Research on diatomite from Polish deposits and the possibilities of its use

Marczyk J., Pławecka K., Hebdowska-Krupa M., Nykiel M., Łach M.

Journal of Achievements in Materials and Manufacturing Engineering

|

2022

|

Vol. 115, nr 1

5--15

EN

Purpose: Diatomite from a deposit in Jawornik Ruski (Poland) has been selected as the material for study. The paper aimeds to show the possibility of using diatomite from the Carpathian Foothills as a sorbent of petroleum substances. Design/methodology/approach: Diatomite in the delivery condition (DC) and diatomite after calcination were used for this study. The material was calcined at 600, 650, 750, 850 and 1000°C. The diatomaceous earth was then granulated. The morphology of diatomite was observed using SEM. Particle size distribution was determined by Laser Particle Analyzer, chemical composition was determined by XRF, and mineralogical composition by XRD. Specific surface area, pore volume and pore size were determined. Thermal analysis (TG, DTA) was carried out. Absorption capacity tests were performed and the effect of diatomite addition on water absorption of concrete samples was determined. Findings: Within the framework of the study, it was shown that diatomite from the Jawornik deposit could be successfully used as a sorbent for petroleum substances. The absorption capacity of calcined at 1000°C diatomaceous earth was 77%. The obtained result exceeds the effectiveness of previously used absorbents, for which the sorption level is 60-70%. This allows commercial use of diatomite from deposits in Poland. In addition, water absorption tests have shown that diatomaceous earth can successfully replace cement used in concrete productione. The most favourablee effect on the reduction of water absorption is the addition of diatomite in the amount of 10%. Practical implications: The properties of diatomaceous earth from the Jawornik Ruski deposit indicate its high potential for use in the synthesis of geopolymers, which is important not only from an economic but also from an ecological point of view. Originality/value: The novelty of this work is the demonstration of the possibility of using diatomite as a sorbent of petroleum substances with high efficiency, exceeding the previously used sorbents.

2

Volcanic tuff as an inhibitor of corrosion in aqueous environment

Hebdowska-Krupa M., Łach M., Mikuła J.

Czasopismo Techniczne. Mechanika

|

2016

|

Y. 113, iss. 5-M

21--43

EN

The aim of the studies was to examine the applicability of volcanic tuff as a corrosion inhibitor in aqueous systems and to identify the mechanisms owing to which the tuff is acting as an inhibitor of corrosion. The scope of research includes: examinations of the structure and selected properties of the tuff from Filipowice, including fractographic examination of the Filipowice tuff rocks, X-ray diffraction analysis, and thermal analysis; study of the corrosion resistance of DC01A low-carbon steel in aqueous systems without and with inhibitor, which is volcanic tuff.

PL

Celem badań było określenie możliwości zastosowania wulkanicznego tufu jako inhibitora korozji w środowiskach wodnych oraz określenie mechanizmów, które powodują, że tuf wulkaniczny działa jako inhibitor korozji. Zakres badań obejmuje: badania struktury i wybranych właściwości tufu z Filipowic, w tym faktograficzne badania tufu w postaci skał, analizy dyfrakcji rentgenowskiej i analizy termicznej; badanie odporności na korozję DC01A stali niskowęglowej w środowiskach wodnych bez oraz z inhibitorem, którym jest tuf wulkaniczny.

3

Influence of the volcanic tuf on the wearability of varnish coating

Hebdowska-Krupa M.

Archives of Foundry Engineering

|

2010

|

Vol. 10, iss. 3 spec.

111--114

EN

At this work an influence of the volcanic tuf on the improvement in the wearability of varnish coatings was described. Examinations were conducted for covers made on the basis of single-component binder - alkid, two-component - acrylic and for comparison of paint hammerite and of varnish of the sailing boat preparation with the addition appropriately prepared of the volcanic tuf. Coatings were put directly on the low-carbon steel without earlier applying undercoats. Conducted examinations were aimed at determining loss of mass of the sample (in the mg) subjected by abrasive circles to the friction about the fixed charge. Comparing findings for covers made of binders mentioned above put directly on steel they stated that the addition of the preparation of the volcanic tuf considerably was improving the wearability of inspected covers.

4

Wpływ tufu wulkanicznego na zmianę charakteru korozji

Hebdowska-Krupa M., Mikuła J.

Zeszyty Naukowe Politechniki Świętokrzyskiej. Nauki Techniczne

|

2007

|

Z. 4

39-40

PL

W niniejszej pracy przedstawiono wyniki badań dotyczących zmiany charakteru korozji stali niskowęglowej DC01 A w środowisku 5% roztworu NaCl, w wyniku zmiany agresywności środowiska, poprzez dodanie do niego odpowiednio przygotowanego preparatu tufu wulkanicznego działającego jako nieorganiczny inhibitor korozji z uwagi na występowanie faz sprzyjających odporności na korozję tj. glinokrzemianu - K(AlSi3O8) oraz krzemionki - SiO2.

EN

In the work was carry out investigations of corrosion resistance of low-carbon steel DC01A in 5% solution NaCl with addition vulcanic tuf as inhibitor reagent. The diffraction X-ray analysis of vulcanic tuf indicated that it contain two phase: sanidine K(AlSi3O8) and quartz SiO2. The vulcanic tuf action as a corrosion of DC01 A steel operate moving the potential to the positive potentials. Microscopic investigations showed, that additions of vulcanic tuf influenced onto change of mechanism of corrosion (from piting to even dissolving).

5

Wpływ tufu wulkanicznego na własności powłok lakierniczych

Hebdowska-Krupa M., Mikuła J.

Zeszyty Naukowe Politechniki Świętokrzyskiej. Nauki Techniczne

|

2007

|

Z. 4

41-42

PL

W niniejszej pracy przedstawiono analizę możliwości zastosowania tufu wulkanicznego jako nieorganicznego inhibitora korozji stosowanego do wyrobu farb antykorozyjnych, a którego zadaniem jest zwiększenie wytrzymałości na działanie wody morskiej, podwyższenie elastyczności, zwiększenia przyczepności oraz odporności na uderzenia.

EN

The results of on-site tests on the inorganic inhibitor application under paint systems on worse prepared steel surface have been described. In present work analysis of possibility of use vulcanic tuf on anticorosive paints wos invetigated. Positive effects of such corrosin protection, have been observed.

6

Wpływ tufu wulkanicznego na odporność korozyjną stali w środowisku 5% NaCl

Hebdowska-Krupa M., Mikuła J.

Archiwum Odlewnictwa

|

2006

|

R. 6, nr 21/2

296--302

PL

W pracy przedstawiono wyniki badań dotyczących zwiększenia odporności korozyjnej stali DC01 A w środowisku 5%NaCl, poprzez dodanie do roztworu odpowiednio przygotowanego preparatu wykonanego z tufu wulkanicznego, działającego jako nieorganiczny inhibitor korozji. Przeprowadzona rentgenowska analiza dyfrakcyjna tufu stwierdziła występowanie dwóch głównych faz: glinokrzemianu K(AlSi3O8) oraz krzemionki SiO2. Z analizy krzywych Tafela wynika, że wraz ze wzrostem koncentracji inhibitora w roztworze rośnie wartość potencjału, czyli inhibitor skutecznie powstrzymuje anodowe rozpuszczanie stali. Badania mikroskopowe wykazały, że dodatki tufu istotnie wpłynęły na zmianę mechanizmu korozji (z międzykrystalicznego na równomierne rozpuszczanie).

EN

In the work was carry out investigations corrosion resistance the steel DC01A in 5% solution NaCl and additions vulcano tuf as inhibitor reagent, The diffraction X-ray analysis of vulcano tuf indicated that consist et two phase: sanidine K(AlSi3O8) and quartz SiO2. The vulcano tuf actin as inhibitor of corrosion DC01 A steel by moving the potential to the positive potentials. Microscopic investigations showed, that additions tuf influenced indeed onto change of mechanism of corrosion (from intercrystalline onto even dissolving).