Effects of ageing heat treatment temperature on the properties of DMLS additive manufactured 17-4PH steel

Świetlicki Aleksander, Wlaczak Mariusz, Szala Mirosław, Turek Marcin, Chocyk Dariusz

Bulletin of the Polish Academy of Sciences. Technical Sciences

|

2023

|

Vol. 71, nr 4

art. no. e146237

EN

Additive manufacturing (AM) is a modern, innovative manufacturing method that enables the production of fully dense products with high mechanical properties and complex shapes that are often impossible to obtain by traditional methods. The 17-4PH grade steel is often applied where high mechanical performance is required. 17-4PH, or AISI 630, is intended for precipitation hardening, an operation that combines solution and ageing treatments and is used to significantly change the microstructure of the steel and enhance its mechanical properties. This study investigates the effect of precipitation hardening on the properties of 17-4PH steel. To examine microstructure and morphology, metallographic tests were performed together with phase composition and chemical composition analyses. Mechanical parameters were determined via Vickers hardness testing and the Oliver-Pharr method. Samples were fabricated using direct metal laser sintering (DMLS), which is one of the powder bed fusion methods. The use of a constant solution treatment temperature of 1040_C and different ageing temperatures made it possible to evaluate the effects of ageing temperature on the mechanical properties and microstructure of 17-4PH. The presence of face-centered cubic FCC g-austenite and body-centerd cubic BCC a-martensite structures were detected. The tests revealed that – similarly to the wrought material – the highest hardness of 382_10:3 HV0:2 was obtained after ageing at 450_C. The nanoindentation test showed the same H/E ratio for the sample after fabrication and after solution treatment at 0.016769, but this value increased after ageing to 127–157.5%. The sample aged at 450_C was characterized by the highest H/E ratio of 0.026367, which indicates the highest wear resistance of this material under employed treatment conditions. In general, the sample treated at 450_C showed the best performance out of all tested samples, proving to have the smallest grain size as well as high Vickers and nanoindentation hardness. On the other hand, the use of solution treatment led to reduced hardness and improved workability of the AM material.

2

Effect of shot peening on corrosion resistance of additive manufactured 17-4PH steel

Świetlicki Aleksander, Walczak Mariusz, Szala Mirosław

Materials Science Poland

|

2022

|

Vol. 40, No. 3

135--151

EN

Components produced by additive manufacturing (AM) via direct metal laser sintering (DMLS) have typical as-fabricated surface defects. As a result, surface properties of AM products should be modified to increase their strength, anti-wear behavior, and at the same time ensure their high corrosion resistance. Surface modification via shot peening (SP) is considered suitable for AM of engineering devices made of 17-4PH (X5CrNiCuNb16-4) stainless steel. The objective of this study was to determine the effect of three types of peening media (CrNi steel shot, glass, and ceramic beads) on the corrosion resistance of specimens of DMLS 17-4PH stainless steel. Results demonstrated that SP caused steel microstructure refinement and induced both martensite (α) formation and retained austenite (γ) reduction. 17-4PH specimens peened showed the increase in surface hardness of 255, 281, and 260 HV0.2 for ceramic, glass, and steel, respectively. DMLS 17-4PH specimens modified by SP exhibited different surface morphology, hardness, and microstructure and thus, these properties affect corrosion performance. The results implied that steel shot peened with steel shot showed the highest resistance to corrosion processes (Icorr= 0.019μA/cm2), slightly worse with glass (Icorr= 0.227μA/cm2) and ceramics (Icorr= 0.660μA/cm2) peened. In the case of ceramic and glass beads, it was possible to confirm the presence of the above-mentioned particles in the surface layer after SP.

3

Cavitation erosion of electrostatic spray polyester coatings with different surface finish

Szala Mirosław, Świetlicki Aleksander, Sofińska-Chmiel Weronika

Bulletin of the Polish Academy of Sciences. Technical Sciences

|

2021

|

Vol. 69, nr 4

art. no. e137519

EN

Polyester coatings are among the most commonly used types of powder paints and present a wide range of applications. Apart from its decorative values, polyester coating successfully prevents the substrate from environmental deterioration. This work investigates the cavitation erosion (CE) resistance of three commercial polyester coatings electrostatic spray onto AW-6060 aluminium alloy substrate. Effect of coatings repainting (single- and double-layer deposits) and effect of surface finish (matt, silk gloss and structural) on resistance to cavitation were comparatively studied. The following research methods were used: CE testing using ASTM G32 procedure, 3D profilometry evaluation, light optical microscopy, scanning electron microscopy (SEM), optical profilometry and FTIR spectroscopy. Electrostatic spray coatings present higher CE resistance than aluminium alloy. The matt finish double-layer (M2) and single-layer silk gloss finish (S1) are the most resistant to CE. The structural paint showed the lowest resistance to cavitation wear which derives from the rougher surface finish. The CE mechanism of polyester coatings relies on the material brittle-ductile behaviour, cracks formation, lateral net-cracking growth and removal of chunk coating material and craters’ growth. Repainting does not harm the properties of the coatings. Therefore, it can be utilised to regenerate or smother the polyester coating finish along with improvement of their CE resistance.