DSC and TA characteristics of the inoculated Al-Zn20 alloy

Krajewski W. K., Buraś J., Piwowarski G., Haberl K., Tsivoulas D.

Archives of Foundry Engineering

2011

Vol. 11, iss. 1

65-68

The paper brings information about inoculation process of the sand-cast binary Al-20 wt% Zn (AlZn20) alloy, inoculated with Ti-containing grain-refiners, i.e. AlTi5B1, AlTi3C0.15 and (AlZn)-Ti3 master alloys (MA). During the experiments thermal analyses (TA) and differential scanning calorimetry (DSC) were used. Macrostructure observations were performed using light microscopy (LM). On the basis of the performed examinations it was found that all the MAs used in this work caused significant grain refinement, which initiates via a heterogeneous nucleation mode. The obtained structure fineness of the inoculated AlZn20 alloy should positively influence its ductility, which is of great importance for the practical application of this group of foundry alloys.

DSC examinations of the Al-20 wt. % Zn sand-cast alloy inoculated with Ti-containing grain-refiners

Tsivoulas D., Czeppe T., Krajewski W. K.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

590-593

The present study continues the research efforts of recent years on the grain- refinement of the sand-cast Al-20 wt. % Zn alloy. The aim of the current experimental work is to optimise the grain-refining Ti-addition by achieving a balance of all the desired properties for an as-cast alloy; small grain size, high tensile strength, high damping properties and low porosity are targeted. This paper is focused on the effects of the addition of four master alloys, containing different amounts of Ti, on the melting and crystallization behaviour of the Al-Zn20 alloy. DSC analysis was carried out in order to compare the base alloy with its four modified variants. These preliminary measurements include the enthalpy/peak area of the phase transformations and the corresponding temperature ranges. The results showed that all the tested master alloys reduced the temperature range for both melting and crystallisation, but on the other hand they significantly increased the enthalpy associated with the phase transformations as compared to the base alloy.

Prezentowana praca jest kontynuacją badań obejmujących modyfikację stopu Al-Zn20, odlewanego do formy piaskowej. Głównym celem prac jest optymalizacja dodatku Ti w celu uzyskania kompleksu dobrych właściwości, tj. obok rozdrobnionego ziarna uzyskanie wysokiej wytrzymałości na rozciąganie, wysokich właściwości tłumiących i niskiej porowatości. Niniejsza praca koncentruje się na przebiegu procesów topienia i krystalizacji stopu Al-Zn20 z dodatkiem czterech rożnych zapraw modyfikujących. Wykonane badania DSC obejmują porównanie stopu wyjściowego i jego czterech, zmodyfikowanych odpowiedników. Wykonane w ramach pracy pomiary dotyczą określenia pola powierzchni pików entalpii przemian fazowych i odpowiadających im zakresów temperatury. Wstępne badania wykazały, że wszystkie zastosowane w badaniach zaprawy zmniejszają zakresy przemian fazowych przy topieniu i krystalizacji, i równocześnie powodują powiększenie entalpii tych przemian, w stosunku do wartości obserwowanych dla stopu wyjściowego.