Wyniki wyszukiwania - BazTech

1

Contribution to Deoxidation of Austenitic Steels in a Vacuum Induction Furnace with Carbon

Šenberger J., Pernica V.

Archives of Foundry Engineering

|

2015

|

Vol. 15, iss. 2

105--109

EN

Deoxidation of steel with carbon under reduced pressure is often used for increasing the steel purity. Suitable units for this purpose in foundries are vacuum induction furnaces. Possibilities of increasing the steel purity by deoxidation with carbon in the vacuum induction furnace were studied for the steel for the petrochemistry of specific composition 25Cr/35Ni. The charge composed of the return material only was melted in the air. During melting the charge oxidized and the oxidizing slag formed. Chemical composition of steel, morphology, chemical composition of inclusions in the steel and chemical composition of slag after vacuuming were studied on the basis of samples taken before and after vacuuming. Temperature and oxygen activity were measured before and after vacuuming. Globular inclusions with dominant content of silicon and manganese were observed in steel before and after vacuuming. Contents of total oxygen in steel didn’t change significantly during vacuuming. On the basis of composition of inclusions and measured oxygen activity the activity of Cr2O3 in inclusions was calculated. A slag sample was taken after vacuuming and equilibrium oxygen activity in steel with regard to the Cr2O3 content in the slag was estimated from the slag composition. Equilibrium oxygen activity in relation to the Cr2O3 content in the slag was higher than equilibrium activity measured in the steel. For this reason it is not possible, under the studied conditions, to decrease oxygen content in steel during vacuuming.

2

The influence of the manganese and copper on the structure and mechanical properties of ductile cast iron

Doležal P., Šenberger J., Musilová I.

Zeszyty Naukowe. Mechanika / Politechnika Opolska

|

2007

|

Vol. 321, z. 89

17-17

EN

The structure of ductile cast iron is formed from graphite and basic metal matrix, which is composed from pearlite, ferrite and alternatively their mixture and other structural components (steadite, inclusion). The cast iron with ferrite matrix is characterized by quite high plasticity, toughness, and good workability whereas the tension strength is lower. The ferrite structure is reached by means of very low content of manganese, phosphorous and perhaps even higher contents of silicon. Higher strength is typical for cast iron with pearlite matrix. Higher additives of manganese and especially cooper promote the formation of pearlite. Alloying by cooper is suitable because ledeburite cannot be formed, as this is possibility for alloying by manganese. The contribution is concerned with the influence of manganese and copper on the structure and mechanical properties of ductile cast iron. The casting wedge blocks with graded content of manganese and copper were used for studying of effect of alloying elements. These castings were used for the metallographic evaluation and determination of the basic mechanical properties. On the base of experiments the correlation among basic mechanical characteristics and structure of DCI (ductile cast iron) matrix in the dependence on the content of manganese and copper was found. The all obtained information can be utilized for optimalization of chemical compounds with regard to requirement properties and for production of ADI alloys.

3

Odzyskowe wytapianie stali Crl3Ni z wdmuchiwaniem tlenu

Levíček P., Stránský K., Šenberger J.

Przegląd Odlewnictwa

|

2003

|

Vol. 53, nr 9

288-294

PL

Odporne na korozję staliwa 13% Cr i 1% Ni stosowane są jako odlewy w turbinach Kapłana Peltona i Francisa. Te staliwa mają dobrą odpomość na kawitację. Proces odzyskowego wytapiania, w którym tlen jest wdmuchiwany do kąpieli opracowano w celu zmniejszenia zawartości gazów (wodoru i azotu) obecnych w przetapianym złomie stali 13%Cr i 1%Ni. Ta technologia była badana i opracowana na podstawie 25 wytopów ze szczególnym uwzględnieniem warunków wdmuchiwania tlenu, własności mechanicznych staliwa (ocenianych próbą udarnościową) i ograniczeniem tworzenia porowatości gazowych w odlewach. Odzyskowe wytapianie stali prowadzono w zasadowych piecach łukowych. Pomiar temperatury kąpieli, aktywności tlenu w kąpieli i równoległe pobieranie próbek do analizy chemicznej prowadzono w następujący sposób: 1) po roztopieniu i nagrzaniu kąpieli przed wdmuchiwaniem tlenu; 2) bezpośrednio po wdmuchaniu tlenu; 3) na początku okresu redukcyjnego po wstępnym odtlenieniu glinem, redukcji żużla i modyfikacji składu chemicznego; 4) na końcu okresu redukcyjnego; 5) w kadzii po spuście i wstępnym odtlenieniu SiCa. Wyniki tych pomiarów podano w tabeli 1, a odpowiadające im własności mechaniczne i udarności z wytopów odzyskowych w tabeli 2. Obróbka cieplna była następująca: wyżarzanie homogenizujące 1150°C/(6/ 12h -jako funkcja, grubości ścianki odlewu)/(chłodzenie na powietrzu) plus hartowanie: z temperatury 940°C/(4-6h)/(chłodzenie na powietrzu) i odpuszczanie 720°C/(4-6h)/(studzenic na powietrzu). Odlewy z wytopów odzyskowych nie posiadały pęcherzy.

EN

Corrosion resistant 13% Cr and 1 % Ni cast steel are used to produce castings for the Kaplan, Pelton and Francis turbines. These cast steels have also a satisfactory cavitation resistance. The oxidation re-melting process, where oxygen is blown into the bath, was elaborated in order to reduce the gas content (hydrogen and nitrogen) in re-melted corrosion-resistant 13% Cr and 1 % Ni steel scrap. This technology was tested on and elaborated for twenty-five melts, with special regard to oxygen-blowing conditions, mechanical properties (verified by the impact test) of the cast steel, and suppressing the formation of gas holes in the castings. Basic electric arc furnaces were used in the oxidation re-melting process of steel scrap. The measuring of bath temperature and oxygen activity in the bath, and the parallel sampling for chemical analysis of the bath were realised in the following melt periods: 1) after meltdownw and heating before oxygen blowing; 2) immediately after the end of oxygen blowing; 3) at the beginning of the reduction period, after preliminary de-oxidation with Al, slag reduction and modification of chemical composition; 4) in the bath at the end of the reduction period; and 5) in the ladle, after tapping and SiCa deoxidation. Results of this measuring are given in Table 1 and the corresponding mechanical properties and impact test results for re-melted steels are in Table 2. The heat treatment of cast samples of re-melted corrosion-resistant steels was as follows: homogenisation annealing at 1150°C/(6-12 h - as a function of the wall thickness of castings)/(air cooling) plus hardening at 940°C/(4-6 h)/air cooling) and tempering at 720°C/(4-6 h)/(air cooling). The castings from the re-melted steel of this type were without bubbles.

4

Study of metal flow through ceramic foam filters

Roučka J., Šenberger J., Veverka A.

Archiwum Odlewnictwa

|

2003

|

R. 3, nr 10

146--154

EN

The paper treats of establishing the instantaneous flow rate, flow capacity of ceramic foam filters of 10 and 20 ppi porosity, and hydraulic resistance of filters when pouring ductile iron. The filters have been found to extend the pouring time.

PL

Artykuł dotyczy ustalania chwilowej prędkości przepływu i wydajności przepływu ceramicznych filtrów pianowych o porowatości 10 i 20 ppi oraz odporności hydraulicznej filtrów w trakcie zalewania żeliwa sferoidalnego. Zauważono, że filtry wydłużają czas zalewania.

5

Modyfikacja czystej miedzi z zachowaniem przewodności elektrycznej

Szajnar J., Gawroński J., Roučka J., Šenberger J.

Archiwum Odlewnictwa

|

2003

|

R. 3, nr 10

241--248

PL

W pracy przeprowadzono badania nad modyfikacją miedzi katodowej M1E. Modyfikacje prowadzono pod kątem nie tylko poprawy jakości struktury ale również utrzymania przewodności elektrycznej właściwej powyżej 57MS/m. Stwierdzono, że najlepsze efekty uzyskuje się przy modyfikacji miedzi borem i cyrkonem.

EN

The paper contains the results of modification of cathode copper M1E researches. The modification has been made for not only improving the quality of structure but also for keeping electrical conductivity above 57MS/m. There was stated that the best results are achieved with boron and zirconium as the modifier.

6

In-mould inoculation of graphitic cast irons using inoculation bodies

Roučka J., Šenberger J., Gawroński J., Szajnar J.

Archiwum Odlewnictwa

|

2003

|

R. 3, nr 10

155--162

EN

The effects of inoculation with the aid of OPTIGRAN and GERMALLOY (SKW Trostberg) inoculation bodies placed on ceramic filters on hard-spot depth, structure and mechanical properties have been verified. It has been proved that this method of inoculation reduces chilling tendency in castings very effectively. It increases graphite dispersiveness and improves the plastic properties of ductile iron. The effect of inoculation is dependent on pouring time and sensitive to pouring temperature.

PL

Zweryfikowano wpływ modyfikacji przy zastosowaniu zapraw modyfikujących OPTIGRAN i GERMALLOY (SKW Trostberg) umieszczanych na filtrach ceramicznych, na głębokość warstwy utwardzonej, strukturę i własności mechaniczne. Zostało udowodnione, że przedstawiona metoda modyfikacji bardzo efektywnie redukuje skłonność do zabieleń. Zwiększa rozdrobnienie grafitu i własności plastyczne żeliwa sferoidalnego. Efekt modyfikacji zależy od czasu zalewania i temperatury zalewania.

7

Vlastnosti niklových superslitin typu inconel 713

Doležal P., Šenberger J.

Zeszyty Naukowe. Mechanika / Politechnika Opolska

|

2001

|

Vol. 279, z. 72

137-140

8

Rozbor príčin vad v ocelích na odlitky pomocí morfologie oxidů a sulfidů

Šenberger J.

Zeszyty Naukowe. Mechanika / Politechnika Opolska

|

1998

|

z. 57

125-130