Mechanical Spectroscopy of Bearing Steel

Lu X., Li W., Lu X., Jin M., Min N., Jin X.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 3A

2085--2091

This study presents mechanical spectroscopy of bearing steel subjected to different heat treatments. A non-thermally activated maximum, P1, was found at 130°C, in quenched martensitic samples, which were austenitized at 1050°C and 860°C, and presented twin martensite microstructures. It is suggested that the mechanism of the P1 maximum, observed on the low-temperature side of Snoek-Köster peak, is related to the change of defect configurations in twinned martensite assisted with high mobility of the solute carbon atoms under an external harmonic stress field applied during mechanical loss measurements.

W pracy przedstawiono wyniki badań spektroskopii mechanicznej stali łożyskowej poddanej różnej obróbce cieplnej. W hartowanych martenzytycznych próbkach, które były austenityzowane w 1050°C i 860°C, i posiadały bliźniaczą mikrostrukturę martenzytu, występuje nietermicznie aktywowane maksimum P1 przy 130°C. Sugeruje się, że mechanizm maksimum P1, które występuje na niskotemperaturowym zboczu piku Snoek-Köstera, związane jest ze zmianą konfiguracji defektów w bliźniaczym martenzycie, przy wysokiej ruchliwości atomów węgla. Maksimum P1 ujawnia się pod wpływem działania harmonicznie zmiennego zewnętrznego pola naprężeń przyłożonego do próbki w trakcie badań metodą spektroskopii mechanicznej.

Experimental Investigation Of Segregation Of Carbon Atoms Due To Sub-Zero Cryogenic Treatment In Cold Work Tool Steel By Mechanical Spectroscopy And Atom Probe Tomography

Min N., Li H. M., Xie C., Wu X. C.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

1109--1113

In this work, we present mechanical spectroscopy of cold work tool steel subjected to sub-zero cryogenic soaking treatment to reveal the carbon segregation and the subsequent carbides refinement. The maximum of Snoek-Köster (SK) peak height was obtained in the sample subjected to soaking 1h at −130°C cryogenic treatment. The SK peak height is reduced with prolonging the soaking time. The results indicate that an increase in the height of SK peak is connected with an increase in dislocation density and the number of segregated carbon atoms in the vicinity of dislocations or twin planes after martensite transformation at −130°C which is confirmed by corresponding TEM and atom probe tomography measurement. Hence, it is suggested that the isothermal martensite, formed during the cryogenic soaking treatment decreases (APT) the height of SK peak.

W pracy przedstawiono wyniki spektroskopii mechanicznej stali narzędziowej do pracy na zimno poddanej obróbce kriogenicznej w celu odsłonięcia segregacji węgla i późniejszego tworzenia węglików. Dzięki połączeniu transmisyjnej mikroskopii elektronowej (TEM) i tomografii atomowej (APT) uzyskano maksymalny pik Snoek-Köstera (SK) w próbce poddanej obróbce kriogenicznej przez 1 godzinę w −130°C. Wysokość piku SK obniża się wraz z wydłużeniem czasu obróbki. Wyniki wskazują, że zwiększenie wysokości piku SK jest połączone ze wzrostem gęstości dyslokacji i liczby segregowanych atomów węgla w sąsiedztwie dyslokacji lub płaszczyzn bliźniaczych po przemianie martenzytycznej w -130°C, co potwierdzone jest odpowiednimi pomiarami TEM oraz APT. W związku z tym proponuje się, że izotermiczny martenzyt powstały podczas obróbki kriogenicznej zmniejsza wysokość piku SK.