Analysis and optimization of using hemihydrates plaster (ß) for casting mould in sanitary ware industry

Sheikh Attar M., Nemati H. R., Sarjahan R.

Materiały Ceramiczne

2011

T. 63, nr 1

143-146

Slip casting is a common method for producing sanitary ware, and it is just possible by plaster moulds. Therefore, in order to reach the best quality of sanitary ware, plaster moulds are playing an important role. Lifetime, water absorption and finished surface of Plaster moulds qualify the quality of final product significantly. Although, some characteristics of plaster mould depends on the plaster directly, others are affected by preparation process of moulds such as mixing time, plaster to water ratio, water temperature and drying process. In this investigation, hemihydrates plaster (ß) of different suppliers has been studied by XRD; also particle size distribution of plasters has been analyzed by sieve shaker. Afterward, the best one has been selected, and effects of parameters involved in process of mould making have been studied to make an efficient plaster mould.

Odlewanie z gęstw stanowi powszechną metodę wytwarzania ceramiki sanitarnej i jest możliwe dzięki formom gipsowym. Zatem, w osiąganiu najlepszej jakości ceramiki sanitarnej ważną rolę odgrywają formy gipsowe. Trwałość, nasiąkliwość i gotowa powierzchnia form gipsowych warunkują znacząco jakość końcowego wyrobu. Chociaż, niektóre charakterystyki formy gipsowej zależą bezpośrednio od gipsu, inne są związane z parametrami procesu przygotowania form takimi jak: czas mieszania, stosunek gipsu do wody, temperatura wody i proces suszenia. W prezentowanej pracy, półhydraty (ß) gipsu od różnych dostawców zostały zbadane za pomocą metody XRD; zanalizowano również rozkłady wielkości cząstek gipsów za pomocą wstrząsarki do sit. Następnie, najlepszy gips został wybrany i użyty do zbadania wpływu parametrów procesu przygotowania form w celu wytworzenia wydajnej formy gipsowej.

Effect of pigments on crystal phases in non-fritted matte glaze

Sarjahani R., Nemati H. R., Sheikh Attar M.

Materiały Ceramiczne

2010

T. 62, nr 4

565-568

Recently, porcelain with matte glaze, as a unique and attractive coating on ceramic products, has attracted many architects and interior designers' attention. Production of matte glaze was a challenge for sanitary ware manufacturers due to long firing cycle, raw glaze, and single firing condition and being hygienic that is very important. Although, using frit facilitates making matte glaze, its high price and reduction of firing temperature keep manufacturers away from its production. In this investigation, the matte glaze has been designed and produced based on the fact that increasing CaO content in glaze composition induces crystal growth; besides, coloured matte glaze has been investigated, different pigments have various effects on crystal morphology and microstructure that they have been studied by XRD. The surface quality of this glaze has been observed by confocal optical microscope. At the end, standard tests for sanitary ware were passed and confirmed the quality.

Ostatnio, porcelana z matowym szkliwem, jako unikalną i atrakcyjną powłoką na wyrobie ceramicznym, przyciąga uwagę wielu architektów i projektantów wnętrz. Wytwarzanie szkliwa matowego było wyzwaniem dla wytwórców wyrobów sanitarnych ze względu na długi cykl wypalania, samo otrzymanie surowego szkliwa i spełnienie warunku spiekania jednoetapowego, a także, co jest bardzo ważne, koniecznością spełnienia wymagań higienicznych. Chociaż, potrzeba użycia urządzeń frytujących do wytwarzania szkliwa matowego, jego wysoka cena i obniżenie temperatury wypalania wstrzymują producentów od ich produkcji. W niniejszej pracy opracowano i wytworzono szkliwo matowe w oparciu o fakt, że zwiększenie zawartości CaO w składzie szkliwa wywołuje wzrost faz krystalicznych; poza tym, zbadano zabarwione szkliwo matowe, różne pigmenty mają odmienny wpływ na morfologię i mikrostrukturę faz krystalicznych, co zbadano za pomocą techniki XRD. Jakość powierzchni tego szkliwa obserwowano za pomocą mikroskopu optycznego współogniskowego. Na koniec, przeprowadzono standardowe badania wyrobu sanitarnego i potwierdzono jego jakość.