The role of ECAP in densification behaviour of PM aluminium alloy

Bidulska J., Kocisko R., Kovacova A., Dutkiewicz J.

Inżynieria Materiałowa

|

2011

|

Vol. 32, nr 2

82-85

EN

The present paper focused on the role of ECAP process on the densification behaviour of PM aluminium alloys. An aluminium powder Al-Mg- Si-Cu-Fe was used as material to be investigated. After applying different compacting pressures in the range of 400 to 700 MPa, specimens were dewaxed at 400°C for 60 min. Sintering was carried out in a vacuum furnace at 610°C for 30 min. The specimens were ECAPed for 1 pass. Structural characterization was carried out on the minimum of 10 different image fields for pressed and sintered specimens as well ECAPed specimens. A decrease of porosity was revealed for all specimens.

PL

Praca dotyczy zastosowania technologii przeciskania przez kanał kątowy ECAP dla zagęszczania proszków stopów aluminium. Badano proszek stopu aluminium Al-Mg-Si-Cu-Fe. Po zastosowaniu prasowania przy różnych ciśnieniach od 400÷700 MPa, próbki oczyszczano z substancji organicznych przez wyżarzanie w 400°C przez 60 min. Następnie próbki spiekano w temperaturze 610°C przez 30 min. Następnie poddano je przeciskaniu w kanale ECAP. Porównano struktury próbek spiekanych i przeciskanych w kilku miejscach i stwierdzono znaczny spadek porowatości.

2

Application of the torsion test in calculating the extrusion force

Pernis R., Bidulska J., Kvačarkaj T., Pokorny I.

Archives of Metallurgy and Materials

|

2011

|

Vol. 56, iss. 1

81-85

EN

The paper deals with the calculation of the extrusion force using the results of the torsion test of aluminium alloy EN AW-2014. The mathematical model for the calculation of the extrusion force requires the knowledge of the functional relationship between the yield stress and the temperature, the deformation and the deformation rate. Based on the proposed mathematical model for the calculation of the yield stress, the functional relationship was derived to determine the extrusion force in the hot extrusion of semi-products of aluminium alloy EN AW-2014.

3

Wear resistance of various type sintered steels

Bidulsky R., Actis Grande M., Zago A., Brytan Z., Bidulska J.

Archives of Metallurgy and Materials

|

2010

|

Vol. 55, iss. 3

623-629

EN

In this work, the influences of the processing conditions (applied load, cooling rate) on the wear resistance of sintered steels were presented. The wear behaviour of various sintered steels, including Astaloy LH, Astaloy CrL, Distaloy AE, PASC60, 316 L and 430 L were carried out by a pin-on-disk test. The effect of chemical composition and different applied loads in vacuum furnace related to a wear resistance (mass loss versus sliding distance) was investigated. The results showed that the microstructure constituents along with relevant hardness values represent an important parameter affecting the wear behaviour of sintered steels and the sinter hardening is suitable heat treatment for improving the wear resistance of sintered steels.

PL

W pracy przedstawiono wpływ parametrów wytwarzania (ciśnienia prasowania, szybkości chłodzenia) na zużycie ścierne stali spiekanych. Mechanizm zużycia ściernego różnych typów stali określono przy użyciu testu pin-on-disk. Zbadano wpływ składu chemicznego oraz ciśnienia prasowania podczas spiekania w próżni na odporność na zużycie ścierne (ubytek masy w funkcji drogi tarcia). Wyniki badań wykazały, że składniki strukturalne wraz z ich charakterystyczną twardością stanowią ważny czynnik wpływający na mechanizm zużycia ściernego, a zastosowanie obróbki cieplnej typu "sinter hardening" jest właściwe dla polepszenia odporności na użycie ścierne stali spiekanych.