Experimental phase studies in the TeO2–CdO system

Karaduman G., Celikbilek M., Ersundu A. E., Solak N., Tatar D., Aydin S.

Materiały Ceramiczne

2011

T. 63, nr 1

40-43

In the present study, phase equilibrium in the TeO2–CdO system has been investigated. Different compositions of (1-x)TeO2–xCdO, where x = 0.10, 0.20, 0.25, 0.30 and 0.40 in molar ratio were prepared. The samples waited at 750°C in a platinum crucible for 30 minutes and then quenched in a water bath. DTA studies performed on as-cast samples. According to the DTA results, all samples were heat-treated at 550°C for 24 hours to obtain phase equilibrium. XRD and SEM/EDS studies were performed on the crystallized samples for microstructural analysis.

W prezentowanej pracy zbadano równowagę fazową w układzie TeO2–CdO. Przygotowano różne składy (1-x)TeO2 – xCdO, gdzie x = 0,10, 0,20, 0,25, 0,30 i 0,40 mol.%. Próbki przetrzymywano w 750°C w tyglu platynowym przez 30 min., a następnie szybko chłodzono w kąpieli wodnej. Badania DTA przeprowadzono na świeżo wytopionych próbkach. Zgodnie z wynikami DTA, wszystkie próbki wygrzewano w 550°C przez 24 h, aby uzyskać stan równowagi fazowej. Badania XRD i SEM/EDS przyprowadzono na wykrystalizowanych próbkach w przypadku analizy mikrostrukturalnej.

Microstructural and thermal characterization of the TeO2–WO3 system

Celikbilek M., Karaduman G., Ersundu A. E., Solak N., Tatar D., Aydin S.

Materiały Ceramiczne

2010

T. 62, nr 4

556-559

In the present study, thermal behaviour and microstructure of the TeO2–WO3 system have been investigated. Different compositions of (1-x)TeO2 – xWO3 system (x = 0.02, 0.05, 0.15, 0.25 and 0.40 in molar ratio) were prepared. The samples waited at 750°C in a platinum crucible for 30 min and then quenched in a water bath. DTA studies were performed on glassy samples. Afterwards, all samples were heat-treated at 550°C for 24 h and furnace cooled to obtain phase equilibrium. XRD and SEM/EDS studies were performed on the crystallized samples for microstructural analysis.

W prezentowanej pracy zbadano zachowanie cieplne i mikrostrukturę tworzyw w układzie TeO2-WO3. Przygotowano różne składy układu (1-x)TeO2 – xWO3, gdzie x = 0.02, 0.05, 0.15, 0.25 i 0.40 w stosunku molowym. Próbki przebywały w 750°C w tyglu platynowym przez 30 min a potem szybko chłodziły się w wodzie. Badania DTA przeprowadzono na próbkach szklistych. Następnie, wszystkie próbki zostały wygrzane w . 550°C przez 24 h i schłodzone z piecem w celu osiągnięcia równowagi fazowej. Badania XRD i SEM/EDS przeprowadzono na krystalizowanych próbkach w przypadku analizy mikrostrukturalnej.