Al2O3-Mo functionally graded material obtained via centrifugal slip casting

Zygmuntowicz J., Baczyńska A., Miazga A., Kaszuwara W., Konopka K.

Materiały Ceramiczne

2017

T. 69, nr 2

73--77

Al2O3-Mo functionally graded material (FGMs) was fabricated successfully by a centrifugal slip casting method. An aqueous ceramic slurry containing 50 vol.% of the solid phase and including 10 vol.% of the molybdenum particles was made. Consolidation was performed by using a centrifugal slip casting process at 3000 rpm for 1.5 h. The morphology and chemical composition of the produced composite were analysed using a scanning electron microscope equipped with an EDS detector. Moreover, the X-ray diffraction was made. The microstructural observation and the stereological analysis confirmed that the molybdenum particles are distributed in the material in a gradient way.

Funkcjonalny materiał gradientowy z układu Al2O3-Mo zostały wytworzony metodą odlewania odśrodkowego mas lejnych. Wodną zawiesinę o zawartość fazy stałej 50% obj. przygotowano na bazie tlenku glinu i proszku molibdenu (10% obj.). Próbki formowano metodą odlewania odśrodkowego; parametry procesu były następujące: v - 3000 obr./min, czas - 1,5 godz. Charakterystyka mikrostruktury oraz składu chemicznego wytworzonego kompozytu została wykonana przy użyciu skaningowego mikroskopu elektronowego z detektorem EDS. Przeprowadzono analizę fazową (XRD) kompozytu. Obserwacje mikrostruktury oraz analiza stereologiczna potwierdziły gradientowe rozmieszczenie cząstek molibdenu w wytworzonym kompozycie.