Internal Friction and Microstructure of Ti and Ti-Mo Alloys Containing Oxygen

Martins Jr J. R. S., Araújo R. O., Nogueira R. A., Grandini C. R.

Archives of Metallurgy and Materials

2016

Vol. 61, iss. 1

25--30

Ti-Mo alloys are promising materials for use as biomaterials, because these alloys have excellent corrosion resistance and a good combination of mechanical properties such as fatigue, low elastic modulus, hardness, and wear resistance. The objective of this paper was to study the effect of heavy interstitial atoms on anelastic properties of Ti-Mo alloys using mechanical spectroscopy. The internal friction and Young’s modulus were measured as a function of temperature using dynamic mechanical analyser. The internal friction spectra were brought about by relaxation processes attributed to shortrange stress induced reorientation of interstitial and substitutional complexes in solid solution. It is suggested that the nature of the relaxing entities can be worked out in further research on Ti-Mo single crystals.

Mechanical Spectroscopy of MgB2 Containing SiC

Silva M. R., Silva L. B. S., Rodriques Jr. D., Grandini C. R.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 4

3083--3086

The compound magnesium diboride (MgB2) has been well-known since the 1950s; however, its superconducting properties were unknown. Intrinsic characteristics of MgB2 make this material a promising candidate for technological applications, although the low value of the irreversibility field and the decrease in critical current density with the increase in the magnetic field considerably reduce its utility. The present work aimed to study the effect of carbon-based doping on anelastic properties of MgB2 as measured by mechanical spectroscopy. The samples were prepared by using the powder-intube method. The samples were made with 5, 7.5, and 10 wt.% of silicon carbide (SiC). The results reveal complex mechanical loss spectra caused by the interaction between point defects and surface defects in the crystalline lattice of MgB2.

Dwuborek związek magnezu (MgBV) jest znany od 1950 roku; jednak jego właściwości nadprzewodzące były nieznane. Swoiste cechy MgB2 czynią ten materiał obiecującym kandydatem do zastosowań technicznych, jednak niskie wartości nieodwracalnego pola i zmniejszenie krytycznej gęstości prądu ze wzrostem pola magnetycznego znacznie zmniejszają jego użyteczność. Celem pracy było zbadanie wpływu domieszkowania związkiem węgla na anelastyczne właściwości MgB2 mierzone metodą spektroskopii mechanicznej. Próbki zostały przygotowane za pomocą metody powder-in-tube (PIT). Wytworzono próbki o zawartości 5, 7.5 i 10 % wag. węglika krzemu (SiC). Wyniki pokazują złożone widma strat mechanicznych powodowanych przez wzajemne oddziaływanie pomiędzy defektami punktowymi i defektami powierzchniowymi w sieci krystalicznej MgB2.