub dwutlenku wolframu. Srebro łączono z ceramiką na drodze metalurgii proszków (mieszanie-prasowanie-spiekanie). Kompozyty prasowano pod ciśnieniem 500 MPa, a następnie spiekano w temperaturze 850°C przez 45 minut w atmosferze argonu. Zbadano wpływ składu na właściwości mechaniczne i elektryczne otrzymywanych kompozytów. Stwierdzono, że wraz ze wzrostem zawartości dodatków ceramicznych do srebra obserwuje się pogorszenie zgęszczalności prasowanych próbek. Dodatek ceramiki do proszku srebra zapobiega jednak występowaniu pęcznienia wyprasek, w porównaniu z kształtką srebrową, podczas procesu ich spiekania. Istnieje korelacja pomiędzy gęstością względną spieków srebro-ceramika, a ich twardością oraz przewodnictwem właściwym. Otrzymane styki kompozytowe srebro-ceramika charakteryzują się wysokim przewodnictwem właściwym (nawet ponad 40 MS/m) i niską rezystancją przejścia (malejącą ze wzrostem siły docisku i niezależną od wielkości przyłożonego prądu elektrycznego). Uzyskano materiały o małej porowatości otwartej.

EN

The simple method for producing silver-ceramics composite contacts was presented. The composite matrix comprises powdered silver that has unique properties, which is obtained in a cathodic reduction of Ag+ -ions with AgCl in the Zn |0.5MH2SO4,AgCl| Ag cell. This method enables the recycling of secondary or waste raw materials that contain silver. It is also allowed to use zinc, steel, or aluminum scrap as the anode. The reinforcing phase consists of ceramic powder materials - titanium boride, silicon carbide, or tungsten dioxide. Silver was combined with ceramic materials using powder metallurgy technologies (mixing - pressing - - sintering). The composites were pressed under 500 MPa of pressure and subsequently sintered at 850° C for 45 minutes in an argon atmosphere. The effect of the chemical composition of the obtained composites on the mechanical and electrical properties was examined. The increase of the content of the ceramic additives in the silver com posites is accompanied with the deterioration of the compressibility of pressed samples. The addition of ceramics in powdered silver prevents compact growth during the sintering process, as compared to a silver compact. There exists a correlation between the relative density of silver-ceramics sinters and their hardness and electrical conductivity. The obtained silver-ceramics composite contacts have a high electrical conductivity (even above 40 MS/m) and low contact resistance (decreasing with growing contact force and independent of the applied current). The open porosity of the obtained materials is low.

3

Ogniwa słoneczne w sektorze komunalnym

Ciuman-Krzemień A., Kowalik R., Norwisz J.

Rynek Instalacyjny

|

2005

|

nr 11

66--70

PL

Promieniowanie słoneczne stanowi największe źródło czystej i odnawialnej energii, którym mogłoby dysponować społeczeństwo. Do powierzchni Ziemi dociera energia mocy rzędu 81·109 MW, z czego 27·109 MW przypada na obszary lądowe. Wartość tę można zestawić wobec światowego zapotrzebowania energetycznego – ok. 0,01·109 MW. Wadą tego źródła jest jednak jego mała gęstość „energetyczna”, przy czym lokalna moc promieniowania słonecznego w istotnym stopniu zależy od szerokości geograficznej danego obszaru. Dla Polski wynosi rocznie od 8400 MJ m–2 (2340 kWh m–2) dla północnych krańców, do 9250 MJ m–2 (2573 kWh m–2) dla południowych [3].

4

Recovery of silver from AgCl by using the cell Zn/H2SO4, AgCl/Ag

Burzyńska L., Harańczyk I., Ciuman-Krzemień A.

Archives of Metallurgy and Materials

|

2004

|

Vol. 49, iss. 1

169-181

EN

Recovery of Ag from AgCl by its direct reduction was investigated in the cell Zn | H2SO4, AgCl | Ag, where AgCl did not directly contact with the reducing metal. Observed sudden drop of the current and of the Ag | AgCl electrode potential indicated the end of the reduction process. An equation describing dependence of the current intensity in the cell Zn | H 2SO4, AgCl | Ag on reduced time was derived and discussed. Current efficiency and reduction degree were also determined. Influence of the concentration of sulfuric acid on the rate of the process and on the size of the reduced silver grains was studied.

PL

Badano proces odzysku srebra metodą katodowej redukcji AgCl przy użyciu ogniwa Zn/H2SO4,AgCl/Ag. Stwierdzono, że zakończeniu procesu redukcji odpowiada nagły spadek mierzonych wartości natężenia prądu oraz potencjału katody Ag/AgCl. Wyprowadzono równanie empiryczne opisujące zależność nateżenia pradu od czasu zredukowanego. Wyznaczono katodową wydajność prądu oraz stopień redukcji. Przedyskutowano wpływ steżenia kwasu na szybkość procesu oraz na wielkość ziaren otrzymanego proszku srebra.

5

Kompozyty na osnowie srebra umacniane cząstkami dyspersyjnymi. Materiały stykowe.

Burzyńska L., Ciuman-Krzemień A.

Rudy i Metale Nieżelazne

|

2002

|

R. 47, nr 9

461-467

PL

Podano charakterystykę własności kompozytów na osnowie srebra umacnianych różnymi typami cząstek dyspersyjnych. Kompozyty te otrzymano w wyniku połączenia dwóch metod: bezprądowego nakładania powłok i prasowania na gorąco.

EN

Characteristics of the properties of different kind of ceramics-reinforced silver matrix composites are described in this paper. These composites were produced by electroless plating and hot pressing.