Study on laser welding of a copper material and stainless steel

Wang Renping

Przemysł Chemiczny

2024

T. 103, nr 9

963--967

A com. fiber laser was used to weld Cu and stainless steel plates. The laser power was 2.2 kW, the welding speed 2.5 mm/s, the spot diam. about 0.5 mm, and the wire feeding speed 2-3.5 mm/s. Ar gas flow rate was 10 L/min. The weld produced was smooth and defect-free, the grain distribution was uniform and the mech. properties of the joint were high. The av. tensile strength of the welded joints was 984 MPa, and the av. yield strength of the joints was 351.4 MPa. The superior ity and potential of laser welding in dissimilar metal welding was evidenced.

Do spawania płyt z miedzi i stali nierdzewnej użyto komercyjnego lasera światłowodowego. Moc lasera wynosiła 2,2 kW, prędkość spawania 2,5 mm/s, średnica plamki ok. 0,5 mm, prędkość podawania drutu 2-3,5 mm/s, a natężenie przepływu argonu 10 L/min. Uzyskana spoina była gładka i wolna od wad, rozkład ziarna był równomierny. Spoina miała dobre właściwości mechaniczne. Średnia wytrzymałość na rozciąganie spoin spawanych wynosiła 984 MPa, a średnia granica plastyczności spoin to 351,4 MPa. Udowodniono potencjał spawania laserowego w spawaniu różnych metali.