The effects of artificial-aging temperature on tensile strength, hardness, microstructure, and fault morphology in AlSiMg

Andoko, Yanuar, Puspitasari P., Ariestoni T. B.

Journal of Achievements in Materials and Manufacturing Engineering

2020

Vol. 98, nr 2

49--55

Purpose: This research examined the effects of artificial-aging temperature and time on tensile strength, hardness, microstructure, and fault morphology in AlSiMg. Design/methodology/approach: This research was conducted using aluminium alloy at 120°C, 150°C, and 180°C artificial-aging temperature and 6 hours holding time. The tensile test used ASTM B211-03 standard and hardness test adapted to ALCOA 6061 standard. Findings: Tensile test results indicated the highest tenacity on aluminium alloy at a 150ºC temperature that was 47.263% strain level. In addition to the strain level, this research also obtained the highest tensile strength level at 180ºC that was 62.267 kgf/mm2 and the highest hardness value that was 110 HV. The increase in tensile strength and hardness at 180°C was caused by the increase in Mg, Si, and Al. Based on the microstructure test, the highest tenacity was obtained at 150°C temperature as the result of closed and gathered Mg2Si precipitates; while at 180°C temperature, the precipitates appeared to be more distributed, causing a rise in hardness value and tensile strength. AlSiMg tenacity also exhibited from the number of dimples compared to cleavages at 150°C temperature. Research limitations/implications: The limitation that found in this research was conducted using AlSiMg aluminium Al6061 specimen with an artificial-aging treatment at 120ºC, 150°C, and 180°C temperature for 6 hours and then compared to the raw material. AlSiMg tensile specimen was made according to ASTM E8-E8M standard. Practical implications: This research can be applied in industrial manufacture process to find tensile strength, hardness, microstructure, and fault morphology of Al6061 alloy. Originality/value: According to research result, can be understood that by conducting these experiments, Artificial-aging treatment temperature variations in AlSiMg aluminium alloy could increase hardness.