Influence of thermal annealing and deposition conditions on structure and physical-mechanical properties of multilayered nanosized TiN/ZrN coatings

Pogrebnjak A. D., Bondar O. V., Erdybaeva N. K., Plotnikov S. V., Turbin P. V., Grankiin S. S., Stolbovoy V. A., Sobol O. V., Kolesnikov D. A., Kozak C.

Przegląd Elektrotechniczny

2015

R. 91, nr 12

228-232

Nanostructured multilayered TiN/ZrN coatings were fabricated using vacuum-arc deposition method. Amount of layers was 134-533; average bilayer thickness was 20-125 nm depending on deposition conditions. Good planarity of nanoscale bilayers were observed. Regularities of phase-structure changes in surface layers under the influence of aggressive oxygen atmosphere and high temperature (700 0С) annealing were established as a model of critical working conditions. Bilayer thickness influence on hardness was explored. Maximum hardness was 42 GPa.

Nanostrukturalne wielowarstwowe powłoki TiN/ZrN otrzymano używając metody próżniowo-łukowego osadzania. Ilość warstw wynosiła 134-533; średnia grubość dwuwarstwowa wynosiła 20-125 nm zależnie od warunków osadzania. Zaobserwowano dobrą planarność podwójnych warstw w nanoskali. Określono prawidłowości zmian struktury fazowej w warstwach powierzchniowych pod wpływem agresywnej atmosfery utleniającej oraz wysokiej temperatury (700 0С) wygrzewania jako model krytycznych warunków pracy. Zbadano wpływ grubości podwójnych warstw na twardość. Maksymalna twardość wynosiła 42 GPa.

Dependence of mechanical and tribotechnical properties of multilayered TiN/ZrN coatings on deposition

Bondar O. V., Stolbovoy V. A., Kylyshkanov M. K., Plotnikov S. V., Erdybaeva N. K., Piotrowska K., Czarnacka K., Karwat C.

Przegląd Elektrotechniczny

2015

R. 91, nr 12

233-236

C-PVD method (vacuum arc deposition of a cathodes) was used for deposition of multilayered coatings, based on TiN/ZrN systems, with different thickness of bilayers. Total thickness of the coatings was 11 – 19 μm, thickness of bilayers varied from 39 to 305 nm for different samples depending on deposition conditions. Microstructure of the coatings, mechanical and tribotechnical properties, and wear resistance were explored. Influence of the bilayer thickness on such properties of the coatings, as hardness, elasticity modulus, wear resistance and wear ratio were explored.

Metoda C-PVD (napylanie próżniowo-łukowe katod) została użyta do osadzania wielowarstwowych powłok, na bazie układów TiN/ZrN o zmiennej grubości pojedynczych warstw. Całkowita grubość powłoki wynosiła 11 – 19 μm, przy czym grubość pojedynczych warstw wahała się od 39 do 305 nm dla różnych próbek zależnie od warunków osadzania. Zbadano mikrostrukturę powłok, właściwości mechaniczne i trybologiczne oraz odporność na zużycie.