Microstructure and microhardness of annealed austenitic cast steel

Christodoulou P., Chylińska R., Garbiak M., Piekarski B.

Inżynieria Materiałowa

|

2013

|

Vol. 34, nr 3

145--148

EN

The study proposes how to use the random HV0.01 microhardness measurements in the description of changes in the microstructure of 0,3C-18Cr-30Ni cast steel with an addition of titanium. The cast steel was investigated in four technological states, i.e. after annealing at 800°C for 10, 100, 500 and 1000 hours. Microhardness measurements were performed on unetched metallographic sections applying a 10 G load for 10 seconds. The measurements were taken at random, each time imposing a grid with 200 points on the surface of a metallographic section. Microhardness distribution density functions were detennined for the investigated technological cast steel States. To peaks occurring in different microhardness distribution density functions were assigned areas of the microstructure characterised by different content of the structural components.

PL

W pracy zaproponowano sposób wykorzystania losowego pomiaru mikrotwardości HV0,01 do opisu zmian w mikrostrukturze staliwa 0,3 C-18Cr-30Ni z dodatkiem tytanu. Badano staliwo w czterech stanach technologicznych - po wyżarzaniu w temperaturze 800°C przez 10, 100, 500 i 1000 godzin. Pomiary mikrotwardości przeprowadzono na zgładach nietrawionych, stosując obciążenie 10 G przez 10 sekund. Pomiary wykonano losowo, każdorazowo nakładając na powierzchnię zgładu siatkę 200 punktów. Wyznaczono funkcje gęstości rozkładów mikrotwardości dla badanych stanów technologicznych staliwa. Pikom występującym w poszczególnych funkcjach gęstości rozkładów mikrotwardości przyporządkowano obszary mikrostruktury charakteryzujące się odmiennym udziałem składników strukturalnych.

2

Sekwencyjne kształtowanie blach metalowych.

Christodoulou P.

Mechanik

|

2006

|

R. 79, nr 5-6

402-402

3

Comparative study of oxidation of Fe-Cr-B-C cast tool steels

Christodoulou P.

Inżynieria Materiałowa

|

2006

|

Vol. 27, nr 3

356-359

EN

A comparative study of oxidation resistance in the air at 900 oC of Fe-Cr-B-C cast tool alloys showed that these alloys outperform H13 tool steel that was used as reference point. Also, it was demonstrated that appropriate selection of low alloying elements (Ni, Cu, Mn, Si, C and B) can widely influence the oxidation resistance of the alloys, and significant influence of the combination of C and Si levels was revealed.

PL

Badania porównawcze odporności na utlenianie staliwa Fe-Cr-B-C w temperaturze 900 oC na powietrzu wykazały, że stopy te są zdecydowanie bardziej odporne na utlenianie od stali narzędziowej H13, która została wybrana jako punkt odniesienia w tych badaniach. Wykazano, że po przez odpowiedni dobór niskostopowych składników (Ni, Cu, Mn, Si, C i B) odporność tych stopów na utlenianie może być kontrolowana w szerokim zakresie. Również wykazano, że kombinacja dodatków C i Si w sposób istotny wpływa na odporność na utlenianie.