New Wear Resistant Iron-Base Matrix Materials For The Fabrication Of Sintered Diamond Tools

Konstanty J., Romański A., Baczek E., Tyrala D.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 2A

633--637

EN

The possibility of the use of inexpensive iron-base powders in the production of sintered diamond tools is again explored. Ball-milled Fe-Ni-Cu-Sn-C and Fe-Mn-Cu-Sn-C powders were consolidated to a virtually pore-free condition by hot pressing at 900°C. The resultant materials are characterised by a combination of high Knoop hardness, 260-440 and yield strength, 780-1350 MPa, and resistance to abrasion. These properties can be significantly modified by changing the milling time.

PL

W artykule zamieszczono wyniki badań nad możliwością zastosowania tanich proszków na bazie żelaza do produkcji spiekanych narzędzi metaliczno-diamentowych. Mielone proszki Fe-Ni-Cu-Sn-C i Fe-Mn-Cu-Sn-C poddano prasowaniu na gorąco w temperaturze 900°C. Otrzymane spieki posiadają gęstość zbliżoną do teoretycznej, wysoką twardość (260-400 HK0.5), granicę plastyczności (780-1350 MPa) oraz dużą odporność na zużycie ścierne. Wymienione własności są w dużym stopniu uzależnione od czasu mielenia proszków wyjściowych.

2

Badania spiekanych materiałów Fe-Ni-C z dodatkiem 8 % brązu wykonanych z mielonych proszków

Romański A., Tokarski T.

Rudy i Metale Nieżelazne Recykling

|

2014

|

R. 59, nr 5

224--232

PL

Głównym celem pracy były badania spiekanych materiałów Fe+12%Ni+0,6%C+8%CuSn20 otrzymanych z proszków poddanych mieleniu w młynie kulowym przez 8 i 120 godz. Metodą prasowania na zimno w sztywnej matrycy pod ciśnieniem 400 MPa wykonano wypraski, które spiekano w dylatometrze Netzsch 402E w temperaturze 850, 900 i 950 °C w atmosferze przepływającej mieszaniny gazów 95%N2-5%H2. Nagrzewanie i chłodzenie realizowane było z prędkością 10 K/min, a czas izotermicznego wygrzewania wynosił 1 godz. Uzyskane spieki poddano badaniom gęstości, twardości oraz mikrostrukturalnym. Na podstawie otrzymanych danych stwierdzono, że materiał uzyskany z proszku mielonego przez 120 godz. bardzo dobrze się spieka już w temperaturze 850 °C i charakteryzuje się drobnoziarnistą mikrostrukturą o małej niejednorodności składu chemicznego. Natomiast proszek mielony przez 8 godz. nie jest podatny na spiekanie w badanym zakresie temperatury.

EN

The main objective of this paper was to study the sintered Fe+12%Ni+0.6%C+8%CuSn20 materials obtained from ballmilled powders for 8 and 120 hours. The cold compacted at 450 MPa samples were sintered in the Netzsch 402E dilatometer at 850, 900 and 950 °C in a 95%N2/5%H2 atmosphere. The heating and cooling rate were 10K/min; specimens were hold at the temperature for one hour. The as-sintered specimens were subjected to density and hardness measurements as well as to microstructural evaluations. The obtained results show that the powder milled for 120 hours has excellent sintering behaviour and despite sintering temperature, sintered material shows homogenous and very fine-grained microstructure. Due to the low sinterability of the ball-milled powder for 8 hours, in order to achieve the near-free pore microstructure, it is necessary to increase sintering temperature above 950 °C.

3

Sintered Fe-Ni-Cu-Sn-C Alloys Made of Ball-Milled Powders

Romański A., Tokarski T., Tyrała D.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 3

947--950

EN

The main objective of this paper was to perform sinterability studies of ball-milled Fe-12%Ni-6.4%Cu-1.6%Sn-0.6%C powders. A mixture of precisely weighed amounts of elemental iron, nickel and graphite, and pre-alloyed 80/20 bronze powders was ball-milled for 8, 30 and 120 hours. After cold-pressing at 400 MPa the specimens were sintered at 900°C for 30 minutes in a reducing atmosphere and subsequently tested for density and hardness as well as subjected to structural studies using scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. The obtained results showed that only the powder ball-milled for 120 hours yielded a near pore-free material after consolidation by cold pressing and pressureless sintering at 900°C. Assuch, it could have a potential to be used in production of diamond-impregnated wire saw beads.

PL

Głównym celem pracy było zbadanie przydatności mielonych proszków w młynie kulowym do wytwarzania spiekanych materiałów Fe-12%Ni-6.4%Cu-1.6%Sn-0.6%C. Mieszankę elementarnych proszków żelaza, niklu oraz grafitu wraz z proszkiem brązu B20 poddano mieleniu w młynie kulowym przez okres 8, 30 i 120 godzin. Prasowane pod ciśnieniem 400 MPa wypraski wykonane z mielonych proszków poddano spiekaniu w temperaturze 900°C przez 30 minut w atmosferze redukującej. Spieki zostały poddane badaniom gęstości, twardości oraz mikrostrukturalnym, obejmującym mikroskopię skaningową oraz rentgenowską analizę fazową. Otrzymane wyniki badań wskazują, że tylko spieki wykonane z proszku mielonego przez 120 godzin odznaczają się niską porowatością i z tego powodu mogą stanowić potencjalny materiał osnowy spiekanych segmentów metaliczno-diamentowych przeznaczonych do produkcji pił linowych.

4

Struktura i własności wybranych spieków Co-Cu-WC otrzymanych metodą prasowania na gorąco

Romański A.

Rudy i Metale Nieżelazne

|

2010

|

R. 55, nr 12

876-882

PL

W artykule przedstawiono wyniki wstępnych badań wybranych materiałów Co-Cu-WC, przeznaczonych na osnowy narzędzi metaliczno-diamentowych. Próbki wykonane techniką prasowania na gorąco poddano badaniom gęstości, wytrzymałości na zginanie oraz strukturalnym, obejmującym mikroskopię optyczną, skaningową oraz mikroanalizę rentgenowską. Analiza uzyskanych wyników wykazała, iż w przyjętych warunkach prasowania na gorąco nie jest możliwe otrzymanie prawie bezporowatych próbek. W celu zastosowania wybranych materiałów na osnowy narzędzi metaliczno-diamentowych konieczna jest zmiana parametrów wytwarzania, które zapewniłyby gęstość względną bliską gęstości teoretycznej.

EN

In this work the results of initial investigation of selected Co-Cu-WC materials intended for a matrix in diamond impregnated tools are presented. Hot pressed specimens were subjected for density measurements as well as examined for 3-point bending test and structural investigations that cover light optical microscopy, SEM and X-ray microanalysis. Obtained results show that applied hot pressing parameters do not ensure the pore-free samples. The application of the selected materials in diamond impregnated tools depends on the hot pressing parameters which should be changed to achieve the required relative density.

5

Factors affecting diamond retention in powder metallurgy diamond tools

Romański A.

Archives of Metallurgy and Materials

|

2010

|

Vol. 55, iss. 4

1073-1081

EN

This paper describes the effects of principle factors which have an influence on potential diamond retention capabilities in powder metallurgy diamond tools. Investigations were carried out using a 3-D computer model of diamond particle embedded in a metallic matrix. The proposed model assumed that the material was fully densified by the hot pressing technique and then cooled down to room temperature. The energies of plastic and elastic deformation of the matrix around the diamond grit as well as recoverable strain energy accumulated in the grit on cooling were calculated. The effects of Young's modulus and yield strength of the matrix as well as friction between diamond and matrix on these energies were analysed. The obtained results have shown that a matrix characterised by high yield strength ensures better diamond retention capacity whereas high Young's modulus of the matrix and its chemical affinity to carbon, which increases friction at the diamond-matrix interface seem to have lower importance.

PL

W pracy przedstawiono analizę wpływu podstawowych czynników mających wpływ na własności retencyjne materiału osnowy w narzędziowych spiekach metaliczno-diamentowych. Badania wykonano z zastosowaniem modeli 3-D cząstki diamentu osadzonej w osnowie. W zaproponowanym modelu założono, że materiał został zagęszczony do gęstości teoretycznej w wyniku prasowania na gorąco i następnie ochłodzony do temperatury otoczenia. Dla temperatury otoczenia obliczano całkowitą energię odkształcenia oraz energię odkształcenia plastycznego materiału osnowy wokół diamentu oraz energię odkształcenia sprężystego cząstki diamentu. Analizie poddano wpływ modułu Younga i granicy plastyczności osnowy oraz współczynnika tarcia pomiędzy cząstką diamentu i osnową na te energie. W wyniku analizy otrzymanych rezultatów badań modelowych stwierdzono, że materiał osnowy odznaczający się większą granicą plastyczności zapewnia wyższe własności retencyjne osnowy. Natomiast większy moduł Younga oraz zwiększenie współczynnika tarcia, np. poprzez zastosowanie osnowy odznaczającej się powinowactwem chemicznym do węgla mają z punktu widzenia retencji diamentu mniejsze znaczenie.

6

Microstructure and phase composition of sintered cobalt-iron materials

Romański A.

Archives of Metallurgy and Materials

|

2009

|

Vol. 54, iss. 2

449-454

EN

This paper describes the effect of the sintering parameters, e.g. temperature and atmosphere, on the microstructure and phase composition of the cobalt-iron materials. Investigations were carried out on the specimens made of the mixtures of elemental cobalt and iron powders, containing 3, 6, 10, 15 and 25 wt.% iron addition. Samples were obtained by cold pressing under 400 MPa then sintered at 900 and 1150 °C for an hour. As a sintering atmospheres both flowing, purified hydrogen and nitrogen was used. The obtained results have shown that density of Co-Fe materials strongly depends on iron content, whereas sintering atmosphere has a minor effect on their hardness. Microstructural investigations have shown that applied sintering atmosphere plays a significant role if grain size and cobalt’s phase composition are taken under consideration.

PL

W artykule przedstawiono wyniki badan poświeconych wpływowi parametrów spiekania, tj. temperatury i atmosfery ochronnej na mikrostrukturę i skład fazowy materiałów kobalt-żelazo. Badaniom poddano próbki wykonane z mieszek elementarnych proszków kobaltu i żelaza, zawierających 3, 6, 10, 15 i 25% wag. Fe. Próbki wykonano techniką jednostronnego prasowania pod ciśnieniem 400 MPa i spiekania w temperaturze 900 oraz 1150 °C przez okres 1 godziny. Jako atmosfery ochronne zastosowano zarówno przepływający wodór, jak i azot. Otrzymane wyniki wykazały, że gęstość spieków Co-Fe jest silnie związana z zawartością żelaza, natomiast rodzaj atmosfery spiekania nie ma znaczącego wpływu na ich twardość. Badania strukturalne wykazały natomiast, że rodzaj zastosowanej atmosfery ochronnej ma zasadnicze znaczenie na wielkość ziarna spieków Co-Fe oraz skład fazowy spiekanego kobaltu.

7

Effect of Friction Coefficient on Diamond Retention Capabilities in Diamond Impregnated Tools

Romański A., Lachowski J.

Archives of Metallurgy and Materials

|

2009

|

Vol. 54, iss. 4

1111-1118

EN

This paper presents the role of friction coefficient between diamond particie and metal matrix and the effect of me-chanical properties of a matrix on its diamond retention capabilities in powder metallurgy (PM) diamond impregnated tools. Investigations were carried out by means of computer modelling techniąue using Abaąus software. In the proposed 2-D axisymmetric model, effects of varied mechanical properties on the energy of plastic deformation of the matrix during cooling to room temperaturę after hot pressing were analysed. In calculations, the diamond particie shape, mismatch between thermal expansion coefficients of the matrix and diamond were also taken into account. Potential retentive properties of the matrix were estimated by the force reąuired to puli out the diamond particie from the matrix. Obtained results have shown that potential retentive properties of the matrix strongly depend on the interactions taking place at the diamond-matrix interface. What is interesting, obtained results have proved that mechanical properties of the matrix are of secondary importance (in limited rangę), when retentive properties are considered.

PL

W artykule opisano rolę współczynnika tarcia pomiędzy diamentem a metriałem osnowy oraz wpływ własności mechanicznych osnowy na zdolność utrzymywania cząstek diamentu w osnowie (jej zdolności retencyjne) w metaliczno-diamentowych narzędziach wytwarzanych techniką metalurgii proszków. Badania zostały wykonano z wykorzystaniem technik komputerowego modelowania przy użyciu programu Abaąus. W zaproponowanym dwuwymiarowym modelu osiowosymetrycznym poddano analizie wpływ zróżnicowanych własności mechanicznych osnowy na wielkość energii jej odkształcenia plastycznego w czasie chłodzenia do temperatury otoczenia po procesie prasowania na gorąco. W obliczeniach uwzględniono także kształt cząstki diamentu oraz różnicę we współczynnikach rozszerzalności cieplnej osnowy i diamentu. Potencjalne własności retencyjne osnowy szacowano wartością siły potrzebnej do wyrwania cząstki diamentu z osnowy. Na podstawie uzyskanych wyników obliczeń stwierdzono, że własności retencyjne osnowy są silnie związane ze zjawiskami zachodzącymi na granicy faz diamentu i osnowy. Stwierdzono również, że w przypadku własności retencyjnych osnowy, jej własności mechaniczne, mają w ograniczonym zakresie drugorzędne znaczenie.

8

Modelowanie stanu naprężeń i odkształceń w spiekanych materiałach narzędziowych metaliczno-diamentowych

Romański A., Lachowski J.

Rudy i Metale Nieżelazne

|

2007

|

R. 52, nr 7

402-410

PL

Przedstawiono wyniki badań modelowych stanu naprężeń i odkształceń w osnowie wokół nieobciążonej cząstki diamentu. Symulacje komputerowe przygotowano z wykorzystaniem programu Abaqus. W zaprezentowanym modelu uwzględniono wpływ własności mechanicznych osnowy, kształtu cząstki diamentu na pole naprężeń i odkształceń osnowy. W obliczeniach przyjęto, że materiał w temperaturze prasowania na gorąco został zagęszczony do gęstości teoretycznej a następnie ochłodzony do temperatury otoczenia. Takie założenie pozwoliło na prześledzenie zmian energii odkształcenia plastycznego i sprężystego ze zmianą temperatury, wynikające z różnicy współczynników rozszerzalności cieplnej diamentu i materiału osnowy. W dalszej części pracy podjęto próbę ustalenia zależności pomiędzy energią odkształcenia plastycznego osnowy a jej własnościami retencyjnymi.

EN

The effective use of diamond impregnated tools is strongly depended on the retentive properties of the metal matrix, which must hold diamond grits firmly. The diamond retentive capability is a complex property, affected by many factors, such as: shape of diamond grits, chemical interactions or mechanical and chemical properties of the matrix. Due to mismatch between thermal expansion coefficients of the matrix and diamond, the stress/strain field is generated in the matrix at diamond surroundings, which also plays a major role when retentive properties are considered. This paper describes the results obtained from numerical analysis of stress and strain field generated in the matrix around unloaded diamond particle using the Abaqus 6.6 software. The effect of mechanical properties of the matrix and diamond particle’s shape on the stress and strain field were considered. In the proposed 2-D axisymmetric model it was assumed that metal-diamond composite was fully densified during hot pressing and then cooled to room temperature. This assumption allows to check the effect of mismatch between thermal expansion coefficients of the matrix and diamond on the recoverable strain energy and energy dissipated by plastic deformation vs. temperature. Finally, it was attempted to find any relationship between energy of plastic deformation of the matrix and its retentive capabilities.

9

Analiza stanu naprężeń wokół cząstki diamentu w spiekach narzędziowych metaliczno-diamentowych

Romański A.

Rudy i Metale Nieżelazne

|

2007

|

R. 52, nr 12

915-921

PL

W artykule omówiono rolę tarcia pomiędzy diamentem a osnową kobaltową na podstawie analizy stanu naprężeń osnowy wokół nieobciążonej cząstki diamentu. Analizę stanu naprężeń wykonano metodą komputerowego modelowania wykorzystując program Abaqus. W celu uproszczenia modelu 2-D przyjęto kulisty kształt cząstki diamentu umieszczonej w osnowie kobaltowej. Założono, że w temperaturze prasowania na gorąco materiał narzędziowy ulega zagęszczeniu do gęstości teoretycznej, a następnie ochłodzony do temperatury otoczenia. Takie założenie umożliwiło analizę naprężeń powstałych w osnowie wokół cząstki diamentu w wyniku dużej różnicy współczynników rozszerzalności cieplnej diamentu i kobaltu. Otrzymane rezultaty pozwalają na stwierdzenie, że zdolność utrzymywania cząstek diamentu przez metaliczną osnowę jest silnie uzależniona od wartości współczynnika tarcia pomiędzy diamentem a materiałem osnowy.

EN

In the present work the effect of friction coefficient between diamond and cobalt matrix on stress field generated around diamond particle is analyses. Investigation were carried out by means of computer modelling technique using Abaqus software. In order to simplify the 2-D axysimmetric model, it was assumed that diamond particle has spherical shape and itis embedded in cobalt matrix. It was also assumed that metal-diamond composite was fully densified during hot pressingand then cooled to room temperature. This assumption has allowed to check the effectof mismatch between thermalexpansion coefficients of the diamond and cobalt matrix. The obtained results has indicated that potential retentive properties ofthe matrix strongly depends on friction coefficient between diamond and metal matrix.

10

Analiza procesu spiekania materiałówmCo-Fe. Cz.1 - Spiekanie w atmosferze obojętnej

Romański A., Frydrych H.

Rudy i Metale Nieżelazne

|

2006

|

R. 51, nr 4

219-224

PL

W artykule przedstawiono wyniki drugiej części pracy poświęconej analizie procesu spiekania materiałów kobalt-żelazo w atmosferze obojętnej — przepływającego azotu. Badaniom poddano próbki zawierające od 3 do 25 % żelaza. Wypraski otrzymane w wyniku prasowania pod ciśnieniem 400 MPa poddano spiekaniu w temperaturze 900, 950, 1000 i 1150 °C. Na podstawie zarejestrowanych krzywych dylatometrycznych określono temperaturę początku spiekania, kinetykę spiekania i wielkość skurczu liniowego próbek.

EN

In this paper the obtained results on sintering process analysis are presented. The undertaken work was the second part of investigations on sintering Co-Fe materials under inert protective atmosphere — nitrogen. The first one was dedicated for sintering under reducing atmosphere — hydrogen. Research program included sintering analysis by the dilatometry on the samples Co-(3÷25 wt.%)Fe, which were made of mixtures obtained from elemental extrafine cobalt and carbonyl iron powders. Compacts were densified under pressure 400 MPa than subjected for sintering at 900, 950,1000 and 1150 °C. Heating and cooling rates were set at 10 K/min, while time of isothermal sintering was 1 hour. On the basis of the recorded data, values describing sintering process were measured, e.g. the kinetics of sintering, sample’s length changes during each sintering step (heating, hold at the temperature and cooling) and overall shrinkage.

11

Analiza procesu spiekania materiałów Co-Fe. Część 1. Spiekanie w atmosferze redukującej

Romański A., Frydrych H.

Rudy i Metale Nieżelazne

|

2006

|

R. 51, nr 1

35-41

PL

W artykule przedstawiono wyniki badań poświęconych analizie procesu spiekania materiałów kobalt-żelazo. Pierwsza część pracy dotyczy badań dylatometrycznych próbek zawierających od 3 do 25 % żelaza, wykonanych z mieszanek elementarnych proszków kobaltu gatunku extrafine i karbonylkowego żelaza. Próbki otrzymano w wyniku prasowania w sztywnej matrycy pod ciśnieniem 400 MPa. Zrealizowano program obejmujący spiekanie w temperaturze 900, 950, 1000 i 1150 stopni Celsjusza w atmosferze redukującej — przepływającego wodoru. Na podstawie zarejestrowanych krzywych dylatometrycznych określono temperaturę początku spiekania, kinetykę spiekania i wielkość skurczu liniowego próbek.

EN

This paper presents the sintering process analysis of Co-Fe materials. The whole research program was divided in to two parts depending on protective atmosphere used during sintering. First one is dedicated for sintering under reducing protective atmosphere — flowing hydrogen. Sintering process was investigated by the dilatometry on the samples Co-(3-25 wt. %)Fe, which were made of mixtures obtained from elemental extrafine cobalt and carbonyl iron powders. Compacts were densified under pressure 400 MPa than subjected for sintering at 900, 950, 1000 and 1150 Celsius degrees. Heating and cooling rates were set at 10 K/min, while time of isothermal sintering was 1 hour. On the basis of the recorded data, values describing sintering process were measured, e.g. the kinetics of sintering, sample’s length changes during each sintering step (heating, hold at the temperature and cooling) and overall shrinkage.

12

The influence of iron content and powder metallurgy processing route on microstructure and mechanical properties of cobalt-iron materials

Frydrych H., Romański A., Konstanty J.

Archives of Metallurgy and Materials

|

2004

|

Vol. 49, iss. 4

973-980

EN

The effects of iron content and Powder Metallurgy (PM) processing conditions on microstructure and mechanical properties of cobalt-iron materials were investigated. The specimens were manufactured from commercial powders by both the conventional single cold press/sinter and hot press routes. The iron content was varied between 3 and 15 wt.%. The specimens were subjected to density measurements, Rockwell hardness, tensile and impact tests, metallographic and fractographic examinations by optical microscopy and scanning electron microscopy, respectively. The investigations indicated that higher mechanical properties were obtained in the hot pressed specimens as compared with their furnace sintered counterparts. This was attributed to the higher densities and additional reinforcement by the presence of the oxide phase in the as-hot-pressed material. Moderate iron additions, of between 6 and 10 wt.%, were found to have a strong positive effect on the ductility of the material notwithstanding its processing route.

PL

W artykule przedstawiono wpływ zawartości żelaza oraz procesów wytwarzania na mikrostrukturę i własności mechaniczne spieków kobalt-żelazo.pieki zawierajace od 3 do 15% zelaza wykonano z komercyjnych proszków metodą konwencjonalnego prosowania i spiekania oraz prasowania na goraco. materiały poddano badaniom gęstości, twardości, wytrzymałości, strukturalnym oraz fraktograficznym z wykorzystaniem mikroskopii optycznej i skaningowej. Przeprowadzone badania wykazały wyższe własności mechaniczne materiałów uzyskanych technologią prasowania na goraco w porównaniu z materiałami spiekanymi. Wynikają one z wiekszej gęstosci spieków oraz umocnieniem wywołanym obecnością tlenków. Wykazano, że zawartośc żelaza w zakresie od 6 do 10% ma bardzo korzystny wpływ na plastyczność spieków niezależnie od sposobu ich wytwarzania.

13

Struktura i własności wybranych spieków Co-Fe prasowanych na gorąco.

Frydrych H., Romański A., Konstanty J., Kordzikowska M.

Rudy i Metale Nieżelazne

|

2003

|

R. 48, nr 2

85-89

PL

Przedstawiono wyniki badań poświęconych ustaleniu wpływu zwiększającej się zawartości żelaza na własności fizyczne, mechaniczne i strukturę prasowanych na gorąco spieków kobaltu. Analizie poddano materiały zawierające 3, 6, 10 i 15 % żelaza. Stwierdzono, że w miarę zwiększania zawartości żelaza własności wytrzymałościowe badanych materiałów pogarszają się, podczas gdy własności plastyczne ulegają poprawie. Największą plastyczność spieków uzyskano dla zawartości 10 % żelaza. Dalsze zwiększenie zawartości żelaza powoduje wzrost wytrzymałości spieków. W wyniku zastosowania technologii prasowania na gorąco uzyskano spieki o bardzo drobnoziarnistej strukturze, znacznie niejednorodnej pod względem składu chemicznego.

EN

Results of a research into determination of an effect of increasing iron content in hot-pressed cobalt sintered compacts on their physical and mechanical properties and structure have been presented. The analysis was made for materials containing 3. 6, 10 and 15% Fe showing that the increase of iron content resulted in deterioration of mechanical properties of the material and in improvement of its plasticity. The highest plasticity was observed for the sinters containing 10% Fe, and further increase of the Fe content resulted in the increase of material's strength. The material obtained by hot-pressing had fine-grained structure, and its chemical composition was clearly inhomogeneous.

14

Spiekane materiały kobalt-zelazo ich struktura i własności.

Frydrych H., Romański A., Pawińska E.

Rudy i Metale Nieżelazne

|

2003

|

R. 48, nr 7

326-332

PL

Przedstawiono wyniki badań poświęconych ustaleniu wpływu zwiększającej się zawartości żelaza na własności fizyczne, mechaniczne i strukturę spieków kobaltu otrzymanych konwencjonalną technologią. Analizie poddano materiały zawierające 3, 6, 10, 15 i 25 % żelaza. Stwierdzono, że zwiększeniu zawartości żelaza od 5 do 15 % towarzyszy obniżenie własności wytrzymałościowych spieków. Największą plastycznością charakteryzują się natomiast spieki z dodatkiem 6 % Fe. Natomiast w przypadku większych zawartości żelaza obserwuje się znaczące zmniejszenie plastyczności spieków. W wyniku prasowania i spiekania mieszanek elementarnych proszków, uzyskano spieki o bardzo drobnoziarnistej strukturze, o coraz większym ziarnie w miarę wzrostu zawartości żelaza.

EN

Results of the investigation into an effect of increasing iron content on the physical and mechanical properties and the structure of cobalt sinters obtained by conventional technology are presented. The materials examined contained 3, 6, 10, 15 and 25 % iron. It was found that an increase of iron content from 5 to 15 % resulted in determination of the strength of sinters, and the highest plasticity had those with an addition of 6 % Fe. At higher iron content, plasticity of the sinters was significantly worse. Mixtures of the basic powders were pressed and sintered, and the sinters obtained had a fine-grained structure. It was also found that an increase of iron content resulted in greater grain size.

15

Spieki narzędziowe metaliczno-diamentowe - własności użytkowe a własności materiału osnowy.

Romański A., Frydrych H., Konstanty J.

Rudy i Metale Nieżelazne

|

2002

|

R. 47, nr 10-11

564-569

PL

Materiały metaliczno-diamentowe, które są elementami roboczymi pił stosowanych do cięcia i obróbki kamieni naturalnych, powinny charakteryzować się dwiema najważniejszymi własnościami: długą żywotnością i zapewniać eksploatację przy umiarkowanym zużyciu energii elektrycznej. W zależności od rodzaju obrabianego kamienia, własności te są wynikiem nie tylko zawartości cząsteczek diamentu, ale przede wszystkim uzależnione są od własności materiału osnowy. Aby świadomie kształtować strukturę i własności materiałów osnowy, konieczna jest znajomość podstawowych zależności występujących pomiędzy nimi a własnościami użytkowymi narzędzi. Próbę ustalenia tych zależności zaprezentowano w niniejszym artykule.

EN

Diamond impregnated segments used in the stone industry for stone cutting applications should guarantee a long tool life and ensure a low power consumption during operation. Depending on the stone type to be cut, these properties are a consequence of the diamond's concentration and bond's properties. In order to engineer the structure and mechanical properties of the metal bond in an efficient way, it is necessary to know the relationships between the bond and segment's properties. This paper describes the effect of the bond's structure and mechanical properties on the behaviour of the tool.

16

Wpływ temperatury spiekania na własności i strukturę spiekanych brązów cynowych

Frydrych H., Romański A., Olszewska I.

Rudy i Metale Nieżelazne

|

2001

|

R. 46, nr 4

181-185

PL

Wykonano badania struktury i własności spieków otrzymanych z trzech różnych proszków brązu cynowego, pochodzących z importu. Zastosowano różne temperatury spiekania. Określono wpływ temperatury spiekania na gęstość i zmiany wymiarowe spieków oraz ich wytrzymałość na zginanie.

EN

The structure and properties of sinters produced at various temperatures, from three different, foreign, tin bronze powders, were analysed. The relations of sintering temperatures, density and bending strength of the sinters were defined.

17

Rola manganu w spiekanych stalach.

Romański A., Frydrych H.

Rudy i Metale Nieżelazne

|

1998

|

R. 43, nr 3

132-139

PL

Na podstawie danych literaturowych przedstawiono przegląd badań nad własnościami spiekanych stali manganowych. Podano również wpływ dodatków stopowych, takich jak miedź, molibden, krzem na zmiany wymiarowe badanych spieków, gęstość, wytrzymałość na rozciąganie, granicę plastyczności, twardość i wydłużenie tych stali.

EN

Based on the review of papers the results of the investigations of sintered manganese steels are presented. The effect of additional alloying elements such as copper, molibdenium and silicon on dimensional changes, density, tensile strength, yield strength, hardness and elongation of such steels are also reported.

18

Properties of Mo-alloyed sintered manganese steels.

Romański A., Ciaś A.

Inżynieria Materiałowa

|

1998

|

R. XIX, nr 4

1175-1178

EN

Sintered alloy steels are needed for mostly PM structural parts. Powder metallurgy techniques provide a means of fabricating high quality steel parts with tailored mechanical properties. It is now possible to produce sintered steel parts with properties equal to and even superior to those of parts made by more traditional routes. Challenges arise both with the material selection and component fabrication. This presentation outlines the processing for high performance structural application.