Microstructure, surface topography and properties of the Ti-6Al-4V alloy nitrided under glow discharge.

Czyrska-Filemonowicz A., Łucki M., Buffat P.A., Moskalewicz T., Lekki J., Wierzchoń T.

Archives of Materials Science

2005

Vol. 26, nr 1-2

79-88

Investigation of the microstructure, topography and properties of the as received Ti-6Al-4V alloy as well as nitrided under glow discharge was performed. The microstructural analyses were carried out using LM, XRD, SEM and analytical TEM. Phase identification and chemical composition of the layer and bulk material were determined by electron diffraction and by energy dispersive X-ray spectrometry. Atomic force microscopy was applied for layer surface topography measurements. Microhardness and Young's modulus measurements together with frictional wear resistance and corrosion resistance tests were performed. The investigation revealed a clear correlation between micro/nanostructure and surface topography of nitrided multilayer with its micro-mechanical, tribological and corrosion properties.

Analytical TEM and AFM studies of nitrided multilayer titanium-base biomaterials

Czyrska-Filemonowicz A., Buffat P.A., Łucki M., Moskalewicz T., Wierzchoń T.

Inżynieria Materiałowa

2004

R. XXV, nr 3

335-338

The micro/nanostructure of the Ti-base alloys (Ti-1Al-1Mn and Ti-6Al-4V) nitrided under glow discharge was characterised using light microscopy, scanning- and analytical transmission electron microscopy (TEM). TEM investigations revealed a very complex multilayered microstructure produced by diffusion at 850°C and 900°C. The delta-TiN, Ti2N and alpha (N) solid solution containing up to 19 at% nitrogen were identified in the nitrided multilayer formed on Ti-1Al-1Mn alloy. The layers formed on the Ti-6Al-4V alloy contain, besides the phases mentioned above, also the Ti2AlN and other minor phases. The topography of the nitrided alloys was investigated by means of atomic force microscopy (AFM). The investigation shows that the nitrided layers present a high degree of surface development. A relationship between the microstructure of the investigated alloys, their micro-mechanical and tribological properties is established. It is shown that the improved properties are related to the presence of nanocrystalline TiN in the outmost sublayer on the top of Ti2N layers that is produced by nitriding under glow discharge on both investigated alloys.

Materiałem do badań były stopy tytanu (Ti-1Al-1Mn i Ti-6Al-4V) azotowane w warunkach wyładowania jarzeniowego. Za pomocą mikroskopu świetlnego, skaningowego- i analitycznego transmisyjnego mikroskopu elektronowego (TEM) przeprowadzono szczegółową charakterystykę mikro/nanostruktury. Badania wykonane przy użyciu TEM ujawniły złożoną mikrostrukturę warstw azotowanych wytworzonych w temperaturach 850 i 900°C. W warstwie azotowanej wytworzonej na stopie Ti-1Al-1Mn zidentifikowano następujące fazy delta-TiN, Ti2N i roztwór stały alfa (N) zawierający do 19% at azotu. Warstwa wytworzona na stopie Ti-6Al-4V oprócz w/w faz zawierała również Ti2AlN oraz inne fazy. Pomiary topografii powierzchni wykonane za pomocą mikroskopu sił atomowych (AFM) wykazały, że warstwy azotowane mają duży stopień rozwinięcia powierzchni. Stwierdzono występowanie wyraźnej korelacji pomiędzy mikrostrukturą azotowanych stopów tytanu, a ich właściwościami mikro-mechanicznymi i tribologicznymi. Wykazano, że poprawa tych właściwości w obu badanych stopach wynika z obecności zewnętrznej nanokrystalicznej podwarstwy TiN wytworzonej przez azotowanie w warunkach wyładowania jarzeniowego.