Improvement of Microstructure and Barrier Properties of Silicate Coatings on Low Carbon Steel by Incorporating Colloidal Nano-SiO2

Majdi M. R., Danaee I., Zaarei D., Farzam M.

Archives of Metallurgy and Materials

2020

Vol. 65, iss. 2

627--638

Silicate coatings have been considered as an alternative to toxic and carcinogenic other chemical treatments. In this paper, a strengthened silicate coating was formed on the surface of low carbon steel by dip immersion method. The modification and strengthening was done by loading colloidal nano-SiO2 into the film. The characterizations of nano-SiO2 were investigated by FESEM, TEM and FT-IR. The effects of nano contents (weight ratio) and drying temperatures on corrosion properties of silicate film were studied. Potentiodynamic polarization, electrochemical impedance spectroscopy and immersion tests have been used to study corrosion behavior of nano-loaded silicate films. Surface morphology, microstructure and its chemical composition were analyzed by means of FESEM, EDS, AFM, XRD, GIXRD, ATR-FTIR and Raman techniques. Results indicated that colloidal nano-SiO2 properly modified the silicate coatings and significantly improved the corrosion resistance and barrier property. Also drying temperature showed a considerable effect in silicate coating and higher corrosion resistance was obtained with 150°C curing.

Effect of Surface Treatment on Corrosion Resistance of 304 Stainless Steel Implants in Tyrode Solution

Ahmadian Z., Danaee I., Golozar M. A.

Archives of Metallurgy and Materials

2014

Vol. 59, iss. 1

25--30

The effect of different surface preparation methods such as mechanical, chemical and electrochemical surface preparation on the formation, stability and deterioration of surface films formed on austenitic 304 stainless steel was investigated in Tyrode’s physiological solution by cyclic polarization curves, AC impedance measurements surface techniques. A hysteresis loop in a cyclic polarization curve was obtained that indicates a delay in repassivation of an existing pit when the potential is scanned cathodically. Electrolytic polishing and ultrasonic cleaning improves corrosion resistance by increasing the value of the corrosion potential and breakdown potential of the passive layer as well as the pit initiation potential. After mechanical polishing no perfect passivation region was observed. Change in surface fractal is in good agreement with the result obtained from height roughness factor of AFM.

Wpływ różnych sposobów przygotowania powierzchni, takich jak mechaniczne, chemiczne i elektrochemiczne na tworze-nie, stabilność i degradację warstw powierzchniowych utworzonych na austenitycznej stali nierdzewnej 304. badano w fizjologicznym płynie Ty rode'a technikami badań powierzchni - cyklicznych krzywych polaryzacyjnych oraz impedancji. Uzyskano pętlę histerezy cyklicznej krzywej polaryzacyjnej, co wskazuje na opóźnienie w repasywacji istniejących wżerów podczas skanowania potencjału w kierunku katodowym. Elektrolityczne polerowanie i czyszczenie ultradźwiękowe poprawia odporność korozyjną poprzez zwiększenie potencjału korozyjnego i potencjału przebicia warstwy pasywnej, jak również potencjału tworzenia się wżerów. Zmiana fraktala powierzchni jest w dobrej zgodności z wynikami uzyskanymi dla wysokościowych współczynników chropowatości z pomiarów AFM.