Nanohardness and elasticity of cell walls of Scots pine (Pinus sylvestris L.) juvenile and mature wood

Mania P., Nowicki M.

Bulletin of the Polish Academy of Sciences. Technical Sciences

2020

Vol. 68, nr 5

1237--1241

The aim of this study was to determine the hardness and reduced modulus of elasticity of juvenile wood of Scots pine (Pinus sylvestris L.) using the nanoindentation method, and then to compare the results obtained with those of mature wood. The hardness of juvenile pine wood determined by means of the nanoindentation method was 0.444 GPa while for mature wood it was 0.474 GPa. Statistically significant differences between the values were found. The reduced modulus of elasticity in juvenile wood was 14.0 GPa and 16.4 GPa in mature wood. Thus, the hardness values obtained were about 7% higher, while the modulus of elasticity was 17% higher in mature wood. All determinations were made in the S2-layer of the secondary cell wall.

Investigation of Modal Behaviour of Resonance Spruce Wood Samples (Picea abies L.)

Mania P., Fabisiak E., Skrodzka E.

Archives of Acoustics

2017

Vol. 42, No. 1

23--28

Results of experimental modal analysis of a resonance and non-resonance spruce wood (Picea abies L.) are presented. The resonance wood came from a tree from Poland and Bosnia and Herzegovina, while the non-resonance wood came from the vicinity of Olsztyn from the north-eastern Poland. The modal parameters (modal frequency, modal damping and mode shapes) of the wood samples were determined for the samples of 8 mm in thickness. Modal analysis was made by pulse excitation. The resonance and non-resonance wood differ in the fundamental modal parameters as well as in the number of potential modes. Additionally, calculated values of damping factor are presented. The values are much bigger for a non-resonance wood than for good quality resonance spruce.