Microstructure and mechanical properties of friction stir lap welded dissimilar Al/Ti alloys by ultrasonic assistance

Dong Zhibo, Zhang Ziao, Hu Wei, Gong Peng, Lv Zan

Archives of Metallurgy and Materials

2022

Vol. 67, iss. 1

91--96

Dissimilar Al/Ti alloy sheets were lap welded with ultrasonic assistance in this work. The influence of ultrasonic vibration on formation, intermetallic compounds (IMCs) and tensile failure load of the obtained joints was discussed. The results showed that voids formed at the lap interface without ultrasonic assistance. No voids can be observed on the joint welded with ultrasonic because the vibration during welding improved the material flow. No obvious IMC formed at the Al/Ti bonding interface of the joint welded without ultrasonic assistance. An IMC layer formed at the bonding interface of Al/Ti with ultrasonic assistance and its thickness increased with decreasing the welding speed. The failure load of the joint welded with ultrasonic assistance was higher than the joint without ultrasonic because the void was eliminated and the thin IMC layer formed at the bonding interface was beneficial to joint strength. All joints presented shear failure mode during the tensile shear tests.

Ultrasonic Assisted Active-Passive Filling Friction Stir Repairing to Eliminate Volume Defects

Wang Tao, Gong Xue, Ji Shude, Xue Gang, Lv Zan

Archives of Metallurgy and Materials

2021

Vol. 66, iss. 1

217--222

Ultrasonic assisted active-passive filling friction stir repairing (A-PFFSR) was proposed to repair volume defects in the metallic parts. Sound joints without interfacial defects could be achieved. Firstly, the ultrasonic was beneficial to improving material flow and atom diffusion, and then eliminated kissing bond defects compared to conventional A-PFFSR joints. Secondly, the equiaxed grains were refined by ultrasonic vibration. Lastly, the repairing passes were reduced due to the ultrasonic, which decreased softening degree of the repaired joints. The maximum tensile strength of 150 MPa was achieved. Therefore, this strategy to repair the volume defects is feasibility and potential in the remanufacturing fields of aerospace and transportation.