Microstructure and corrosion behaviour of Al-Si alloy treated by high intensity ultrasonic vibrations

El Nashar R. M., El-Aziz A. M., Khalifa W., Abd El Ghani N. T.

Ochrona przed Korozją

2012

nr 2

34-39

The effect of ultrasonic liquid metal treatment on the microstructure and the corrosion behaviour of the A356 Al-Si alloy was studied. The microstructures of the Al-Si were observed by means of optical and scanning electron microscopes. The corrosion behaviour was studied electrochemically and by gravimetric method. The results showed that the microstructure was modified from a coarse acicular plate-like form when no ultrasonic vibration was used, to a fi nely dispersed rosette-like form when ultrasonic treatment was employed. The ultrasonically treated samples showed higher resistance to pitting than the untreated sample. The soaking process negatively affected the pitting resistance.

Badano wpływ ultradźwiękowej obróbki ciekłego metalu na mikrostrukturę i zachowanie korozyjne stopu A356 Al-Si. Mikrostruktury Al-Si obserwowano przy użyciu mikroskopu optycznego i elektronowego mikroskopu skaningowego. Zachowanie korozyjne badano metodami elektrochemicznymi i metodą grawimetryczną. Wyniki badań wykazały, że po obróbce ultradźwiękowej, mikrostruktura uległa przekształceniu z płaskich i szorstkich igiełek do postaci drobno rozproszonej w kształcie rozety. Próbki po obróbce ultradźwiękami wykazywały większą odporność na korozję wżerową niż próbki bez obróbki , natomiast moczenie odporność tę pogorszyło.