Wyniki wyszukiwania - BazTech

1

Oxide coatings on titanium produced by oxidation in fluidized bed

Jasiński J., Mendzik K., Tatar K., Szota M.

Advances in Materials Science

|

2008

|

Vol. 8, nr 1(15)

48-53

EN

The main product of a process of titanium oxidation is titanium oxide, which covers the titanium surface. More-over oxidation in fluidized bed in temperature range of 600-700°C influences on outer layers of titanium specimen, where a diffusion layer of oxygen is observed. Microstructures of titanium with visible oxide coatings on its surface after thermo-chemical treatment are described. Microhardness measurements of titanium surface layers after oxidation process were made with a Knoop microhardness tester and showed significant differences accord-ing to oxidation parameters. Finally, the surfaces of titanium after oxidation in fluidized bed were scratched in aim to measure their adhesion to the substrate surface.

2

Characteristic of oxide layer obtained on titanium used for medical application

Jasiński J., Jeziorski L., Mendzik K., Tatar M., Szota M.

Inżynieria Materiałowa

|

2007

|

Vol. 28, nr 3-4

643-646

EN

Oxidation is one of the most employed methods to improve titanium and its alloys properties especially in medical application. This process like most of the thermo-chemical treatment processes substantially influences on the characteristic of surface layers and the same on its mechanical and useful properties. Oxide coatings produced during titanium oxidation were examined due to their composition identification. Titanium was oxidized in fluidized bed in temperature range between 500^700°C. Microstructures of titanium with a visible oxide coating on its surface after thermo-chemical treatment and changes of grain size in core of titanium samples are described. Moreover X-ray phase analysis of obtained oxides coatings was made as well as microhardness measurements of titanium surface layers after oxidation process. Finally, the surfaces of titanium after oxidation in fluidized bed were measured by Auger electron spectroscopy.

PL

Utlenianie jest jedną z najczęściej stosowanych metod poprawy własności tytanu i jego stopów. Proces ten jak większość procesów obróbki cieplno chemicznej ma znaczący wpływ na charakterystykę warstwę wierzchnią materiału a tym samym na jego własności mechaniczne i użytkowe. W artykule przedstawiono wyniki analizy składu warstwy tlenkowej uzyskanej podczas utleniania tytanu. Proces utleniania przeprowadzono w złożu fluidalnym w zakresie temperatur od 500 do 700°C. Po przeprowadzonej obróbce sporządzono zgłady metalograficzne i opisano mikrostrukturę tytanu z widoczną na jego powierzchni warstwą tlenkowa oraz zmianę wielkości ziarna w rdzeniu próbek. Uzyskane warstwy poddano rentgenowskiej analizie fazowej oraz wykonano pomiary mikrotwardości. W końcowym etapie badań powierzchnię tytanu po utlenianiu w złożu fluidalnym poddano analizie z wykorzystaniem spektroskopii elektronowej Augera.

3

Mikrostruktura i właściwości drutu tytanowego po utlenianiu w złożu fluidalnym

Jasiński J., Mendzik K., Tatar M., Szota M.

Hutnik, Wiadomości Hutnicze

|

2007

|

Vol. 74, nr 1-2

32-34

PL

Utlenianie jest jedną z najczęściej stosowanych metod do polepszania własności tytanu i jego stopów. Proces ten, jak większość procesów obróbki cieplnochemicznej, w znaczący sposób wpływa na charakterystykę mikrostruktury i warstwy wierzchniej materiałów, a tym samym na ich własności mechaniczne i użytkowe. W artykule tym przedstawiono wyniki badań drutu tytanowego poddanego utlenianiu w złożu fluidalnym. W celu zminimalizowania kontaktu drutu tytanowego z innymi metalami, w procesie wykorzystano retorykę kwarcową ze złożami składającymi się z cząstek SiO2. W celu zoptymalizowania efektów procesu, powierzchnię próbek poddano aktywacji mechanicznej poprzez szlifowanie na papierze ściernym. W dalszym etapie badań mikrostrukturę próbek po procesie utleniania poddano analizie na mikroskopie świetlnym i skaningowym. Przeprowadzono również badania składu fazowego i mikrotwardości otrzymanej warstwy tlenkowej.

EN

Oxidation is one of the most employed method to improve titanium and its alloys properties. That process like most of the thermochemical treatment processes substantially influences on the characteristic of microstructure and surface layers of materials and the same on its mechanical and useful properties. The results of research and analysis of titanium wire fluidized bed oxidation process in this article was shown. For the process was used quartz retort containing SiO2 particles in order to reduce titanium contact with other metals to the minimum. Due to process effect optimizing the samples surface was mechanical activated with the grinding paper. In the further of research the microstructure of oxidized samples was analyzed with the light and scanning microscopy. Moreover there were phase analysis of obtained oxides coatings made as well as microhardness measurements of titanium surface layers after oxidation process.

4

Zmiana odporności korozyjnej materiałów po obróbce powierzchniowej do zastosowań biomedycznych

Mendzik K., Lubas M., Jasiński J., Jeziorski L., Szota M.

Engineering of Biomaterials

|

2007

|

Vol. 10, no. 67-68

42-44

5

Struktura iwłaściwości tytanu technicznego po utlenieniu w złożu fluidalnym

Jasiński J., Mendzik K., Jeziorski L.

Inżynieria Materiałowa

|

2006

|

Vol. 27, nr 5

1021-1023

PL

W pracy przedstawiono wyniki badań dotyczące utleniania tytanu w złożu fluidalnym. Przeanalizowano wpływ zastosowanych parametrów obróbki cieplno-chemicznej na mikrostrukturę tytanu i jego właściwości mechaniczne. Utlenianie przeprowadzono w zakresie temperatury 773-973 K, a czas procesu wynosił od 5 do 15 godzin. Efektem utleniania tytanu w złożu fluidalnym było powstanie na powierzchni tytanu powłoki tlenkowej. Dyfuzja tlenu w czasie procesu spowodowała w niektórych przypadkach znaczny wzrost umocnienia. Rentgenograficzna analiza składu fazowego wykazała występowanie w powłoce tlenkowej, przy zastosowanych parametrach, tylko jeden rodzaj tlenku tytanu - TiO2.

EN

In this paper results of measurements on titanium oxidized in fluidized bed are shown. The effect on titanium microstructure and mechanical properties of applied thermo-chemical treatment there is presented. The range of oxidation temperature was from 773 to 973 K and the process time from 5 to 15 hours. After oxidation process in fluidized bed on titanium surface a thin oxide coating is formed, which thickness varies in dependence of used parameters. Oxygen diffusion into titanium substrate during the process in some cases caused significant increase in hardness of titanium surface layer. The X-ray diffraction analysis shown that the oxide layer is composed only of one titanium oxide type - TiO2.

6

Badania powłoki tlenkowej na tytanie po utlenieniu w złożu fluidalnym

Rylski A., Mendzik K., Jasiński J.

Inżynieria Materiałowa

|

2006

|

Vol. 27, nr 5

1197-1199

PL

Powłoki tlenkowe wytworzone w czasie utleniania tytanu poddano badaniom w celu identyfikacji składu tych powłok. Tytan utleniano w atmosferze powietrza w złożu fluidalnym w zakresie temperatury 773-973 K. Czas procesu prowadzonego w temperaturze 923 K wynosił 5 h, natomiast w pozostałych temperaturach 10 h. Przedstawiono mikrostruktury tytanu po przeprowadzonej obróbce cieplnej z widocznymi na jego powierzchni powłokami złożonymi z tlenków. Powierzchnię tytanu po utlenianiu w złożu fluidalnym poddano analizie używając spektroskopii elektronów Augera.

EN

Oxide coatings produced during titanium oxidation were examined due to their composition identification. Titanium was oxidized in fluidized bed in temperature range between 773-973 K. Microstructures of titanium with a visible oxide coating on its surface after thermo-chemical treatment are described. Moreover X-ray phase analysis of obtained oxide coatings was made as well as microhardness measurements of titanium surface layers after oxidation process. Finally, the surfaces of titanium after oxidation in fluidized bed were measured by Auger electron spectroscopy.

7

Powłoki tlenkowe po utlenianiu tytanu w złożu fluidalnym

Jasiński J., Mendzik K., Jeziorski L., Stodolnik B., Torbus R.

Inżynieria Materiałowa

|

2005

|

Vol. 26, nr 5

477-477

PL

W pracy przedstawione są wyniki badań nad tytanem po utlenianiu w złożu fluidalnym złożonym z cząstek SiO2. Zastosowano trzy temperatury procesu: 773, 873 oraz 973 K i utleniano w czasie 10 h w atmosferze powietrza. Opisano mikrostruktury tytanu po przeprowadzonej obróbce cieplno-chemicznej. Dokonano również analizy fazowej uzyskanych powłok tlenkowych oraz zbadano rozkład mikrotwardości w warstwie wierzchniej tytanu po procesie utleniania.

EN

In this work results of investigation of titanium after oxidation in fluidized bed containing SiO2 particles are shown. The temperature ranges from 773 to 973 K. Samples were oxidized for 10 hours in air atmosphere. Microstructures of titanium after thermo-chemical treatment are described in this work. Moreover there were phase analysis of obtained oxides coatings made as well as microhardness measurements of titanium surface layers after oxidation process.