Optimizing Dry Ultrafine Grinding of Talc in Attritor Mill

El-Mofty Salah E., Elbendari A. M., El-Midany A. A., Abdel-Rahman M. K.

Inżynieria Mineralna

2023

no. 2, vol. 1

361--366

In this work, the parameters affecting the dry grinding of talc in the attritor mill were investigated. The attritor was tested with its initial design without balls then with balls as additional grinding media to prepare a feed passing 45 microns. The prepared feed (-45 mm) was used to produce a product with 10 μm or less using statistical design in presence of balls. The presence of balls enhances product fineness. The significance of the studied factors is: stirrer speed>mill filling >grinding time. In addition, the d50 was correlated with studied factors. The mean particle size (d50) as low as 6 μm was obtained at 460 rpm, 20% mill filling, and after 60 min grinding time.

W niniejszej pracy zbadano parametry wpływające na mielenie talku na sucho w młynie Attritor. Attritor został przetestowany w początkowej wersji bez kulek, a następnie z kulkami jako dodatkowym medium mielącym w celu przygotowania nadawy przechodzącej przez 45 mikronów. Przygotowany wsad (-45 mm) został wykorzystany do wytworzenia produktu o uziarnieniu 10 μm lub mniejszym przy użyciu statystycznego projektu w obecności kulek. Obecność kulek zwiększa stopień rozdrobnienia produktu. Znaczenie badanych czynników to: prędkość mieszadła > wypełnienie młyna > czas mielenia. Ponadto d50 był skorelowany z badanymi czynnikami. Średni rozmiar cząstek (d50) tak niski jak 6 μm uzyskano przy 460 obr/min, 20% wypełnieniu młyna i po 60 min mielenia.