Polymer-metal complexes based on gellan

Vasiliu S., Racovita S., Neagu V., Popa M., Desbrieres J.

Polimery

2010

T. 55, nr 11-12

839-845

By dropwise adding solutions of gellan (Gil) or gellan + poly(vinyl alcohol) (PVAL) mixture into different metal salt solutions - FeCl3 · 6 H2O, FeCl2 · 4 H2O, CoCl2 · 6 H2O, CuCl2 · 2 H2O - at 30 °C under constant stirring, preparation of spherical microparticles based on polymer-metal complexes has been performed. FT-IR spectroscopy, TGA analysis and swelling measurements of these microparticles in water showed the influence of the metal type ions on their structure, thermal stability and water swelling capacity. The FT-IR spectroscopy allows to explain the mechanism of polymer-metal complexes formation and the optical microscopy showed that the microparticles obtained had good sphericity with average diameter ranging from 719 μm to 830 μm. The thermal stability of the polymer-metal complexes was found to be higher than that of the gellan.

Opisano prosty i łatwy do zrealizowania sposób otrzymania w temp. 30 °C kompleksów gelanu (Gll - anionowy, wielkocząsteczkowy, dezaktywowany polisacharyd pochodzenia naturalnego) lub mieszanin Gil + poli(alkohol winylowy) (PVAL) z wodzianami różnych soli metali (FeCl3, FeCl2, CuCl2, CoCl2) (rys. l, tabela 1). Kompleksy mają postać regularnych okrągłych mikrocząstek o wymiarach 719-830 μm. Na podstawie widm IR (rys. 2 i 3, tabela 2) zinterpretowano mechanizm powstawania kompleksów i określono ich budowę. Zbadano termostabilność kompleksów oraz kinetykę ich degradacji cieplnej (rys. 4, tabela 3); jest to wieloetapowy proces o skomplikowanym przebiegu. Scharakteryzowano zjawisko pęcznienia kompleksów w wodzie w temp. 25 °C (rys. 5, tabela 4) ustalając następującą zależność stopnia spęcznienia od rodzaju zawartego w nich metalu: Fe³+ < Fe²+ < Cu²+ < Co²+.

Crosslinking polymerization of polyfunctional monomers by free radical mechanism

Vlad C. D., Vasiliu S.

Polimery

2010

T. 55, nr 3

181-185

The crosslinked architectures based on diallyl maleate (DAM) obtained by suspension polymerization techniques have been studied. The influence of synthesis parameters on the structure of poly(diallyl maleate) [poly(DAM)] and copolymers of DAM with methyl methacrylate (MM) [poly(DAM-co-MM)] was also investigated. The effect of the diluents (n-butyl acetate or cyclohexanole) on the inner macroporous structure (apparent and skeletal density, pore volume, total porosity, cyclohexane uptake) has been studied. The experimental results showed that the values of the solvent uptake are strongly influenced by the diluent quantity as well as its solubility parameter.

Przedmiotem badań był proces sieciowania na drodze polimeryzacji suspensyjnej maleinianu diallilu (DAM) i jego kopolimeru z metakrylanem metylu (MM). Określono wpływ warunków prowadzenia reakcji na strukturę otrzymanych poli(maleinianu diallilu) [poly(DAM)] i poli(maleinianu diallilu-ko-metakrylanu metylu) [poly(DAM-co-MM)]. Badano także wpływ rodzaju rozcieńczalnika (octan n-butylu lub cykloheksanol) i jego ilości na makroporowatą strukturę produktów. W tym celu wyznaczano gęstość pozorną, gęstość szkieletową, objętość porów, porowatość całkowitą i absorpcję cykloheksanu. Wyniki badań pokazują, że wielkość absorpcji rozpuszczalnika silnie zależy od ilości jak i parametru rozpuszczalności rozcieńczalnika.