Sintering and grain growth behaviour of ultra fine Al2O3 powder

Mazaheri M., Razavi Hesabi Z., Haghighatzadeh M., Sadrnezhaad S. K.

Materiały Ceramiczne

2010

T. 62, nr 3

297-300

The sub-micrometer alumina powder with an average particle size of 150 nm was sintered, using two different methods, i.e. conventional sintering (CS) and two-step sintering (TSS). While the grain size of full-dense structures produced by conventional sintering ranges between 1-2 žm, the application of an optimum TSS regime led to a remarkable decrease of grain size down to ∼500 nm. The results show that low temperature isothermal dwell at 1150 ° after heating the green compacts up to 1300 ° decreased the grain size from 1.2 žm to 850 nm. A further decrease of the first step temperature to 1250 ° led to the formation of a finer structure with an average grain size of 500 nm.

Submikronowy proszek Al2O3 o średnim rozmiarze cząstki wynoszącym 150 nm spiekano przy użyciu dwóch metod: konwencjonalnego spiekania (CS) i spiekania dwuetapowego (TSS). Podczas gdy rozmiar ziarna całkowicie zagęszczonych struktur, wytworzonych za pomocą konwencjonalnego spiekania, mieścił się w przedziale 1-2 žm, zastosowanie optymalnego reżimu TSS prowadziło do niezwykłego zmniejszenia rozmiaru ziarna poniżej ∼500 nm. Wyniki pokazują, że izotermiczne niskotemperaturowe przetrzymanie w 1150 stopni C, zastosowane po wygrzaniu surowych wyprasek aż do 1300 stopni C, zmniejsza rozmiar ziaren z 1.2 žm na 850 nm. Dalsze obniżenie temperatury pierwszego etapu spiekania do 1250 stopni C prowadziło do utworzenia bardziej drobnoziarnistej mikrostruktury o średnim rozmiarze ziarna wynoszącym 500 nm.