Transport properties of nanocrystalline and microcrystalline Gd-doped ceria

Baldinozzi G., Dolle M., Kusiński J., Petot C., Petot-Ervas G.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

483-486

Electrical conductivity measurements of Gd-doped ceria polycrystals, sintered from different sources of submicronic powder, have allowed us to illustrate the influence of size scale on the ionic conductivity. In samples doped with 10 moles % Gd2O3. The ionic conductivity passes through a maximum for grain sizes included between 200 and 500 nm. Furthermore, for the nanocrystalline samples an enhancement of the ionic conductivity is observed when the amount of dopant increases.These results were analyzed according to XPS characterizations performed on polycrystal fracture surfaces. These analysis show a grain size dependent gadolinium segregation at the periphery of the grains, which decreases with grain size, but which depends also of both densification conditions and starting powders. It follows from this set of results that the maximum of ionic conductivity occurs for a mean enrichment at the periphery of the grains close to Gd/ Ce = 0.9.

Polikrystaliczne probki CeO2 domieszkowane gadolinem spiekano z różnego rodzaju mieszanin nano- i mikroproszkow. Wyniki badań uzyskanych na próbkach zawierających 10% mol. Gd2O3 pokazują, że przewodnictwo jonowe osiąga maksimum w zakresie wielkości ziarna pomiędzy 200 do 300 nm. Ponadto wykazano, że w nanokrystalicznych próbkach wzrost przewodnictwa jonowego następuje wraz ze wzrostem zawartości domieszki, podczas gdy dla materiału gruboziarnistego przewodnictwo jonowe osiąga maksimum przy 10% mol. Gd2O3. Wyjaśniono to, jako efekt wpływu wielkości ziarna proszku na segregację Gd do zewnętrznych stref ziaren, co potwierdzono badaniami za pomocą techniki XPS na przełomach próbek.

Transport properties of nanocrystalline gadolinium-doped ceria

Baldinozzi G., Dolle M., Gosset D., Surble S., Kusiński J., Petot C., Petot-Ervas G.

Inżynieria Materiałowa

2007

Vol. 28, nr 3-4

233-235

Gd-doped ceria nanocrystalline powders (5, 7.5, 10 and 15 mol % GdĄ) having grain sizes smaller than 17 nm were prepared by the combustion technique. Polycrystalline samples were obtained by uniaxial hot pressing. The samples were characterized by X-ray diffraction, scanning and transmission electron microscopy. The final grain size, smaller than 100 nm, depends on the sintering conditions and on the amount of Gd. The transport properties of these polycrystalline specimens were studied by impedance spectroscopy. These results are compared to those obtained for microcrystalline samples and they show that the ionic conductivity of these materials goes through a maximum for a grain size in the range 300-500 nm. XPS analysis suggests that this behaviour is related to the segregation of Gd at the region near the grain surfaces, which is less pronounced when the grain size decreases.

Nanokrystaliczne proszki tlenku ceru domieszkowanego Gd (5, 7.5, 10 i 15 mol % Gd203), o wielkościach krystalitów mniejszych niż 17 nm, wytworzono metodą syntezy. Polikrystaliczne próbki uzyskane w procesie jednoosiowego prasowania na gorąco poddano badaniom z wykorzystaniem technik dyfrakcji rentgenowskiej oraz obserwacji mikroskopowych TEM i SEM. Stwierdzono, iż końcowa wielkość ziarna, mniejsza niż 100 nm, uzależniona jest od warunków procesu spiekania oraz zawartości domieszki Gd. Własności przewodzące domieszkowanych tlenków określono z wykorzystaniem układu pomiarowego rejestrującego zmiany impedancji. Porównanie otrzymanych tą drogą wyników z wartościami uzyskanymi dla tlenków mikrokrystalicznych pozwoliło na stwierdzenie, iż maksymalne wartości przewodności jonowej uzyskuje się dla tlenków charakteryzujących się wielkością ziarna z zakresu 100-300 nm. Przeprowadzona analiza XPS sugeruje, że wynik taki jest skutkiem segregacji Gd (w okolicy powierzchni krystalitów), która jest mniej widoczna gdy maleje wielkość krystalitów.