Stokes flow in a lid-driven cavity under the effect of an inclined magnetic field is studied. The radial basis function (RBF) approximation is employed to the magnetohydrodynamic (MHD) equations which include Navier-Stokes equations of fluid dynamics and Maxwell’s equations of electromagnetics through Ohm’s law with the Stokes approximation. Numerical results are obtained for the moderate Hartmann number (0 ≤ M ≤ 80) and different angles of a magnetic field (0 ≤ α ≤ π). It is found that the increase in the Hartmann number causes the development of new vortices under the main flow due to the impact of a magnetic field. However, the type of the inclination angle (acute or obtuse) determines the location of the vortices.

Effect of Post-Heat Treatment on Microstructure and Mechanical Properties of Cu-Fe-Co Powder Alloy Fabricated by Hot Pressing

Çelik E., Aslan A. K.

Archives of Metallurgy and Materials

2018

Vol. 63, iss. 1

371--377

In this study, the powder mixture which consists of Cu-Fe-Co was produced by using the method of hot pressing technique. In addition, effect of heat treatment process on microstructure and mechanical properties of this alloy was investigated. Following the hot pressing process applied on the samples, heat treatment was carried out at 950°C for two different dwelling times (90 and 180 minutes). Measured density values were considered as physical characteristics, while hardness and fracture strength values were considered as mechanical characteristics. It was observed that porosity rates of hot pressed samples were decreased by increasing of temperature and pressing parameters. In this study it was observed that Cu was spread in matrix and filled the micro porosities. Hardness values were determined to be decreased as a result of grain growth after heat treatment process. That 4 fold increased elongation % values which were achieved by TRS experiments were observed as well.