Investigation of Selected Physical Properties of Knitted Fabrics Produced From Macaroni Yarns

Çeven E. K., Günaydin G. K.

Fibres & Textiles in Eastern Europe

|

2018

|

Vol. 26, no. 4 (130)

59--66

EN

Recently there have been new trends in fancy yarns in order to meet consumer demands for drapery, decorative and outwear fabrics. Macaroni yarns are a promising group of fancy yarn which allows new yarn designs with different raw materials at different yarn counts. In the study, supreme knitted fabrics were produced withmacaroni yarns ofdifferent raw materials (polyester, acyclic, cotton) at different yarn counts (Nm 2/1, Nm 2.5/1, Nm 3.3/1, Nm 4/1 and Nm 4.5/1).Completely randomised one-factor analysis of variance (ANOVA) was used for determination of the statistical significance of the fabric type on selectedphysical properties of knitted macaroni fabrics in terms of fabric weight (g/m2), dimensional change (%) in the wale and course direction, abrasion resistance, and air permeability properties before and after the washing process.According to the results of the statistical analyses performed using the experimental values obtained from the tests, wedetermined that the fabric weights (g/m2), dimensional changes (%) in the wale and course direction, abrasion resistance and air permeability properties before and after washing were significantly influenced by the macaroni yarn’sstructural parameters (such as the yarn count andraw material comprising it).

PL

Na świecie pojawiły się ostatnio nowe trendy w obszarze przędz fantazyjnych, tak aby sprostać wymaganiom konsumentów w zakresie tkanin dekoracyjnych i wierzchnich. Przędze makaronowe są obiecującą grupą przędz fantazyjnych, ich zastosowanie pozwala na otrzymanie nowych wzorów. W badaniu wyprodukowano dzianiny z przędz makaronowych z różnych surowców (poliester, bawełna) przy różnych ilościach przędzy. Do oceny statystycznej wykorzystano jednoczynnikową analizę wariancji (ANOVA). Zgodnie z wynikami analiz statystycznych przeprowadzonych z wykorzystaniem wartości doświadczalnych uzyskanych z badań ustalono, że masa (g/m2), zmiany wymiarów (%) w obu kierunkach, odporność na ścieranie i przepuszczalność powietrza przed i po płukaniu znacząco wpływają na parametry strukturalne przędz makaronowych.

2

Investigation of Moisture Management and Air Permeability Properties of Fabrics with Linen and Linen-Polyester Blend Yarns

Çeven E. K., Günaydin G. K.

Fibres & Textiles in Eastern Europe

|

2018

|

Vol. 26, no. 4 (130)

39--47

EN

This paper has focused on moisture management (MMT) and air permeability properties of fabrics produced from linen (100%) and linen-polyester yarns (80% polyester and 20% linen) at different weft densities. In the experimental study, eighteen different types of fabrics composed of six different weft yarns with three levels of weft density (weft density of 8,10 &12 pick/cm for 100% linen fabrics and 14,16,18 pick/cm for polyester-linen fabrics) were selected in order to determine the influence of weft density and yarn structural parameters (number of yarn folds) on moisture management as well asair permeability properties. The following weft yarns were selected: 104/1 tex, 104/2 tex & 104/3 tex for 100% linen and41/1 tex, 41/2 tex & 41/3 tex for 80% Polyester – 20% linen fabrics, whereas the warp yarn wasconstant - 50/1 tex 100% linen for all fabric types. Satin type fabrics were subjected to moisture management tests andair permeability tests as well. According to test results, it was determined that some of the moisture management(wetting time, absorption rate (%/s) and one-way accumulative transport index of the fabrics’ top surfaces and bottom surfaces) andair permeability properties were significantly affected by the number of yarn folds and the weft density at a 0.05 significance level.

PL

W pracy skoncentrowano się na przepuszczalności wilgoci (MMT) i powietrza tkanin wykonanych z przędzy lnianej (100%) i lniano-poliestrowej (80% poliester i 20% len) przy różnych gęstościach wątków. W badaniu eksperymentalnym osiemnaście różnych rodzajów tkanin składających wykonanych z sześciu różnych rodzajów przędz o trzech gęstościach wątku (8, 10 i 12 na 1 cm dla 100% tkanin lnianych i 14, 16, 18 na 1 cm dla tkanin poliestrowo-lnianych) przebadano pod kątem określenia wpływu gęstości wątku i parametrów strukturalnych przędzy na właściwości przepuszczalności powietrza i wilgoci. Do badań wybrano następujące rodzaje przędz wątkowych: 104/1 tex, 104/2 tex i 104/3 tex dla 100% lnu oraz 41/1 tex, 41/2 tex i 41/3 tex dla 80% poliestru / 20% len, mając na uwadze, że przędza osnowowa była taka sama dla wszystkich typów tkanin (50/1 tex, 100% len). Tkaniny zostały poddane testom przepuszczalności powietrza i wilgoci. Na podstawie wyników badań ustalono, że niektóre czynniki dotyczące właściwości związanych z wilgocią (czas zwilżania, szybkość wchłaniania (%/s) i jednokierunkowy skumulowany wskaźnik transportu powierzchni górnych i dolnych) oraz właściwości przepuszczalności powietrza uległy znacznej zmianie na skutek zmiany gęstości wątku na poziomie istotności 0,05.

3

Investigation of Tensile and Stiffness Properties of Composite Yarns with Different Parameters

Çeven E. K., Aytaş H.

Fibres & Textiles in Eastern Europe

|

2016

|

Vol. 24, no. 4 (118)

51--58

EN

In this experimental study, we investigated the effects of core yarn diameter and cover yarn type on the mechanical properties of composite yarns produced using a hollow spindle twisting machine according to the method of covering. Composite yarns containing stainless steel (SS) metal wires with diameters of 50 μm and 100 μm were produced with seven different cover yarns varying in their raw material and structure. These cover yarns were as follows: polypropylene, cotton, core-spun polyester/cotton, continuous filament polyester, continuous filament polyamide 6.6, core-spun polyester/polyester, and polyester cut fibre yarns. The mechanical properties measured were tensile behaviour and stiffness. According to the findings of the statistical analyses performed using the experimental values, the core yarn diameter, cover yarn type and the interactions of these factors were all significant factors affecting the tenacity, elongation at break, work of rupture and stiffness properties of the composite yarns. Composite yarns containing continuous filament polyamide 6.6 cover yarn showed higher tenacity values, while the maximum elongation at break was obtained for the composite yarns containing continuous filament polyester cover yarn. Both polyester and polyamide 6.6 possessed higher work of rupture values among the other types of cover yarns. An increase in the SS wire diameter resulted in a significant increment in stiffness values. The results of this study implied that it is important to give importance to component yarn types when designing composite yarns with desired physical properties.

PL

Badano wpływ zmian średnicy przędzy rdzeniowej i owijającej na właściwości mechaniczne przędz kompozytowych wytworzonych techniką wydrążonego wrzeciona metodą oplatania. Przędze kompozytowe zawierające metalowe druty ze stali nierdzewnej (SS) o średnicach 50 μm do 100 μm zostały wyprodukowane z siedmiu przędz owijanych o zróżnicowanym składzie surowcowym i zróżnicowanej strukturze. Przędzami owijającymi były polipropylen, bawełna, poliester/bawełna przędza rdzeniowa, ciągłe włókna poliestrowe, ciągłe włókna PA z poliamidu 6.6, poliester/poliester przędza rdzeniowa oraz cięte włókna poliestrowe. Mierzono i wyznaczano właściwości mechaniczne przy rozciąganiu i sztywność. Zgodnie z analizami średnica przędzy rdzeniowej, rodzaj przędzy oplatającej i interakcje zachodzące pomiędzy tymi parametrami okazały się istotnymi czynnikami wpływającymi na wytrzymałość na rozciąganie, wydłużenie przy zerwaniu, pracę zrywania i właściwości charakteryzujące sztywność przędz kompozytowych. Przeprowadzono dokładną analizę wpływu przędz składowych na uzyskane parametry oraz wytypowano korzystne dla danych warunków rozwiązanie.

4

Effect of chenille yarns produced with selected comfort fibres on the abrasion and bending properties of knitted fabrics

Kavuşturan Y., Çeven E. K., Özdemir Ö.

Fibres & Textiles in Eastern Europe

|

2010

|

Vol. 18, no. 1 (78)

48--53

EN

In this study, the effects of pile and core yarn material types on the abrasion and bending behavior of chenille knitted fabrics were studied. For this purpose different chenille yarns were produced from seven types of pile yarn material and two types of core yarn material at the same yarn counts. The different pile yarn fibre types used for the production of chenille yarns were comfort fibres like tencel, bamboo, modal, soybean, 50/50% soybean-tencel and conventional fibres like viscose and cotton; the different core yarn types were polyester and viscose. The abrasion resistance of knitted fabrics made from these yarns was measured with a Martindale Abrasion tester. According to the results of statistical analyses performed using the experimental values, physical properties like mass and thickness loss due to abrasion were affected by the pile and core yarn types. Course way, wale way and fabric bending rigidity properties were not affected by the core yarn fibre types. The course way bending rigidity property was affected by the pile yarn fibre types, while the wale way and fabric bending rigidity properties were affected by the pile yarn fibre types for undyed yarns.

PL

Badano wpływ przędz rdzeniowych i okrywowych na odporność na ścieranie i zachowanie przy zginaniu dzianin szenilowych. W tym celu wyprodukowano szereg dzianin szenilowych z siedmiu rodzajów przędz okrywowych oraz dwóch rodzajów przędz rdzeniowych o takich samych masach liniowych. Przędze okrywowe wykonane były z tak zwanych włókien komfortowych jak włókna celulozowe tencel i modalne, bambusowe, sojowe, mieszankowe 50/50% sojowe/tencel oraz konwencjonalnych takich jak wiskozowych i bawełnianych. Przędze rdzeniowe wykonano z włókien poliestrowych i wiskozowych. Odporność na ścieranie z dzianin wykonanych z tych przędz testowano za pomocą przyrządu typu Martindale . Na podstawie analizy statystycznej uzyskanych wyników eksperymentalnych stwierdzono, że fizyczne właściwości jak utrata masy i grubości dzianiny zależą od typu przędz okrywowych i rdzeniowych zastosowanych do produkcji dzianiny. Konfiguracja rządków i kolumienek oraz sztywność na zginanie dzianin nie zależały od rodzaju zastosowanych przędz rdzeniowych. Sztywność zginania w kierunku rządków była uzależniona od rodzaju zastosowanych przędz okrywowych podczas gdy sztywność kierunku kolumienek zależała od typu przędz okrywowych dla dzianin nie barwionych.

5

The Effect of Vacuum Steaming Parameters on the Physical Properties of Chenille Yarns

Çeven E. K., Özdemir Ö.

Fibres & Textiles in Eastern Europe

|

2008

|

Vol. 16, no. 2 (67)

35--40

EN

In this study, the effects of vacuum steaming process parameters on the physical properties of chenille yarns and fabrics were studied. For this purpose chenille yarns were produced with viscose and acrylic pile and core yarns in different yarns counts. The chenille yarns were subjected to vacuum steaming at varying process parameters, for example the steaming temperature (60, 80 and 110 °C) and steaming period (20, 40 and 60 minutes). According to the results of statistical analyses performed using experimental values obtained before and after vacuum steaming, physical parameters, like yarn count, twist, tenacity, elongation and work-of-break values were affected by the vacuum steaming process. An increase in fabric abrasion resistance was observed when the vacuum steamed chenille yarns were used as filling in the woven fabric construction. Process parameters are significant regarding change in yarn count and twist, but are insignificant regarding change in work-of-break values. Temperature is not a significant factor during any change in the tenacity of viscose chenille yarn, but is a significant factor in any change in the elongation values of acrylic chenille yarns.

PL

Badano wpływ parametrów parowania próżniowego na właściwości fizyczne przędz szenilowych i produkowanych z nich tkanin. Dla tego celu wyprodukowano przędze szenilowe o różnej masie liniowej, stosując włókna wiskozowe i akrylowe w okrywie i rdzeniu. Wyprodukowane przędze poddano parowaniu próżniowemu o różnych parametrach, np. temperaturach pary 60, 80 i 110 °C i czasie obróbki 20, 40 i 60 minut Na postawie wyników badań eksperymentalnych, poddanych analizie statystycznej, określono takie parametry fizyczne jak masa liniowa, wytrzymałość właściwa, wydłużenie przy zerwaniu oraz energia potrzebna do zerwania przędzy i analizowano jak na nie wpływają parametry procesu parowania. Stwierdzono wzrost odporności tkanin na ścieranie przy stosowaniu parowanych przędz szenilowych. Badane parametry procesu istotnie wpływały na zmiany masy liniowej i skrętu, natomiast jedynie nieznacznie na energię zerwania. Temperatura nie jest ważnym czynnikiem wpływającym na zmiany wytrzymałości właściwych przędz szenilowych wiskozowych, ale wpływa na wydłużenie przy zerwaniu przędz akrylowych.

6

Using Fuzzy Logic to Evaluate and Predict Chenille Yarn’s Shrinkage Behaviour

Çeven E. K., Özdemir Ö.

Fibres & Textiles in Eastern Europe

|

2007

|

Vol. 15, no. 3 (62)

55--59

EN

In this study, a fuzzy logic system is used to determine the effects of yarn parameters on the boiling shrinkage behaviour of chenille yarns. Chenille yarns are produced with different yarn counts, pile lengths, and twist levels on a chenille yarn machine. In the production of such yarns, the core yarn component is selected as acrylic while the pile yarn component is selected as viscose. The boiling water shrinkage of chenille yarns is measured according to a laboratory test method. Experimental data is used to establish the fuzzy logic model and construct basic principles. According to the results, chenille yarns with higher twist levels and shorter pile lengths have lower shrinkage values, and the yarn count has a significant effect on shrinkage. The comparison of the results obtained from the fuzzy logic model and the experiments shows that there is a strong linear relationship between the measured and predicted yarn shrinkage values.

PL

System „logiki rozmytej” został zastosowany dla określenia wpływu parametrów przędzy na kurczliwość przędzy szenilowej we wrzącej wodzie. Przędze szenilowe o różnej masie liniowej, długości okrywy i skręcie produkowane są na specjalnych maszynach. Przy produkcji tego rodzaju przędz, rdzeń jest często wykonywany z przędzy akrylowej, podczas gdy składnik stosowany jako okrywa, - z wiskozy. Skurcz przędzy szenilowej we wrzącej wodzie był mierzony za pomocą metody laboratoryjnej. Uzyskane wyniki posłużyły dla opracowania modelu „logiki rozmytej” oraz podstawowych zależności. Zgodnie z wynikami eksperymentów, przędze szenilowe o większym skręcie i krótszej okrywie charakteryzują się mniejszym skurczem. Również masa liniowa wpływa wyraźnie na skurcz. Porównanie wyników uzyskanych za pomocą modelu „logiki rozmytej” z wynikami eksperymentów wskazuje, że istnieje ścisła liniowa zależność pomiędzy nimi.

7

A Study of the Basic Parameters Describing the Structure of Chenille Yarns

Çeven E. K., Özdemir Ö.

Fibres & Textiles in Eastern Europe

|

2006

|

Vol. 14, no. 2 (56)

24--28

EN

The basic parameters describing the structure of chenille fancy yarns produced on a chenille yarn machine have been characterised. The effect of the properties of the component yarns, and that of machine parameters on the final count of the chenille yarns, have been studied. For this purpose chenille yarns were produced in different pile lengths, twist levels, yarn counts of component yarns, and an expression is derived to determine the final count of these chenille yarns. Correlation analysis confirmed a strong linear relationship with a high value of correlation coefficient (above 0.95) between the final count values of chenille yarn samples obtained from the expression (formula) and that obtained from the measurements.

PL

Scharakteryzowano podstawowe parametry opisujące strukturę fantazyjnych przędz szenilowch, wytwarzanych na maszynie do produkcji przędz szenilowych. Badano wpływ właściwości przędz składowych oraz parametrów maszyny na końcowy numer przędzy. W tym celu wyprodukowano przędze szenilowe o różnej długości okrywy, skręcie i masie liniowej przędz składowych. Opracowano zależność dla określania końcowego numeru przędzy szenilowej. Analiza korelacji potwierdziła wyraźną liniową zależność, przy wysokiej wartości współczynnika korelacji (powyżej 0.95) pomiędzy końcowym numerem przędzy szenilowej obliczonej na podstawie wyżej wspomnianej zależności, a numerem stwierdzonym na podstawie pomiaru wyprodukowanych próbek.