Curing reaction of azomethine epoxy liquid crystals

Cascaval C. N., Mititelu-Mija A.

Polimery

2007

T. 52, nr 4

251-254

The aromatic epoxy N,N-bis[4-(2,3-epoxy propoxy)benzylidene]-1,4-phenylenediamine (AZ-1) with mesogenic properties was synthesized and cured in the presence of 4,4’-methylene-bis(3-chloro-2,6-diethylaniline) (MCDEA) or 2,7-diaminofluorene (DAF) as the curing agents. The curing reactions were studied by differential scanning calorimetry (DSC), polarized optical microscopy (POM) and wide-angle X-ray scattering. The product obtained in the curing reaction of AZ-1/MCDEA mixture shows a texture of smectic-like structure. The curing reaction of AZ-1/DAF mixture led to a heterogeneous structure, without liquid crystalline properties.

Zsyntetyzowano aromatyczną epoksydową N,N’-bis[4-(2,3-epoksypropoksy)benzylideno]-1,4-fenylenodiaminę (AZ-1, Schemat A) wykazującą właściwości mezogeniczne, którą następnie utwardzano w obecności 4,4’-metyleno-bis(3-chloro-2,6-dietyloaniliny) (MCDEA) lub 2,7-diaminofluorenu (DAF) (schemat B). Reakcję utwardzania badano metodą skaningowej kalorymetrii różnicowej (DSC) (rys. 1, 4 i 5), szerokokątowego rozpraszania promieni rentgenowskich (WAXS) (rys. 3) i za pomocą polaryzacyjnego mikroskopu optycznego (POM) (rys. 2). Produkt otrzymany w wyniku utwardzania mieszaniny AZ-1/MCDEA charakteryzuje się teksturą odpowiadającą fazie smektycznej. Utwardzanie mieszaniny AZ-1/DAF prowadzi do otrzymania struktury heterogenicznej, która nie wykazuje właściwości ciekłokrystalicznych.

Kinetics of the curing reaction of selected epoxy resin-amine systems

Cascaval C. N., Rosu D., Mititelu-Mija A., Rosu L.

Polimery

2006

T. 51, nr 3

199-205

The paper is a review of authors' research works on curing reaction of some commercial and synthesized by them epoxy resins (among others - with liquid crystalline fragments). As curing agents 5 aromatic diamines differing in chemical structure were used. The results of investigation of curing kinetics by differential scanning calorimetry (DSC) confirm the significant effect of heating rate (up to 20 oC/min) on the process. It was found, for example, that for small heating rate (2-5 oC/min) DSC thermograms of epoxy resins with liquid crystalline fragments show double exothermic peak contrary to the thermograms of typical epoxy resins showing single exothermic peaks. This phenomenon is attributed to the formation of smectic structure during the curing (at temp. 132-162 oC). Usefulness of three various kinetic models (by Barret, Borchardt-Daniels or Kissinger) describing the curing process investigated have been compared.

Artykuł przedstawia przegląd własnych prac dotyczących reakcji utwardzania niektórych handlowych i syntetyzowanych przez autorów żywic epoksydowych [handlowej żywicy epoksydowej typu diglicydylowego eteru bisfenolu A (DGEBA), diglicydylowego eteru 4,4'-bifenolu (DGEBP), trzech różniących się podstawnikiem R we wzorze ogólnym (II) czerofunkcyjnych żywic epoksydowych otrzymanych na podstawie tetraglicydylowych pochodnych różnych diamin, a także związku epoksydowego zawierającego mezogeniczny fragment bifenylowy (DGEBP) bądź naftalenowy (DGEDHN)]. Jako utwardzacze zastosowano 5 różniących się budową chemiczną diamin aromatycznych (tabela 1). Wyniki badania kinetyki utwardzania metodą różnicowej kalorymetrii skaningowej (DSC, rys. 1-3, tabele 4 i 5) świadczą o istotnym wpływie szybkości ogrzewania (do 20 oC/min) na ten proces. Stwierdzono m.in., że w warunkach małej szybkości ogrzewania (2-5 oC) na termogramach DSC żywic epoksydowych z fragmentami ciekłokrystalicznymi (np. DGEBP, rys. 4) występuje podwójny pik egzotermiczny, w przeciwieństwie do termogramów typowych żywic epoksydowych z pojedynczym pikiem egzotermicznym. Zjawisko to przypisano tworzeniu się w trakcie utwardzania (temp. 132-162 oC) struktury smektycznej. Porównano przydatność trzech różnych modeli kinetycznych (Barretta, Borchardta-Danielsa i Kissingera, tabela 5) do opisu badanego procesu utwardzania.