Texture inhomogeneity in titanium deformed by ECAP

Skrotzki W., Kloden B., Lankau A., Chulist R., Kopylov V., Brokmeier H.-G.

Archives of Metallurgy and Materials

2008

Vol. 53, iss. 1

29-32

Titanium of commercial purity was deformed by equal channel angular pressing (ECAP) with back-pressure at 380°C using 4 passes of route Bc. Billets of 120 mm length were pressed at 0.4 mm s -1 through square channels (14 mm x 14 mm) intersecting sharply at an an gle of 90°. The global texture measurements of the starting and ECAP processed material were done by neutron diffraction. To investigate the texture inhomogeneity after ECAP the local texture was measured with high-energy synchrotron radiation at different positions in the cross-section of the billet. The texture gradient with regard to intensity and orientation of the dominant texture component is characterized and discussed.

Tytan o czystości przemyslowej (klasa 2) zostal odkształcony w procesie wyciskania w kanale kątowym (ECAP) z przeciwciśnieniem w temperaturze 380°C w 4 przepustach wg. drogi BC. Wlewki 120 mm długości byly wyciskane przy predkości 0.4 mm s-1 przez prostokątny kanał kwadratowy (14 x 14 mm2 ). Pomiary tekstury globalnej w materiale wejściowym i po odkształceniu wykonano metodą dyfrakcji neutronów. Aby zbadać niejednorodność tekstury po odksztalłeniu zmierzono tekstury lokalną przy wykorzystaniu promieniowania synchrotronowego o wysokiej energii w różnych obszarach przekroju poprzecznego wlewka. Wskazane zostały zalety tej metody ujawnienia gradientu tekstury. Omówione zostały intensywności odchylenia dominujących składowych tekstury w odniesieniu do ich idealnych położeń wynikających z prostego ścinania.