Electrodeposition of Ni/SiC composite coating aluminium

Burzyńska L., Rudnik E., Ćwięka K.

Archives of Metallurgy and Materials

2009

Vol. 54, iss. 3

845-851

A hydrometallurgical method for production of Ni/SiC composite coating on aluminium was developed. The following consecutive stages were proposed: zincating of aluminium substrate for 5 min in alkaline zincate solution, electroless nickel deposition for 1 h by immersion in nickel-acetate solution with sodium hypophosphite as a reductant and, finally, electrodeposition of Ni/SiC composite from a chloride-sulphate bath for 6 h at current density of 1 A/dm2. The stages were essential to achieve good adherence of the multilayer system to the aluminium surface. Microscopic observations showed uniform thickness of the individual layers over cross-sections of the sample. Microhardness of the composite was approx. 770 HV.

Opracowano hydrometalurgiczną metodę wytwarzania powłok kompozytowych Ni/SiC na aluminium. Proces obejmuje następujące główne etapy: nakładanie powłoki cynkowej na aluminium na drodze cementacji w roztworze alkalicznym przez okres 5 min; bezprądowe (autokatalityczne) osadzanie powłoki niklowej przez okres 1 godz. przy użyciu podfosforynu sodu jako reduktora; elektrolityczne współosadzanie powłok kompozytowych Ni/SiC z kąpieli chlorkowo-siarczanowej przez okres 6 godz. przy gęstości prądu 1 A/dm2. Wymienione etapy pozwalają na uzyskanie układu wielowarstwowego o dobrej wzajemnej przyczepności poszczególnych warstw. Obserwacje mikroskopowe przekrojów poprzecznych próbek wykazały tworzenie się warstewek o równomiernej grubości. Mikrotwardość powłoki kompozytowej nałożonej na aluminium wynosiła ok. 770 HV.